The effect of copper and manganese on magnetic minor hysteresis loops in neutron irradiated Fe model alloys

Abstract Changes of magnetic minor hysteresis loops in pure Fe, Fe–1 wt% Mn, Fe–0.9 wt% Cu, and Fe–0.9 wt% Cu–1 wt% Mn model alloys after neutron irradiation have been studied. Minor-loop coefficients which are obtained from scaling relations between minor-loop parameters and in proportion to internal stress, were found to decrease in all model alloys after the irradiation to a fluence of 3.32 × 1019 n cm−2. The decrease of the coefficients is larger for alloys including Cu and is enhanced by 1 wt% Mn addition. Such decrease implying the reduction of internal stress during irradiation is in contrast with changes of yield strength after the irradiation that increase with Cu and Mn contents. A qualitative explanation was given on the basis of the preferential formation of Cu precipitates along pre-existing dislocations which reduces internal stress of the dislocations.

[1]  Le-fu Zhang,et al.  Minor Hysteresis Loop in Fe Metal and Alloys , 2004 .

[2]  B. Wirth,et al.  Precipitation in neutron-irradiated Fe-Cu and Fe-Cu-Mn model alloys : a comparison of APT and SANS data , 2003 .

[3]  K. Ara,et al.  Neutron irradiation effects in Fe–Cu–Ni–Mn model alloys studied by measurements of magnetic minor hysteresis loops , 2007 .

[4]  T. Yamamoto,et al.  On the effect of dose rate on irradiation hardening of RPV steels , 2005 .

[5]  K. F. Russell,et al.  APT characterization of irradiated high nickel RPV steels , 2007 .

[6]  John B. Goodenough,et al.  A Theory of Domain Creation and Coercive Force in Polycrystalline Ferromagnetics , 1954 .

[7]  In Sup Kim,et al.  Effect of neutron irradiation on magnetic properties in the low alloy Ni-Mo steel SA508-3 , 1997 .

[8]  J. Bentley,et al.  A TEM study of neutron-irradiated iron , 1982 .

[9]  B. Wirth,et al.  Positron annihilation spectroscopy and small-angle neutron scattering characterization of the effect of Mn on the nanostructural features formed in irradiated Fe–Cu–Mn alloys , 2005 .

[10]  L. Dupré,et al.  Magnetic evaluation of the hardening and softening of thermally aged iron–copper alloys , 2007 .

[11]  H. Kronmüller,et al.  Micromagnetism and the Microstructure of Ferromagnetic Solids , 2003 .

[12]  K. Ara,et al.  The Effect of BCC-Cu Precipitation on Magnetism in Thermally Aged Fe-1wt.%Cu Model Alloys , 2007, IEEE Transactions on Magnetics.

[13]  Michael K Miller,et al.  Embrittlement of RPV steels: An atom probe tomography perspective , 2007 .

[14]  M. R. Govindaraju,et al.  Monitoring neutron embrittlement in nuclear pressure vessel steels using micromagnetic Barkhausen emissions , 1994 .

[15]  Michael Blaszkiewicz,et al.  The Development of Nondestructive Evaluation (NDE) for Monitoring the Embrittlement in Nuclear Reactor Pressure Vessels , 1996 .

[16]  G. E. Lucas,et al.  Recent progress in understanding reactor pressure vessel steel embrittlement , 1998 .

[17]  Kee-Ok Chang,et al.  Changes in magnetic parameters of neutron irradiated RPV Linde80 high copper weld surveillance specimens , 2002 .

[18]  I. Procházka,et al.  TEM and PAS study of neutron irradiated VVER-type RPV steels , 2002 .

[19]  B. Wirth,et al.  Composition and magnetic character of nanometre-size Cu precipitates in reactor pressure vessel steels: Implications for nuclear power plant lifetime extension , 2002 .

[20]  G. E. Lucas,et al.  Embrittlement of nuclear reactor pressure vessels , 2001 .

[21]  D. Jiles.  Magnetic properties and microstructure of AISI 1000 series carbon steels , 1988 .

[22]  I. M. Robertson,et al.  Low-dose neutron-irradiation damage in α-iron , 1982 .

[23]  C. Wert,et al.  Effect of Inclusions on Coercive Force of Iron , 1950 .

[24]  J. Koutský,et al.  Radiation Damage of Structural Materials , 1994 .

[25]  D. Jiles.  The effect of compressive plastic deformation on the magnetic properties of AISI 4130 steels with various microstructures , 1988 .

[26]  M. L. Hamilton,et al.  Mechanical property change in neutron irradiated Fe-Cr and Fe-Mn alloys, and their defect structures , 1994 .