Convenient architectures of Cu2O/SnO2 type II p-n heterojunctions and their application in visible light catalytic degradation of rhodamine B

3D hierarchical heterostructures of p-type Cu2O/n-type SnO2 were synthesized by impregnating porous SnO2 nanospheres with different weight percentages of Cu2O by a simple hydrothermal route. The heterostructures were then evaluated for their photocatalytic performance under visible light irradiation for degradation of rhodamine B (RhB), an organic pollutant. In addition, the effect of varying Cu2O content, and thereby the composition, morphology and photocatalytic activity of the Cu2O/SnO2 nanocomposite were investigated. XRD revealed that the Cu2O/SnO2 nanocomposite comprised of cassiterite tetragonal structured SnO2 and cubic structured Cu2O. HR-TEM and FE-SEM of the as synthesized nanocomposite indicated nearly monodispersed nanospheres with an average size around 60 nm. A UV-vis absorption edge of the Cu2O/SnO2 nanocomposite synthesized in a 1 : 1 ratio was observed at 484 nm (Eg ∼ 2.56 eV) that indicated considerable absorption in the visible region of the solar spectrum. An enhancement in photocatalytic activity was observed with an increase in Cu2O impregnation and the complete photo-oxidation of RhB was possible with the 1 : 1 mole ratio Cu2O/SnO2 nanocomposite in 90 min under optimized conditions. Photocatalytic activity of the Cu2O/SnO2 nanocomposite for the degradation of RhB was much higher than that of individual nanoparticles, primarily attributed to the anti-recombination effect of photogenerated electrons and holes at the junction due to formation of p–n heterojunctions. Identification of intermediates and a detailed mechanism of the photo-oxidation process was accomplished by using analytical techniques such as high-performance liquid chromatography [HPLC] and UV-vis diffuse reflectance [DR] spectroscopy.

[1]  Xinghua Li,et al.  Electrospun nanofibers of p-type NiO/n-type ZnO heterojunctions with enhanced photocatalytic activity. , 2010, ACS applied materials & interfaces.

[2]  D. Yuan,et al.  Luminescent properties of Mn2+-doped SnO2 nanoparticles , 2003 .

[3]  D. Goodman,et al.  Oxidation Catalysis by Supported Gold Nano-Clusters , 2002 .

[4]  Kaixun Huang,et al.  Self-assembly synthesis of single-crystalline tin oxide nanostructures by a poly(acrylic acid)-assisted solvothermal process. , 2006, The journal of physical chemistry. B.

[5]  Kalyan Kumar Chattopadhyay,et al.  Excellent Photocatalytic Activity of Mixed Phase Ultra Slim TiO2 Nanofibers for the Degradation of Organic Wastes , 2012 .

[6]  J. Leckie,et al.  An efficient bicomponent TiO2/SnO2 nanofiber photocatalyst fabricated by electrospinning with a side-by-side dual spinneret method. , 2007, Nano letters.

[7]  S. Manorama,et al.  Influence of morphology and surface characteristics on the photocatalytic activity of rutile titania nanocrystals , 2008 .

[8]  S. Manorama,et al.  Hierarchical mesoporous In2O3 with enhanced CO sensing and photocatalytic performance: distinct morphologies of In(OH)3 via self assembly coupled in situ solid-solid transformation. , 2015, ACS applied materials & interfaces.

[9]  S. Kondawar,et al.  Nanostructure cobalt oxide reinforced conductive and magnetic polyaniline nanocomposites , 2013 .

[10]  Peng Zhang,et al.  High photocatalytic activity of ZnO-carbon nanofiber heteroarchitectures. , 2011, ACS applied materials & interfaces.

[11]  R. Hegde.  Core level binding energy shifts in dilute tin alloys , 1982 .

[12]  Nguyen Duc Hoa,et al.  Design of SnO2/ZnO hierarchical nanostructures for enhanced ethanol gas-sensing performance , 2012 .

[13]  K. Chattopadhyay,et al.  Three dimensional Ag2O/TiO2 type-II (p-n) nanoheterojunctions for superior photocatalytic activity. , 2013, ACS applied materials & interfaces.

[14]  Vinod Kumar,et al.  The role of surface and deep-level defects on the emission of tin oxide quantum dots , 2014, Nanotechnology.

