A biobased photocurable binder for composites with transparency and thermal stability from biomass-derived isosorbide

A biobased photocurable binder was synthesized from isosorbide in a high yield (91%) and used as a binder for transparent glass fabric composites. The photocurable isosorbide binder showed a lower refractive index (n = 1.489) than that of glass (n = 1.560) and low viscosity (48.6 cP at 25 °C) owing to the wedge-shaped fused ring structure of the isosorbide moiety. Transparent glass fabric composites were prepared by refractive index matching using a cardo-type fluorene based binder (n = 1.583) as a co-binder. A glass fabric composite photocured with equal wt% of the cardo- and isosorbide-based binder showed 85% of transmittance at 550 nm by UV-visible spectroscopy. It also showed a considerably good coefficient of thermal expansion (α1 = 16.3 ppm K−1) and glass transition temperature (142 °C by DMA). As the wt% of the isosorbide-based binder increased, the network structure of the binder mixture became tight to give a higher glass transition temperature but the composite's transparency was decreased.

[1]  Bartosz Janicki,et al.  Synthesis and Characterization of Low Viscosity Dimethacrylic Resin Based on Isosorbide , 2013 .

[2]  Faye R Toulan,et al.  Isosorbide-methacrylate as a bio-based low viscosity resin for high performance thermosetting applications , 2013 .

[3]  J. Koo,et al.  Synthesis and Characteristics of a Biobased High-Tg Terpolyester of Isosorbide, Ethylene Glycol, and 1,4-Cyclohexane Dimethanol: Effect of Ethylene Glycol as a Chain Linker on Polymerization , 2013 .

[4]  P. Ducrot,et al.  Chemo-enzymatic preparation of new bio-based bis- and trisphenols: new versatile building blocks for polymer chemistry , 2013 .

[5]  J. Koo,et al.  Advanced Polymerization and Properties of Biobased High Tg polyester of Isosorbide and 1,4-Cyclohexanedicarboxylic Acid through in Situ Acetylation , 2013 .

[6]  A. Rozanski,et al.  Fully Isohexide-Based Polyesters: Synthesis, Characterization, and Structure–Properties Relations , 2013 .

[7]  A. Rozanski,et al.  Semicrystalline Polyesters Based on a Novel Renewable Building Block , 2012 .

[8]  Bartosz Janicki,et al.  Investigation on synthesis and properties of isosorbide based bis-GMA analogue , 2012, Journal of Materials Science: Materials in Medicine.

[9]  Regina Palkovits,et al.  Isosorbide as a renewable platform chemical for versatile applications--quo vadis? , 2012, ChemSusChem.

[10]  J. Pascault,et al.  Polymers from renewable 1,4:3,6-dianhydrohexitols (isosorbide, isomannide and isoidide): A review , 2010 .

[11]  A. N. Nakagaito,et al.  Fiber-content dependency of the optical transparency and thermal expansion of bacterial nanofiber reinforced composites , 2006 .

[12]  J. Stansbury,et al.  Synthesis and photopolymerization of low shrinkage methacrylate monomers containing bulky substituent groups. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[13]  Hiroyuki Hamada,et al.  Impact response of woven glass-fabric composites - I. Effect of fibre surface treatment , 1998 .

[14]  D. Day,et al.  Interfacial Bonding and Optical Transmission for Transparent Fiberglass/Poly(Methyl Methacrylate) Composites , 1995 .

[15]  Carlos Domínguez,et al.  Photocurable polymers applied as encapsulating materials for ISFET production , 1995 .

[16]  J. R. Olson,et al.  Fabrication and Mechanical Properties of an Optically Transparent Glass Fiber/Polymer Matrix Composite , 1992 .

[17]  P. Stoss,et al.  1,4:3,6-dianhydrohexitols. , 1993, Advances in carbohydrate chemistry and biochemistry.

[18]  J. Mays,et al.  Glass transition temperatures of polymethacrylates with alicyclic side groups , 1990 .

[19]  K. E. Reed.  Dynamic mechanical analysis of fiber reinforced composites , 1980 .