A synergistic damage mechanics approach for composite laminates with matrix cracks in multiple orientations

Abstract This paper treats the problem of elastic response of composite laminates containing matrix cracks in plies of multiple orientations. The approach taken has been described as synergistic damage mechanics (SDM) and has been previously illustrated for [ 0 m / ± θ n / 0 m / 2 ] s laminates with cracks of equal density in + θ and - θ plies [Singh, C.V., Talreja, R., 2008. Int. J. Solids Struct. 45(16), 4574–4589]. The current work extends the approach to [ 0 m / ± θ n / 90 r ] s and [ 0 m / 90 r / ± θ n ] s laminates with cracks additionally in the 90°-plies. The interaction between the ± θ -cracks and the 90°-cracks is analyzed in terms of the crack surface displacements using a three-dimensional finite element (FE) model and found to be significant only for crack orientations close to 90°. The stiffness degradation of the laminate with all cracking modes simultaneously present is formulated by continuum damage mechanics using a second order tensor characterization of damage. The elastic moduli changes predicted by the SDM procedure are validated by independent three-dimensional FE calculations. For a particular case of quasi-isotropic [ 0 / 90 / ∓ 45 ] s laminate, the elastic moduli predictions are evaluated against experimental data. Finally, a parametric study is performed to examine the effects of ply thickness changes on stiffness properties.

[1]  Ramesh Talreja,et al.  Damage mechanics of composite materials , 1994 .

[2]  George Z. Voyiadjis,et al.  Damage in composite materials , 1993 .

[3]  Their Composites,et al.  Composite Materials: Fatigue and Fracture , 1992 .

[4]  Constantinos Soutis,et al.  Modelling stiffness degradation due to matrix cracking in angleply composite laminates , 2000 .

[5]  Constantinos Soutis,et al.  The effect of delaminations induced by transverse cracks and splits on stiffness properties of composite laminates , 2000 .

[6]  J. Vārna,et al.  Crack face sliding effect on stiffness of laminates with ply cracks , 2006 .

[7]  J. Adkins.  Symmetry relations for orthotropic and transversely isotropic materials , 1959 .

[8]  Constantinos Soutis,et al.  Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting , 2000 .

[9]  Maria Kashtalyan,et al.  Stiffness and fracture analysis of laminated composites with off-axis ply matrix cracking , 2007 .

[10]  Peter Gudmundson,et al.  An analytic model for thermoelastic properties of composite laminates containing transverse matrix cracks , 1993 .

[11]  Kenneth Reifsnider,et al.  An Investigation of Cumulative Damage Development in Quasi-Isotropic Graphite/Epoxy Laminates , 1982 .

[12]  Ramesh Talreja,et al.  Analysis of multiple off-axis ply cracks in composite laminates , 2008 .

[13]  Janis Varna,et al.  Constitutive Relationships for Laminates with Ply Cracks in In-plane Loading , 2005 .

[14]  J. Tong,et al.  On matrix crack growth in quasi-isotropic laminates—I. Experimental investigation , 1997 .

[15]  P. Gudmundson,et al.  First Order Analysis of Stiffness Reduction Due to Matrix Cracking , 1992 .

[16]  Costas Soutis,et al.  Analysis of multiple matrix cracking in [±θm/90n]s composite laminates. Part 1: In-plane stiffness properties , 1992 .

[17]  Ramesh Talreja,et al.  Damage in composite laminates with off-axis plies , 1999 .

[18]  T. Aoki,et al.  Overall thermoelastic properties of symmetric laminates containing obliquely crossed matrix cracks , 2005 .

[19]  S. L. Ogin,et al.  On matrix crack growth in quasi-isotropic laminates—II. Finite element analysis , 1997 .

[20]  J. Varna.  Physical interpretation of parameters in synergistic continuum damage mechanics model for laminates , 2008 .

[21]  K. P. Herrmann,et al.  Stiffness degradation induced by multilayer intralaminar cracking in composite laminates , 1999 .

[22]  Ramesh Talreja,et al.  Continuum modelling of damage in ceramic matrix composites , 1991 .

[23]  H. Fukuda,et al.  Progress in durability analysis of composite systems , 1996 .