Effects of lithium salts on ASR gel composition and expansion of mortars

Suppression of alkali-silica reaction (ASR) expansion in mortar and concrete by the addition of lithium salts has been confirmed by some workers. It has been revealed that lithium hydroxide tended to reduce the reaction between sodium or potassium hydroxide and reactive silica, and that the ASR gel incorporating lithium was less expansive. However, it has not been reported how the addition of a lithium salt influenced the composition of the ASR gel. The calcium in ASR gel is considered to play an important role in the expansion of the gel. Thus, it is significant to characterize ASR gel composition in mortars containing lithium salts by BSE-EDS analysis. This study aims to discuss the mechanisms of suppression of ASR expansion in mortar by lithium salts from the viewpoint of ASR gel composition. The average CaO/SiO{sub 2} ratio in ASR gels decreased with increasing amount of added lithium salts. It should be noted that the extent of variations in the CaO/SiO{sub 2} ratio in ASR gels significantly decreased with increasing amount of lithium salts. The addition of relatively small amounts of LiOH and Li{sub 2}CO{sub 3} resulted in increased expansion. We also obtained an unexpected result that ASR gels became homogeneous withmore » respect to their CaO contents at high dosage levels. However, the reduction in average CaO/SiO{sub 2} ratios and the homogenization in the CaO content of ASR gels due to the addition of lithium salts may not be related to the expansion of mortars.« less