Optimization of Atmospheric Plasma Spray Process Parameters using a Design of Experiment for Alloy 625 coatings

Alloy 625 is a Ni-based superalloy which is often a good solution to surface engineering problems involving high temperature corrosion, wear, and thermal degradation. Coatings of alloy 625 can be efficiently deposited by thermal spray methods such as Air Plasma Spraying. As in all thermal spray processes, the final properties of the coatings are determined by the spraying parameters. In the present study, a D-optimal experimental design was used to characterize the effects of the APS process parameters on in-flight particle temperature and velocity, and on the oxide content and porosity in the coatings. These results were used to create an empirical model to predict the optimum deposition conditions. A second set of coatings was then deposited to test the model predictions. The optimum spraying conditions produced a coating with less than 4% oxide and less than 2.5% porosity. The process parameters which exhibited the most important effects directly on the oxide content in the coating were particle size, spray distance, and Ar flow rate. The parameters with the largest effects directly on porosity were spray distance, particle size, and current. The particle size, current, and Ar flow rate have an influence on particle velocity and temperature but spray distance did not have a significant effect on either of those characteristics. Thus, knowledge of the in-flight particle characteristics alone was not sufficient to control the final microstructure. The oxidation index and the melting index incorporate all the parameters that were found to be significant in the statistical analyses and correlate well with the measured oxide content and porosity in the coatings.

[1]  Sanjay Sampath,et al.  Development of process maps for plasma spray: case study for molybdenum , 2003 .

[2]  D. G. McCartney,et al.  Microstructural characterization of high velocity oxy-fuel sprayed coatings of Inconel 625 , 1997 .

[3]  Katherine T. Faber,et al.  Optimization of small-particle plasma-sprayed alumina coatings using designed experiments , 2001 .

[4]  C. Persson,et al.  Influence of particle in-flight characteristics on the microstructure of atmospheric plasma sprayed yttria stabilized ZrO2 , 2001 .

[5]  Pierre Fauchais,et al.  Understanding plasma spraying , 2004 .

[6]  Lili Zheng,et al.  Melting and oxidation behavior of in-flight particles in plasma spray process , 2005 .

[7]  S. Gong,et al.  Influence of water vapor on the high temperature oxidation behavior of thermal barrier coatings , 2003 .

[8]  C. J. Smithells,et al.  Smithells metals reference book , 1949 .

[9]  H. Singh,et al.  Characterization of oxide scales to evaluate high temperature oxidation behavior of Ni–20Cr coated superalloys , 2007 .

[10]  Jonathan Lawrence,et al.  On the role of microstructure form and dimension in surface energy changes in a magnesia partially stabilized zirconia bioceramic following CO2 laser irradiation , 2004 .

[11]  J. Matějíček,et al.  Role of thermal spray processing method on the microstructure, residual stress and properties of coatings: an integrated study for Ni–5 wt.%Al bond coats , 2004 .

[12]  F. Azarmi Vacuum plasma spraying , 2005 .

[13]  J. A. Little,et al.  The effect of spray parameters on the properties of high velocity oxy-fuel NiAl intermetallic coatings , 2000 .

[14]  Y. Itoh,et al.  Influence of high-temperature protective coatings on the mechanical properties of nickel-based superalloys , 1999 .

[15]  Ghislain Montavon,et al.  Modeling of the APS plasma spray process using artificial neural networks: basis, requirements and an example , 2004 .

[16]  H. Herman,et al.  Rapid solidification and microstructure development during plasma spray deposition , 1996 .

[17]  A. A. Syed,et al.  In-flight oxidation of stainless steel particles in plasma spraying , 2005 .

[18]  R. K. Meyer,et al.  The Coordinate-Exchange Algorithm for Constructing Exact Optimal Experimental Designs , 1995 .