Polyvinylidene fluoride (PVDF) as a biomaterial: from polymeric raw material to monofilament vascular suture.

This study identified the effects of various manufacturing processes on the crystalline microstructure, mechanical properties, and biocompatibility of a polyvinylidene fluoride (PVDF) suture. To achieve this, changes in the crystalline microstructure and the tensile behavior of PVDF monofilaments were monitored in vitro after different thermal processing, coloration, and sterilization treatments. In addition, the in vivo biocompatibility of the manufactured and sterilized PVDF suture was assessed by using it to anastomose a preclotted polyester vascular prosthesis as a thoracoabdominal bypass in a series of dogs. The tissue response was followed by histologic and scanning electron microscopy over implantation periods ranging from 4 h to 6 months. Differential scanning calorimetry and infrared spectroscopy (FTIR-ATR) showed that thermal processing and the addition of a coloring agent had a direct effect on modifying the crystalline microstructure and hence changing the mechanical properties. For example, thermal processing converted some of the alpha phase into the beta and gamma polymorphs, whereas coloration led only to a major increase in the beta-to-alpha ratio. The tensile properties were found to be optimized when the relative proportion of the beta and gamma phases combined compared to the alpha form gave rise to an FTIR A509/A532 absorption ratio between 4.0 and 4.5. Sterilization was found to cause some modifications to the crystalline microstructure near the surface of the monofilaments, but it did not change their mechanical properties. Pathologic examination of the anastomotic regions after different periods of implantation revealed a minimal cellular response, with no mineralization, intimal hyperplasia, or excessive fibrous tissue reaction. This good biocompatibility, together with other desirable characteristics such as ease of manipulation and satisfactory mechanical strength, makes PVDF an attractive alternative monofilament suture material for cardiovascular surgery.

[1]  R. Guidoin,et al.  Why Make Monofilament Sutures Out of Polyvinylidene Fluoride? , 1994, ASAIO journal.

[2]  R. Guidoin,et al.  Biocompatibility and Biofunctionality of a Gelatin Impregnated Polyester Arterial Prosthesis , 1993, Engineering Plastics.

[3]  N. Fanti,et al.  Influence of molecular weight on the crystallization of poly(vinylidene fluoride) , 1989 .

[4]  B. Granz,et al.  PVDF hydrophone for the measurement of shock waves (lithotripsy) , 1989 .

[5]  S. Lang,et al.  Measurement applications based on pyroelectric properties of ferroelectric polymers , 1989 .

[6]  R. Guidoin,et al.  Fate of polyester arterial prostheses implanted as thoraco-abdominal by-passes in dogs: haematology, pathology, and biochemistry. , 1988, Clinical and investigative medicine. Medecine clinique et experimentale.

[7]  M. Muthukumar,et al.  Analysis of the crystalline phase transformation of poly(vinylidene fluoride) , 1985 .

[8]  M. Vaccari,et al.  Polypropylene suture fracture. , 1985, The Annals of thoracic surgery.

[9]  Lambert Wc,et al.  Anastomotic false aneurysms: a comparison of braided Dacron and polypropylene sutures. , 1982 .

[10]  G. Cornel Fracture of polypropylene suture. , 1982, The Annals of thoracic surgery.

[11]  M. Litt,et al.  The Crystal Structure of the ? Phase of Poly(vinylidene fluoride) , 1980 .

[12]  K. Matsushige,et al.  Melting point of oriented poly(vinylidene fluoride) form‐i crystal under tensile stress , 1980 .

[13]  G. Davies,et al.  Evidence for a new crystal phase in conventionally poled samples of poly(vinylidene fluoride) in crystal form II , 1979 .

[14]  G. Lawrie,et al.  Suture material as a factor in the occurrence of anastomotic false aneurysms. An analysis of 26 cases. , 1979, Archives of surgery.

[15]  L. Sauvage,et al.  The Preclotting of Porous Arterial Prostheses , 1978, Annals of surgery.

[16]  D. Y. Yoon,et al.  Formation of a New Crystal Form (αp) of Poly(vinylidene fluoride) under Electric Field , 1978 .

[17]  Steven C. Roth,et al.  Electric‐field‐induced phase changes in poly(vinylidene fluoride) , 1978 .

[18]  Yozo Chatani,et al.  Crystal Structures of Three Crystalline Forms of Poly(vinylidene fluoride) , 1972 .

[19]  Masamichi Kobayashi,et al.  Molecular Conformation and Packing of Poly(vinylidene fluoride). Stability of Three Crystalline Forms and the Effect of High Pressure , 1972 .

[20]  G. R. Crane,et al.  Pyroelectricity and Optical Second Harmonic Generation in Polyvinylidene Fluoride Films , 1971 .

[21]  J. Lando,et al.  Polymorphism of poly(vinylidene fluoride). III. The crystal structure of phase II , 1970 .

[22]  H. Kawai,et al.  The Piezoelectricity of Poly (vinylidene Fluoride) , 1969 .

[23]  Anton Peterlin,et al.  Nuclear magnetic resonance and x‐ray determination of the structure of poly(vinylidene fluoride) , 1966 .

[24]  A. Büchtemann,et al.  Field-induced changes of dipole orientation in PVDF determined by infrared spectroscopy , 1991 .

[25]  Andrew J. Lovinger,et al.  Poly(Vinylidene Fluoride) , 1982 .

[26]  Y. Wada,et al.  Piezoelectricity, pyroelectricity, and the electrostriction constant of poly(vinylidene fluoride) , 1971 .