The magnetic properties and microstructural evolution of Zr-doped FePt alloy films prepared by dc-magnetron sputtering were investigated. Compared to an undoped Fe59Pt41 binary film, Zr-doped FePt alloy films showed accelerated ordering transformation kinetics accompanying smaller grains: we were able to fabricate a Zr-doped FePt film [e.g., (Fe59Pt41)97Zr3] possessing very fine grain size (5 nm in average) and high coercivity (7.3 kOe) within 10 min annealing at 500 °C. It is thought that the point defects and lattice strain introduced by Zr-doping activated the nucleation rate of the ordered phase. In particular, for Zr-doped FePt films containing less than 45 at. % Pt, the ordered L10 phase was decomposed into a disordered phase after excessive annealing due to the formation of a Pt–Zr compound, most likely Pt3Zr, that reduces the effective Pt content in the ordered phase.

[1]  C. H. Park,et al.  Effects of annealing condition on the structural and magnetic properties of FePt thin films , 1999 .

[2]  Margaret Evans Best,et al.  High K/sub u/ materials approach to 100 Gbits/in/sup 2/ , 2000 .

[3]  P. Kuo,et al.  Microstructure and magnetic properties of the (FePt)100−xCrx thin films , 2000 .

[4]  S. Okamoto,et al.  Ordering and orientation of CoPt/SiO2 granular films with additive Ag , 2000 .

[5]  W. Hsu,et al.  Effects of W and Ti on the grain size and coercivity of Fe50Pt50 thin films , 2000 .

[6]  P. Kuo,et al.  Magnetic properties and microstructure of FePt–Si3N4 nanocomposite thin films , 2000 .

[7]  C. Luo,et al.  FePt:SiO2 granular thin film for high density magnetic recording , 2000 .

[8]  Laura H. Lewis,et al.  On the relationship of high coercivity and L10 ordered phase in CoPt and FePt thin films , 1999 .

[9]  Leo Brewer,et al.  A most striking confirmation of the Engel metallic correlation , 1967 .

[10]  David E. Laughlin,et al.  Fabrication and nanostructure of oriented FePt particles , 2000 .

[11]  P. J. Meschter,et al.  An investigation of high temperature thermodynamic properties in the Pt-Zr and Pt-Hf systems , 1977 .

[12]  K. Inomata,et al.  Effect of large boron additions to magnetically hard Fe‐Pt alloys , 1988 .

[13]  Kazuhiro Hono,et al.  Microstructure and magnetic properties of FePt–Al–O granular thin films , 2000 .

[14]  W. Soffa,et al.  Structure and magnetic properties of rapidly-solidified iron-platinum and iron-palladium alloys , 1990, International Conference on Magnetics.

[15]  G. Hadjipanayis,et al.  CoPt/Ag nanocomposites for high density recording media , 1998 .

[16]  Y. Liu,et al.  Nanostructure and magnetic properties of composite CoPt:C films for extremely high-density recording , 2000 .

[17]  Ibrahim Ansara,et al.  Experimental and thermodynamic assessment of the FeZr system , 1995 .