Brittle Failure Mechanism of SnAgCu and SnPb Solder Balls during High Speed Ball Shear and Cold Ball Pull Tests

This study investigated brittle solder joint failure mechanisms during high-speed solder ball shear and pull testing. BGA package samples with different solder alloys (Sn4.0%Ag0.5%Cu and Sn37%Pb) were fabricated and a series of solder ball shear and pull tests were conducted at various testing speeds. The ball shear test speeds ranged from 10 mm/s to 3000 mm/s, while the ball pull test speeds ranged from 5 mm/s to 500 mm/s. Following high-speed shear/pull testing, the brittle fracture surfaces of the solder balls and corresponding pad were inspected using SEM/EDX. The results describe an increased incidence of brittle interfacial fracture for SnAgCu solder compared to SnPb solder. Microstructure analysis of brittle solder joint fracture surfaces appears an effective method to aid correlation between board level drop test and high-speed solder ball shear/pull tests.

[1]  C. Birzer,et al.  Drop test reliability improvement of lead-free fine pitch BGA using different solder ball composition , 2005, 2005 7th Electronic Packaging Technology Conference.

[2]  A. Valota,et al.  High Speed Pull Test Characterization of BGA solder joints , 2006, EuroSime 2006 - 7th International Conference on Thermal, Mechanical and Multiphysics Simulation and Experiments in Micro-Electronics and Micro-Systems.

[3]  Tsgereda Alazar,et al.  On Measurement of Effective Silicon Backend Strength Using Bump Pull/Shear Techniques , 2005 .

[4]  Xingjia Huang,et al.  Characterization and analysis on the solder ball shear testing conditions , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[5]  S. Lee,et al.  Investigation of IMC thickness effect on the lead-free solder ball attachment strength: comparison between ball shear test and cold bump pull test results , 2006, 56th Electronic Components and Technology Conference 2006.

[6]  Y. Mai,et al.  Drop Impact: Fundamentals and Impact Characterisation of Solder Joints , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[7]  Fubin Song,et al.  High-Speed Solder Ball Shear and Pull Tests vs. Board Level Mechanical Drop Tests: Correlation of Failure Mode and Loading Speed , 2007, 2007 Proceedings 57th Electronic Components and Technology Conference.

[8]  G. Raiser,et al.  Solder Joint Reliability Improvement Using the Cold Ball Pull Metrology , 2005 .

[9]  Tai Chong Chai,et al.  The mechanics of the solder ball shear test and the effect of shear rate , 2006 .

[10]  K. Newman,et al.  BGA brittle fracture - alternative solder joint integrity test methods , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..