Si-N nanowire formation from Silicon nano and microparticles.

We report silicon nitride whisker formation from hydrogenated amorphous silicon (a-Si:H) nanoparticles grown by PECVD for the first time. We compared the results with the kinetics of whisker formation from ball milled crystalline silicon (c-Si) microparticles. Whisker formation is analyzed at different temperatures (900–1440 °C) and oxygen partial pressures. At temperatures equal or above 1350 C and at low oxygen partial pressure we observe monocrystalline α-Si 3 N 4 whiskers having 30–100 nm diameter and several microns length. By increasing the oxygen partial pressure, the structure of whiskers is completely changed, as shown by electron microscopy. In this case we observe α-Si 3 N 4 whiskers covered by an amorphous silica layer at 1350 C. Finally, when the precursor material is silicon microparticles, thicker (170–330 nm) and longer whiskers are formed.

[1]  M. I. Alayo,et al.  On the nitrogen and oxygen incorporation in plasma-enhanced chemical vapor deposition (PECVD) SiOxNy films , 2002 .

[2]  Jing Zhu,et al.  A simple method to synthesize Si3N4 and SiO2 nanowires from Si or Si/SiO2 mixture , 2001 .

[3]  Enric Bertran,et al.  Enhancement of oxidation rate of a-Si nanoparticles during dehydrogenation , 2001 .

[4]  Yongge Cao,et al.  Fabrication of β-Si3N4 nano-fibers , 2001 .

[5]  Hongliang He,et al.  Shock-induced transformation of β-Si3N4 to a high-pressure cubic-spinel phase , 2000 .

[6]  Jing Zhu,et al.  Reversible bending of Si_3N_4 nanowire , 2000 .

[7]  Zhangjian Zhou,et al.  Combustion synthesis of α–Si_3N_4 whiskers , 1999 .

[8]  R. Riedel,et al.  Progress in silicon-based non-oxide structural ceramics , 1997 .

[9]  T. Araki,et al.  Preparation of Microcoiled Si3 N 4 Fibers by Impurity Metal Activated Chemical Vapor Deposition and Their Mechanical Properties , 1995 .

[10]  M. A. Rodríguez,et al.  Single crystal ß‐Si3N4 fibers obtained by self‐propagating high temperature synthesis** , 1995 .

[11]  C. Kawai,et al.  Preparation of fibre-like silicon nitride from amorphous silicon nitride powder , 1995 .

[12]  P. Ramesh,et al.  Carbothermal reduction and nitridation reaction of SiO_x and preoxidized SiO_x: Formation of α-Si_3N_4 fibers , 1994 .

[13]  P. Gopalakrishnan,et al.  Preparation of fibre-like silicon nitride from silicon powder , 1993 .

[14]  H. Wada,et al.  Synthesis and characterization of silicon nitride whiskers , 1990 .

[15]  N. Setaka,et al.  Preparation of silicon nitride single crystals by chemical vapor deposition , 1974 .

[16]  P. Wong,et al.  Kinetics of Nitridation of Si Powder Compacts , 1973 .