Balling behavior of stainless steel and nickel powder during selective laser melting process

Balling phenomenon, as a typical selective laser melting (SLM) defect, is detrimental to the forming quality. In this work, a detailed investigation into the balling behavior of selective laser melting of stainless steel and pure nickel powder was conducted. It was found that the SLM balling phenomenon can be divided into two types generally: the ellipsoidal balls with dimension of about 500 μm and the spherical balls with dimension of about 10 μm. The former is caused by worsened wetting ability and detrimental to SLM quality; the latter has no obvious detriment to SLM quality. The oxygen content plays an important role in determining the balling initiation, which can be considerably lessened by decreasing the oxygen content of atmosphere to 0.1%. A high laser line energy density, which can be obtained by applying high laser power and low scan speed, could enable a well-wetting characteristic. The effect of scan interval on balling initiation is not obvious as long as the scan track is continuous. The surface remelting procedure can also alleviate the balling effect in a certain extent, due to the melting and wetting of metal balls. Moreover, the balling phenomenon of pure nickel was also studied, and the results implied that the balling discipline had a universality.

[1]  Rémy Glardon,et al.  An innovative method to build support structures with a pulsed laser in the selective laser melting process , 2012 .

[2]  Yifu Shen,et al.  Balling phenomena in direct laser sintering of stainless steel powder: Metallurgical mechanisms and control methods , 2009 .

[3]  Fude Wang Mechanical property study on rapid additive layer manufacture Hastelloy® X alloy by selective laser melting technology , 2012 .

[4]  Abdolreza Simchi,et al.  Direct metal laser sintering : Material considerations and mechanisms of particle : Rand tooling of powdered metal parts , 2001 .

[5]  Yusheng Shi,et al.  Consecutive sub-sector scan mode with adjustable scan lengths for selective laser melting technology , 2009 .

[6]  Zhigang Wang,et al.  Selective laser melting W–10 wt.% Cu composite powders , 2010 .

[7]  A. Esnaola,et al.  Study of mechanical properties of AISI 316 stainless steel processed by “selective laser melting”, following different manufacturing strategies , 2010 .

[8]  Wilhelm Meiners,et al.  Selective Laser Melting , 2012 .

[9]  Mohsen Badrossamay,et al.  Mapping and Modelling Single Scan Track Formation in Direct Metal Selective Laser Melting , 2004 .

[10]  I. Chang,et al.  Instability of scan tracks of selective laser sintering of high speed steel powder , 1999 .

[11]  Yifu Shen,et al.  Balling phenomena during direct laser sintering of multi-component Cu-based metal powder , 2007 .

[12]  Ph. Bertrand,et al.  Parametric analysis of the selective laser melting process , 2007 .

[13]  Tahar Laoui,et al.  Balling processes during selective laser treatment of powders , 2004 .

[14]  Li Wang,et al.  Densification behavior of gas and water atomized 316L stainless steel powder during selective laser melting , 2010 .

[15]  Abdolreza Simchi,et al.  Direct laser sintering of metal powders: Mechanism, kinetics and microstructural features , 2006 .

[16]  L. Froyen,et al.  Selective laser melting of iron-based powder , 2004 .

[17]  Yifu Shen,et al.  Effects of processing parameters on direct laser sintering of multicomponent Cu based metal powder , 2006 .

[18]  Yusheng Shi,et al.  Effects of processing parameters on the temperature field of selective laser melting metal powder , 2009 .

[19]  Abdolreza Simchi,et al.  Effects of laser sintering processing parameters on the microstructure and densification of iron powder , 2003 .