[15]  Z. Shao,et al.  Fabrication of CuO/ZnO composite films with cathodic co-electrodeposition and their photocatalytic performance , 2010 .

[16]  S. S. Kim,et al.  Novel growth of CuO-functionalized, branched SnO2 nanowires and their application to H2S sensors , 2012 .

[17]  D. S. Misra,et al.  Defect‐Related Emissions and Magnetization Properties of ZnO Nanorods , 2010 .

[18]  L. Tjeng,et al.  Electronic structure of Cu2O and CuO. , 1988, Physical review. B, Condensed matter.

[19]  M. Islam,et al.  Electron affinity and work function of polycrystalline SnO2 thin film , 1986 .

[20]  M. Stroscio,et al.  Observation of ultraviolet emission and effect of surface states on the luminescence from tin oxide nanowires , 2009 .

[21]  Qi Li,et al.  Synthesis of Cu₂O nanospheres decorated with TiO₂ nanoislands, their enhanced photoactivity and stability under visible light illumination, and their post-illumination catalytic memory. , 2014, ACS applied materials & interfaces.

[22]  K. Ogle,et al.  The acid–base properties of the surface of native zinc oxide layers: An XPS study of adsorption of 1,2-diaminoethane , 2007 .

[23]  Hyung-Wook Ha,et al.  Fluorine-doped nanocrystalline SnO2 powders prepared via a single molecular precursor method as anode materials for Li-ion batteries , 2006 .

[24]  A. Walcarius,et al.  Sorption of Iodide on Cuprite (Cu2O) , 2000 .

[25]  Guo-Qiang Lo,et al.  An inverted organic solar cell employing a sol-gel derived ZnO electron selective layer and thermal evaporated MoO3 hole selective layer , 2008 .

[26]  Yong-Mook Kang,et al.  Preparation and electrochemical properties of SnO2 nanowires for application in lithium-ion batteries. , 2007, Angewandte Chemie.

[27]  Dongfang Zhang.  Synergetic effects of Cu2O photocatalyst with titania and enhanced photoactivity under visible irradiation , 2013 .

[28]  M. Hon,et al.  Electrodeposition of nanocrystalline SnO2 coatings with two-layer microstructure , 2004 .

[29]  Moo Hwan Cho,et al.  Oxygen vacancy induced band gap narrowing of ZnO nanostructures by an electrochemically active biofilm. , 2013, Nanoscale.

[30]  J. Jang,et al.  Heterojunction semiconductors: A strategy to develop efficient photocatalytic materials for visible light water splitting , 2012 .

[31]  M. F. Abdel-Messih,et al.  Photocatalytic decolorization of Rhodamine B dye using novel mesoporous SnO2–TiO2 nano mixed oxides prepared by sol–gel method , 2013 .

[32]  A. Gambhire,et al.  Visible-light-activated nanocomposite photocatalyst of Cr2O3/SnO2 , 2013, Journal of Nanostructure in Chemistry.

[33]  C. Carabatos,et al.  Near infrared optical and photoelectric properties of Cu2O. I. Infrared absorption in Cu2O after annealing in oxygen or He+ particles bombardments , 1972 .

[34]  V. Roy,et al.  Tube-like ternary α-Fe2O3@SnO2@Cu2O sandwich heterostructures: synthesis and enhanced photocatalytic properties. , 2014, ACS applied materials & interfaces.

[35]  S. Phanichphant,et al.  Photocatalytic Degradation of Methyl Orange by CeO2 and Fe–doped CeO2 Films under Visible Light Irradiation , 2014, Scientific Reports.

[36]  M. Leung,et al.  Template-free synthesis of hierarchical porous SnO2 , 2010 .

[37]  Tao Zhang,et al.  Photocatalytic degradation of Acid Blue 62 over CuO-SnO2 nanocomposite photocatalyst under simulated sunlight. , 2007, Journal of environmental sciences.

[38]  Jinhua Ye,et al.  Nitrogen‐doped Lamellar Niobic Acid with Visible Light‐responsive Photocatalytic Activity , 2008 .

[39]  Role of ambient air on photoluminescence and electrical conductivity of assembly of ZnO nanoparticles , 2011, 1109.2253.

