In-line AFM characterization of STI profile at the 65 nm node with advanced carbon probes

The present paper shows the characterization of the shallow trench isolation (STI) profile of 65 nm node ULSI logic products done with an automated AFM system and high-density carbon tips. The combined utilisation of special tips and dedicated analysis algorithms has allowed the precise measurement of both the step height between the isolation oxide and the silicon active area, and the depth of the divot that is generally formed at the isolation oxide's sidewalls. Moreover, the robustness of this methodology has been assessed by evaluating the maximum number measurement runs before the appearance of relevant artifacts due to tips' apex modifications. Finally, TEM cross-sections were run in order to determine the accuracy of the measurements.

Jean-Claude Royer | Massimo D. Sardo | Audrey Berthoud | Christian Kusch

[1] Alain C. Diebold,et al. Handbook of Silicon Semiconductor Metrology , 2009 .

[2] J. Kotthaus,et al. Sharpened electron beam deposited tips for high resolution atomic force microscope lithography and imaging , 1995 .

[3] C. W. Hagen,et al. High-resolution electron-beam-induced deposition , 2008 .

[4] J. H. Yeh,et al. Using in-line AFM to monitor STI profile in 65-nm technology development , 2006, SPIE Advanced Lithography.

[5] P. Hoffmann,et al. Mechanical properties of high-aspect-ratio atomic-force microscope tips , 2002 .

[6] Single-walled carbon nanotube probes for AFM imaging , 2004, 17th IEEE International Conference on Micro Electro Mechanical Systems. Maastricht MEMS 2004 Technical Digest.