Abstract In this work the melting behaviour of plutonium dioxide has been studied for the first time via laser heating. With this method, the short experiment duration combined with minimal contact between sample and containment minimized undesired side effects, such as sample reduction, vaporisation or reaction with the holder. The sample temperature was measured by fast pyrometry, and inflections in the recorded thermograms revealed the liquid-to-solid transition. This latter was also detected via a method based on the reflectance study of a low-power laser beam reflected by the sample surface. Multi-channel spectro-pyrometry was used to investigate, in parallel, the normal spectral emittance of the samples in the wavelength range between 550 and 920 nm at the investigated temperature. The present experimental melting temperature of (3017 ± 28) K is much higher than the values obtained in the past by traditional heating techniques. It is suggested that, in contrast to the present data, previous results were affected by extensive reaction of the plutonium dioxide samples with the containment and/or changes in the O/Pu ratio at high temperature.

[1]  L. F. Epstein,et al.  Ideal solution behavior and heats of fusion from the UO2-PuO2 phase diagram , 1967 .

[2]  D. Manara,et al.  Computer simulations of non-congruent melting of hyperstoichiometric uranium dioxide , 2009 .

[3]  Dario Manara,et al.  Melting of Stoichiometric and Hyperstoichiometric Uranium Dioxide , 2005 .

[4]  C. Ronchi,et al.  Laser-Pulse Melting of Nuclear Refractory Ceramics , 2002 .

[5]  James F. Schooley,et al.  Temperature : its measurement and control in science and industry , 1992 .

[6]  E. R. Gardner,et al.  The plutonium-oxygen phase diagram , 1965 .

[7]  William E Lee,et al.  Laser melting of spark plasma-sintered zirconium carbide: thermophysical properties of a generation IV very high-temperature reactor material , 2009 .

[8]  Christine Guéneau,et al.  Thermodynamic modelling of the plutonium–oxygen system , 2008 .

[9]  K. Konashi,et al.  Effect of Oxygen-to-Metal Ratio on Melting Temperature of Uranium and Plutonium Mixed Oxide Fuel for Fast Reactor , 2008 .

[10]  H. Preston‐Thomas,et al.  The International Temperature Scale of 1990 (ITS-90) , 1990 .

[11]  Ping Zhang,et al.  Optical properties of UO2 and PuO2 , 2009, 0911.3733.

[12]  J. K. Fink,et al.  Thermophysical properties of uranium dioxide , 2000 .

[13]  Dario Manara,et al.  New techniques for high-temperature melting measurements in volatile refractory materials via laser surface heating. , 2008, The Review of scientific instruments.

[14]  W. E. Baily,et al.  The solid-liquid phase diagram for the UO2-PuO2 system☆ , 1967 .

[15]  Masato Kato,et al.  Solidus and liquidus temperatures in the UO2–PuO2 system , 2008 .

[16]  Juan J. Carbajo,et al.  A review of the thermophysical properties of MOX and UO , 2001 .

[17]  D. Dewitt,et al.  Theory and practice of radiation thermometry , 1988 .

[18]  C. Alcock,et al.  Thermodynamic Properties of Individual Substances , 1994 .

[19]  D. Manara,et al.  Laser melting of uranium carbides , 2009 .

[20]  A. Tenney,et al.  Radiation Ratio Thermometry , 2007 .

[21]  F. Pavese,et al.  Recommended values of temperature on the International Temperature Scale of 1990 for a selected set of secondary reference points , 1996 .

[22]  Masato Kato,et al.  Solidus and liquidus of plutonium and uranium mixed oxide , 2008 .