Relationship between field emission property and composition of carbon nanotube paste for large area cold cathode

CNT paste was made by mixture of multi-walled carbon nanotubes (MWNT) powder, organic vehicles and inorganic binder. Then firing process was performed at different temperature under air and N/sub 2/ atmosphere. It was found that emission property of CNT paste was changed by firing temperature due to remained resin. We obtained good emission property from CNT paste treated at 350/spl deg/C.

[1] Jing Sun,et al. Production of aqueous colloidal dispersions of carbon nanotubes. , 2003, Journal of colloid and interface science.

[2] Arjun G. Yodh,et al. High Weight Fraction Surfactant Solubilization of Single-Wall Carbon Nanotubes in Water , 2003 .

[3] I. Han,et al. Fabrication and characterization of gated field emitter arrays with self-aligned carbon nanotubes grown by chemical vapor deposition , 2002 .

[4] P. Pendleton,et al. Adsorption of Anionic Surfactant by Activated Carbon: Effect of Surface Chemistry, Ionic Strength, and Hydrophobicity , 2001 .

[5] K. Esumi. Interactions between Surfactants and Particles: Dispersion, Surface Modification, and Adsolubilization. , 2001, Journal of colloid and interface science.

[6] Wonbong Choi,et al. Field emission from carbon nanotubes for displays , 2000 .

[7] Young Hee Lee,et al. Fully sealed, high-brightness carbon-nanotube field-emission display , 1999 .

[8] H. Dai,et al. Self-oriented regular arrays of carbon nanotubes and their field emission properties , 1999, Science.

[9] S. Tans,et al. Room-temperature transistor based on a single carbon nanotube , 1998, Nature.

[10] W. D. de Heer,et al. A Carbon Nanotube Field-Emission Electron Source , 1995, Science.

[11] Lian Gao,et al. Development of a dispersion process for carbon nanotubes in ceramic matrix by heterocoagulation , 2003 .