Electrospinning of collagen and elastin for tissue engineering applications.

Meshes of collagen and/or elastin were successfully prepared by means of electrospinning from aqueous solutions. Flow rate, applied electric field, collecting distance and composition of the starting solutions determined the morphology of the obtained fibres. Addition of PEO (M(w)=8 x 10(6)) and NaCl was always necessary to spin continuous and homogeneous fibres. Spinning a mixture of collagen and elastin resulted in fibres in which the single components could not be distinguished by SEM. Increasing the elastin content determined an increase in fibres diameters from 220 to 600 nm. The voltage necessary for a continuous production of fibres was dependent on the composition of the starting solution, but always between 10 and 25 kV. Under these conditions, non-woven meshes could be formed and a partial orientation of the fibres constituting the mesh was obtained by using a rotating tubular mandrel as collector. Collagen/elastin (1:1) meshes were stabilized by crosslinking with N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (EDC) and N-hydroxysuccinimide (NHS). This treatment afforded materials with a high thermal stability (T(d)=79 degrees C) without altering their original morphology. Upon crosslinking PEO and NaCl were fully leached out. Smooth muscle cells grew as a confluent layer on top of the crosslinked meshes after 14 d of culture.

[1]  V. Daggett,et al.  The molecular basis for the inverse temperature transition of elastin. , 2001, Journal of molecular biology.

[2]  Jiangtao Hu,et al.  Chemistry and Physics in One Dimension: Synthesis and Properties of Nanowires and Nanotubes , 1999 .

[3]  E Bell,et al.  A blood vessel model constructed from collagen and cultured vascular cells. , 1986, Science.

[4]  J. Feijen,et al.  Biocompatibility and tissue regenerating capacity of crosslinked dermal sheep collagen. , 1994, Journal of biomedical materials research.

[5]  F A Auger,et al.  A completely biological tissue‐engineered human blood vessel , 1998, FASEB journal : official publication of the Federation of American Societies for Experimental Biology.

[6]  I. Chronakis,et al.  Polymer nanofibers assembled by electrospinning , 2003 .

[7]  Karthik Nagapudi,et al.  Engineered collagen–PEO nanofibers and fabrics , 2001, Journal of biomaterials science. Polymer edition.

[8]  M. Kotaki,et al.  Aligned biodegradable nanofibrous structure: a potential scaffold for blood vessel engineering. , 2004, Biomaterials.

[9]  Darrell H. Reneker,et al.  Electrospinning process and applications of electrospun fibers , 1995 .

[10]  Y. Fung,et al.  Biomechanics: Mechanical Properties of Living Tissues , 1981 .

[11]  E. Chaikof,et al.  High-resolution analysis of engineered type I collagen nanofibers by electron microscopy. , 2001, Scanning.

[12]  Robert M. Nerem.  Critical issues in vascular tissue engineering , 2004 .

[13]  J. Feijen,et al.  Relations between in vitro cytotoxicity and crosslinked dermal sheep collagens. , 1992, Journal of biomedical materials research.

[14]  Darrell H. Reneker,et al.  Beaded nanofibers formed during electrospinning , 1999 .

[15]  Darrell H. Reneker,et al.  Bending instability of electrically charged liquid jets of polymer solutions in electrospinning , 2000 .

[16]  Jan Feijen,et al.  Tissue engineering of blood vessels: characterization of smooth‐muscle cells for culturing on collagen‐and‐elastin‐based scaffolds , 2004, Biotechnology and applied biochemistry.

[17]  D. Shaw,et al.  Introduction to colloid and surface chemistry , 1970 .

[18]  A A Poot,et al.  First steps towards tissue engineering of small-diameter blood vessels: preparation of flat scaffolds of collagen and elastin by means of freeze drying. , 2006, Journal of biomedical materials research. Part B, Applied biomaterials.

[19]  Cato T Laurencin,et al.  Electrospun nanofibrous structure: a novel scaffold for tissue engineering. , 2002, Journal of biomedical materials research.

[20]  Y. Fung.  Mechanical Properties and Active Remodeling of Blood Vessels , 1993 .

[21]  David L Kaplan,et al.  Electrospinning Bombyx mori silk with poly(ethylene oxide). , 2002, Biomacromolecules.

[22]  David G Simpson,et al.  Electrospinning collagen and elastin: preliminary vascular tissue engineering. , 2004, Frontiers in bioscience : a journal and virtual library.

[23]  G. Faury.  Function-structure relationship of elastic arteries in evolution: from microfibrils to elastin and elastic fibres. , 2001, Pathologie-biologie.

[24]  Andreas Greiner,et al.  Nanostructured Fibers via Electrospinning , 2001 .

[25]  Emilie J. Siochi,et al.  Electrospinning of a micro-air vehicle wing skin , 2003 .

[26]  J. Feijen,et al.  Cross-linking of dermal sheep collagen using a water-soluble carbodiimide. , 1996, Biomaterials.

[27]  D. Reneker,et al.  Nanometre diameter fibres of polymer, produced by electrospinning , 1996 .

[28]  L. Debelle,et al.  The structures of elastins and their function. , 1999, Biochimie.

[29]  Joseph M. DeSimone,et al.  Electrospinning of polymer nanofibers with specific surface chemistry , 2002 .

[30]  D. Mooradian,et al.  The role of vascular smooth muscle cell integrins in the compaction and mechanical strengthening of a tissue-engineered blood vessel. , 1999, Tissue engineering.

[31]  Burak Erman,et al.  Electrospinning of polyurethane fibers , 2002 .

[32]  G. Oliver,et al.  CarBamate Kinase of Lactobacillus Buchneri Ncdo110. II. KInetic Studies and Reaction Mechanism , 1987, Biotechnology and applied biochemistry.

[33]  J. Deitzel,et al.  The effect of processing variables on the morphology of electrospun nanofibers and textiles , 2001 .

[34]  M. Kotaki,et al.  A review on polymer nanofibers by electrospinning and their applications in nanocomposites , 2003 .

[35]  Hak Yong Kim,et al.  Nanofibrous mats of poly(trimethylene terephthalate) via electrospinning , 2004 .

[36]  Laura E Niklason,et al.  Requirements for growing tissue-engineered vascular grafts. , 2003, Cardiovascular pathology : the official journal of the Society for Cardiovascular Pathology.

[37]  Elliot L. Chaikof,et al.  Generation of Synthetic Elastin-Mimetic Small Diameter Fibers and Fiber Networks , 2000 .

[38]  Michael P Brenner,et al.  Controlling the fiber diameter during electrospinning. , 2003, Physical review letters.