[40]  A. Kareiva,et al.  XRD and FTIR characterisation of historical green pigments and their lead-based glazes , 2014 .

[41]  A. Govind,et al.  Optical and photocatalytic properties of heavily F(-)-doped SnO2 nanocrystals by a novel single-source precursor approach. , 2011, Inorganic chemistry.

[42]  D. Bahadur,et al.  Influence of confinement regimes on magnetic property of pristine SnO2 quantum dots , 2012 .

[43]  E. Samulski,et al.  Large-Scale, solution-phase growth of single-crystalline SnO2 nanorods. , 2004, Journal of the American Chemical Society.

[44]  Aivaras Kareiva,et al.  Spectroscopic analysis of blue cobalt smalt pigment , 2010 .

[45]  D. Goodman,et al.  Correlation of Relative X-ray Photoelectron Spectroscopy Shake-up Intensity with CuO Particle Size , 1999 .

[46]  S. Manorama,et al.  Facile Synthesis of Face Oriented ZnO Crystals: Tunable Polar Facets and Shape Induced Enhanced Photocatalytic Performance , 2013 .

[47]  Dongfang Zhang.  Photobleaching of pollutant dye catalyzed by p-n junction ZnO-CuO photocatalyst under UV-visible light activation , 2012, Russian Journal of Physical Chemistry A.

[48]  S. Manorama,et al.  A facile and green approach for the controlled synthesis of porous SnO₂ nanospheres: application as an efficient photocatalyst and an excellent gas sensing material. , 2012, ACS applied materials & interfaces.

[49]  Dmitri Golberg,et al.  Laser‐Ablation Growth and Optical Properties of Wide and Long Single‐Crystal SnO2 Ribbons , 2003 .

[50]  Jinzhao Huang,et al.  Morphology-modulation of SnO2 Hierarchical Architectures by Zn Doping for Glycol Gas Sensing and Photocatalytic Applications , 2015, Scientific Reports.

[51]  Yujie Feng,et al.  Synthesis of visible-light responsive graphene oxide/TiO(2) composites with p/n heterojunction. , 2010, ACS nano.

[52]  M. J. Weaver,et al.  ELECTROCHEMICAL CONTROL OF GAS-PHASE OXIDATION AND REDUCTION OF COPPER AS PROBED BY SURFACE-ENHANCED RAMAN SPECTROSCOPY , 1999 .

[53]  Yimei Zhu,et al.  Copper oxide nanocrystals. , 2005, Journal of the American Chemical Society.

[54]  M. A. Hasan,et al.  Influence of CuOx additives on CO oxidation activity and related surface and bulk behaviours of Mn2O3, Cr2O3 and WO3 catalysts , 2000 .

[55]  J. Kang,et al.  Fabrication of the SnO2/α-Fe2O3 Hierarchical Heterostructure and Its Enhanced Photocatalytic Property , 2011 .

[56]  F. Su,et al.  Heterojunctions generated in SnO2–CuO nanocatalysts for improved catalytic property in the Rochow reaction , 2015 .

[57]  R. Sathyamoorthy,et al.  Flower-shaped CuO Nanostructures: Synthesis, Characterization and Antimicrobial Activity , 2013 .

[58]  W. S. Li,et al.  Raman spectra of CuO nanocrystals , 1999 .

[59]  S. Manorama,et al.  Viable method for the synthesis of biphasic TiO2 nanocrystals with tunable phase composition and enabled visible-light photocatalytic performance. , 2012, ACS applied materials & interfaces.

[60]  D. Kang,et al.  Facile synthesis of core–shell SnO2/V2O5 nanowires and their efficient photocatalytic property , 2010 .

[61]  Bing Xie,et al.  Photocatalytic H2 production from acetic acid solution over CuO/SnO2 nanocomposites under UV irradiation , 2010 .

[62]  H. Seema,et al.  Graphene–SnO2 composites for highly efficient photocatalytic degradation of methylene blue under sunlight , 2012, Nanotechnology.

[63]  S. G. Kumar,et al.  Zinc oxide based photocatalysis: tailoring surface-bulk structure and related interfacial charge carrier dynamics for better environmental applications , 2015 .

