Physical, Mechanical, and Durability Properties of Concrete Containing Wood Chips and Sawdust: An Experimental Approach

With a circular economy in the spotlight, wood waste has emerged as an important secondary raw material. Bearing this in mind, a comprehensive experimental study was carried out to evaluate the feasibility of using concrete compositions containing wood chips and sawdust for structural and non-structural building applications. First, the mineral and wood aggregates used in the composite design were fully characterized. Twelve compositions containing varying types of wood particles in different amounts were then produced and characterized in terms of physical and mechanical performance (e.g., mass density, compressive strength, modulus of elasticity, and flexural strength). Subsequently, two compositions with optimized features (mass density below 2125 kg/m3, compressive strength above 25 MPa, and maximum volume content of wood) were selected to undergo additional experimental tests. These included microstructural characterization, as well as the evaluation of relevant durability (e.g., wetting–drying, freeze–thaw, and thermal shock cycles) and hygrothermal (e.g., thermal conductivity, water absorption, and shrinkage and expansion) properties. All compositions showed compressive strength above 30 MPa. The durability assessment of selected compositions further showed that compressive strength after relevant artificial aging was still higher than the predefined criteria. Promising hygrothermal properties (minimal water absorption and low thermal conductivity) were also recorded.

[1]  T. Abu-Lebdeh,et al.  Assessment of Woodcrete Using Destructive and Non-Destructive Test Methods , 2022, Materials.

[2]  C. Abid,et al.  Experimental Investigation on Mechanical and Thermal Properties of Concrete Using Waste Materials as an Aggregate Substitution , 2022, Materials.

[3]  A. Tadeu,et al.  Lightweight cement composites containing end-of-life treated wood – Leaching, hydration and mechanical tests , 2022, Construction and Building Materials.

[4]  K. Islam,et al.  Effectiveness of wood waste sawdust to produce medium- to low-strength concrete materials , 2021, Journal of Building Engineering.

[5]  A. Fadiel,et al.  Mechanical Properties of Concrete Including Wood Shavings as Fine Aggregates , 2021, American Journal of Engineering and Applied Sciences.

[6]  R. D. T. Filho,et al.  Building materials in a circular economy: The case of wood waste as CO2-sink in bio concrete , 2021 .

[7]  H. Brouwers,et al.  Bio-based ultra-lightweight concrete applying miscanthus fibers: Acoustic absorption and thermal insulation , 2020, Cement and Concrete Composites.

[8]  R. Belarbi,et al.  Utilization of treated saw dust in concrete as partial replacement of natural sand , 2020 .

[9]  Libo Yan,et al.  Behavior of adhesively bonded engineered wood – Wood chip concrete composite decks: Experimental and analytical studies , 2020 .

[10]  D. Zwicky.  Mechanical properties of organic-based lightweight concretes and their impact on economic and ecological performances , 2020, Construction and Building Materials.

[11]  M. Jalal,et al.  RETRACTED: Strength and dynamic elasticity modulus of rubberized concrete designed with ANFIS modeling and ultrasonic technique , 2020 .

[12]  Libo Yan,et al.  Interfacial bond behavior between wood chip concrete and engineered timber glued by various adhesives , 2020 .

[13]  Pablo Ballesteros-Pérez,et al.  Mechanical Properties and Seismic Performance of Wood-Concrete Composite Blocks for Building Construction , 2019, Materials.

[14]  J. Lizarazo-Marriaga,et al.  Modulus of elasticity and Poisson's ratio of fiber-reinforced concrete in Colombia from ultrasonic pulse velocities , 2019, Journal of Building Engineering.

[15]  P. Pal.  Dynamic Poisson's Ratio and Modulus of Elasticity of Pozzolana Portland Cement Concrete , 2019 .

[16]  F. Krausmann,et al.  Measuring Progress towards a Circular Economy: A Monitoring Framework for Economy‐wide Material Loop Closing in the EU28 , 2018, Journal of industrial ecology.

[17]  K. Rens,et al.  Ultrasonic wave propagation in EPS lightweight concrete and effective elastic properties , 2018, Construction and Building Materials.

[18]  Shazim Ali Memon,et al.  Effective use of sawdust for the production of eco-friendly and thermal-energy efficient normal weight and lightweight concretes with tailored fracture properties. , 2018 .

[19]  Vanderley Moacyr John,et al.  Education for sustainable use of cement based materials , 2017, Cement and Concrete Research.

[20]  M. Khelifa,et al.  Mechanical characterization of concrete containing wood shavings as aggregates , 2017 .

[21]  M. J. Morales-Conde,et al.  Physical and mechanical properties of wood-gypsum composites from demolition material in rehabilitation works , 2016 .

[22]  Francis C. Bergeron,et al.  Assessment of the coherence of the Swiss waste wood management , 2014 .

[23]  S. Zhang,et al.  Evaluation of Relationship between Water Absorption and Durability of Concrete Materials , 2014 .

[24]  S. Limkatanyu,et al.  Parawood particle cement composite boards under accelerated wet/dry cycling and natural aging , 2013 .

[25]  Stephen W. Jones,et al.  Non-destructive testing of ultra high performance fibre reinforced concrete (UHPFRC): A feasibility study for using ultrasonic and resonant frequency testing techniques , 2012 .

[26]  Taghi Tabarsa,et al.  Evaluation of using waste timber railway sleepers in wood–cement composite materials , 2012 .

[27]  Mahyuddin Ramli,et al.  The implementation of wood waste ash as a partial cement replacement material in the production of structural grade concrete and mortar: An overview , 2011 .

[28]  M. Bederina,et al.  Effect of the addition of wood shavings on thermal conductivity of sand concretes: Experimental study and modelling , 2007 .

[29]  Gert Heshe,et al.  DS/ENV 1992-1-1 NAD. National Application Document for Eurocode 2: Design of Concrete Structures, Part 1-1: General Rules and Rules for Buildings , 1993 .