Grain Boundary Phosphorus Segregation in Thermally Aged Low Alloy Steels

Intergranular embrittlement due to grain boundary segregation of phosphorus is recognized as one of the potential degradation factors in irradiated reactor low alloy steels at high neutron fluence. In this study, low alloy steels thermally aged at 400-500°C were investigated to evaluate the correlation between phosphorus segregation and intergranular embrittlement. Phosphorus segregation determined using Auger electron spectroscopy increased after thermal aging above 450°C and was in good agreement with the calculated value based on McLean's model. No influence of thermal aging on tensile properties or hardness was observed. The ductile brittle transition temperature determined using a one-third size Charpy impact test increased at a P/Fe peak ratio of 0.14. These results indicated that there is a threshold level of phosphorus segregation for non-hardening embrittlement. The ductile to brittle transition temperature (DBTT) increased with the proportion of intergranular fracture, so this result shows that there is a relationship between DBTT and the proportion of intergranular fracture. The fracture stress decreases due to non-hardening embrittlement on the thermally aged material with high proportion of intergranular fracture.

[1]  K. F. Russell,et al.  Characterization of phosphorus segregation in neutron-irradiated Russian pressure vessel steel weld , 1995 .

[2]  H. Grabke,et al.  Site competition in grain boundary segregation of phosphorus and nitrogen in iron , 1981 .

[3]  Y. Nikolaev,et al.  Grain boundary embrittlement due to reactor pressure vessel annealing , 1994 .

[4]  Phn Ray,et al.  Temper Embrittlement, Irradiation Induced Phosphorus Segregation and Implications for Post-Irradiation Annealing of Reactor Pressure Vessels , 1999 .

[5]  An APFIM Survey of Grain Boundary Segregation and Precipitation in Irradiated Pressure Vessel Steels , 1994 .

[6]  W. Server,et al.  Review of Phosphorus Segregation and Intergranular Embrittlement in Reactor Pressure Vessel Steels , 2001 .

[7]  C. A. Hippsley,et al.  Review of thermal ageing data and its application to operating reactor pressure vessels , 1993 .

[8]  S. Druce,et al.  Effect of ageing on properties of pressure vessel steels , 1986 .

[9]  H. Grabke,et al.  Grain boundary segregation of phosphorus and carbon in ferritic iron , 1986 .

[10]  B. A. Gurovich,et al.  Intergranular and intragranular phosphorus segregation in Russian pressure vessel steels due to neutron irradiation , 2000 .

[11]  W. Beeré,et al.  The Effect of Heat Treatment on Phosphorus Segregation in a Submerged-Arc Weld Metal , 1999 .

[12]  H. Grabke,et al.  Equilibrium segregation of phosphorus at grain boundaries of Fe–P, Fe–C–P, Fe–Cr–P, and Fe–Cr–C–P alloys , 1981 .