Recovery of internal friction in cold-worked aluminium containing 0.35 wt% Fe†

Solution treated as well as aged wires of an Al alloy containing 0.35 wt% Fe are subjected to different amounts of pre-torsional deformation up to 8% at room temperature, the internal friction Q of these wires is then measured as a function of the time following deformation. It is found that the time dependence of the decay of Q can be fairly described by an Avrami-type equation of the form: (Q – Q) = (Q – Q) exp Ktn with the time power n equals about 1/3. The decay rate K is found to take values strongly dependent on the degree of pre-deformation in case of the solution treated specimens, while such a dependence is not observed in the aged specimens. The results are essentially explained on the basis of dislocation damping. Sowohl losungsbehandelte als auch gealterte Drahte einer Al-Legierung mit 0,35 Gew% Fe werden im unterschiedlichen Grade einer Vor-Torsionsdeformation bis zu 8% bei Zimmertemperatur ausgesetzt und dann die innere Reibung Q dieser Drahte als Funktion der der Deformation folgenden Zeit gemessen. Es wird gefunden, das die Zeitabhangigkeit des Abfalls von Q sich gut durch eine Avrami-Gleichung der Form: (Q – Q) = (Q – Q) exp Ktn mit einem Zeitexponenten n von etwa 1/3 beschreiben last. Es wird gefunden, das die Abfallrate K Werte annimmt, die stark vom Grade der Vordeformation fur den Fall der losungsbehandelten Proben abhangen, wahrend eine derartige Abhangigkeit in gealterten Proben nicht beobachtet wird. Die Ergebnisse werden im wesentlichen auf der Grundlage von Versetzungsdampfung erklart.