[64]  W. Jaegermann,et al.  Nanostructured SnO2-ZnO heterojunction photocatalysts showing enhanced photocatalytic activity for the degradation of organic dyes. , 2012, Inorganic chemistry.

[65]  K. Parida,et al.  Fabrication of novel p-BiOI/n-ZnTiO3 heterojunction for degradation of rhodamine 6G under visible light irradiation. , 2013, Inorganic chemistry.

[66]  Shengtao Jiang,et al.  Effective Decolorization of Azo Dye Utilizing SnO2/CuO/Polymer Films under Simulated Solar Light Irradiation , 2011 .

[67]  A. Majid,et al.  Characterization of CuO phase in SnO2–CuO prepared by the modified Pechini method , 2010 .

[68]  Bai Xu,et al.  Preparation and photocatalytic properties of mesoporous SnO2-hexaniobate layered nanocomposite , 2010 .

[69]  Christos G. Takoudis,et al.  OXIDE FILM FORMATION AND OXYGEN ADSORPTION ON COPPER IN AQUEOUS MEDIA AS PROBED BY SURFACE-ENHANCED RAMAN SPECTROSCOPY , 1999 .

[70]  Panagiotis Lianos,et al.  Production of electricity and hydrogen by photocatalytic degradation of organic wastes in a photoelectrochemical cell: the concept of the Photofuelcell: a review of a re-emerging research field. , 2011, Journal of hazardous materials.

[71]  X. Jiao,et al.  CuO microflowers composed of nanosheets: Synthesis, characterization, and formation mechanism , 2007 .

[72]  Weihua Tang,et al.  CTAB-assisted synthesis and photocatalytic property of CuO hollow microspheres , 2009 .

[73]  Jing Ouyang,et al.  CuO nanoparticles encapsulated inside Al-MCM-41 mesoporous materials via direct synthetic route , 2014, Scientific Reports.

[74]  S. Manorama,et al.  Hierarchical SnO/SnO2 nanocomposites: Formation of in situ p–n junctions and enhanced H2 sensing , 2013 .

[75]  J. Chrzanowski,et al.  Raman scattering from cupric oxide , 1989 .

[76]  Yu,et al.  Raman study of CuO single crystals. , 1990, Physical review. B, Condensed matter.

[77]  Jun Yu Li,et al.  Designed synthesis of a novel BiVO₄-Cu₂O-TiO₂ as an efficient visible-light-responding photocatalyst. , 2015, Journal of colloid and interface science.

[78]  K. Yu,et al.  MICROSTRUCTURAL CHANGE OF NANO-SNO2 GRAIN ASSEMBLAGES WITH THE ANNEALING TEMPERATURE , 1997 .

[79]  Shu-fen Li,et al.  Study on thermal decomposition of copper(II) acetate monohydrate in air , 2012, Journal of Thermal Analysis and Calorimetry.

[80]  S. Supothina,et al.  Characterization of SnO2 thin films grown from aqueous solutions , 2000 .

[81]  Jinhua Ye,et al.  A comparison study of rhodamine B photodegradation over nitrogen-doped lamellar niobic acid and titanic acid under visible-light irradiation. , 2009, Chemistry.

[82]  Yongfa Zhu,et al.  Visible Photocatalytic Activity Enhancement of ZnWO4 by Graphene Hybridization , 2012 .

[83]  Wen Zhu,et al.  Photogenerated electron reservoir in hetero-p–n CuO–ZnO nanocomposite device for visible-light-driven photocatalytic reduction of aqueous Cr(VI) , 2015 .

[84]  C. Pan,et al.  TiO2/graphene composite from thermal reaction of graphene oxide and its photocatalytic activity in visible light , 2011 .

[85]  Cheng Sun,et al.  Visible light-driven photocatalytic degradation of rhodamine B over NaBiO3: pathways and mechanism. , 2009, The journal of physical chemistry. A.

[86]  Y. Qian,et al.  Preparation, characterization and application of a new kind of mesoporous composite , 2006 .

[87]  B. Mehta,et al.  Surface-modified CuO layer in size-stabilized single-phase Cu2O nanoparticles , 2001 .

[88]  Li Xu,et al.  Preparation of sphere-like g-C3N4/BiOI photocatalysts via a reactable ionic liquid for visible-light-driven photocatalytic degradation of pollutants , 2014 .