Wear progression of carbide tool in low-speed end milling of stainless steel

A study was undertaken to investigate the wear of PVD-coated carbide and uncoated carbide tools during milling of STAVAX (modified AISI 420 stainless steel) at low speeds. No significant change in the tool wear was observed when the cutting speed was increased from 25 to 50 m/min. It was found that increasing the hardness of the workpiece from 35 to 55 HRC caused a marked increase in the flank wear and a change in the dominant wear mechanism. In machining STAVAX with a hardness of 35 and 40 HRC, the coated tool was predominantly subjected to abrasive wear throughout the duration of testing. During machining STAVAX with a hardness of 55 HRC with the coated tool, three distinct stages of tool wear occurred, (i) initial wear by abrasion, followed by (ii) cracking and chipping, and (iii) the formation of individual surface fracture at the cracks which would then enlarge and coalesce to form a large fracture surface. The coated tool showed much higher fracture resistance than the uncoated tool. The high fracture resistance exhibited by the coated tool could be attributed to the effectiveness of the coating in preventing the formation of cracks which would act as preferential sites for fracture to take place. The experimental results also show that coating prevents edge chipping and enhances the abrasive wear resistance of the tool. Both the ductility of the workpiece and the tool wear appeared to have influences on the surface finish of the workpiece. It was found that the cutting fluid was effective in preventing catastrophic failure of the tool.

[1]  Mohammed Nouari,et al.  Experimental verification of a diffusion tool wear model using a 42CrMo4 steel with an uncoated cemented tungsten carbide at various cutting speeds , 2005 .

[2]  H. S. Shan,et al.  Thermal cracking of carbide tools during intermittent cutting , 1978 .

[3]  Jining He,et al.  Microhardness and toughness of the TiN coating prepared by reactive plasma spraying , 2005 .

[4]  H. Shao,et al.  Machinability study on 3%Co–12%Cr stainless steel in milling , 2007 .

[5]  M. Silva,et al.  Some observations on wear and damages in cemented carbide tools , 2006 .

[6]  V. Marinov,et al.  Experimental study on the abrasive wear in metal cutting , 1996 .

[7]  J. A. Bailey,et al.  Surface Integrity in Machining Solution-Treated and Aged 2024-Aluminum Alloy, Using Natural and Controlled Contact Length Tools. Part I—Unlubricated Conditions , 1984 .

[8]  G. Fox-Rabinovich,et al.  Hard AlTiN, AlCrN PVD coatings for machining of austenitic stainless steel , 2006 .

[9]  Kim Seng Lee,et al.  Wear of TiC-coated carbide tools in dry turning , 1999 .

[10]  Janez Kopac,et al.  Wear mechanisms of cutting tools in high-speed cutting processes , 2001 .

[11]  S. H. Yeo,et al.  Wear of CBN Tools in Ultra-Precision Machining of STAVAX , 2002 .

[12]  P. C. Pandey,et al.  The thermal condition of the tool cutting edge in intermittent cutting , 1980 .

[13]  S. Tung,et al.  Tool life and wear mechanism of uncoated and coated milling inserts , 1999 .

[14]  Ning Liu,et al.  The milling performances of TiC-based cermet tools with TiN nanopowders addition against normalized medium carbon steel AISI1045 , 2005 .

[15]  Y. G. Lu,et al.  Performance of Uncoated and Coated Carbide Tools in the Ultra-Precision Machining of Stainless Steel , 2004 .

[16]  Bryan Kok Ann Ngoi,et al.  Wear characteristics of PCBN tools in the ultra-precision machining of stainless steel at low speeds , 2003 .

[17]  L. A. Dobrzański,et al.  Wear of PVD-coated solid carbide end mills in dry high-speed cutting , 2004 .

[18]  Bryan Kok Ann Ngoi,et al.  Evaluation of machining performance of STAVAX with PCBN tools , 2004 .

[19]  Álisson Rocha Machado,et al.  Performance of cutting fluids during face milling of steels , 2001 .

[20]  S. Hogmark,et al.  Wear and failure mechanisms of multilayered PVD TiN/TaN coated tools when milling austenitic stainless steel , 2000 .

[21]  M. Stoudt,et al.  SUPPRESSION OF FATIGUE CRACKING WITH NANOMETER-SCALE MULTILAYERED COATINGS , 2000 .

[22]  Imtiaz Ahmed Choudhury,et al.  Wear mechanism of TiN coated carbide and uncoated cermets tools at high cutting speed applications , 2004 .

[23]  K. Abou-El-Hossein,et al.  High-speed end-milling of AISI 304 stainless steels using new geometrically developed carbide inserts , 2005 .

[24]  Bo Chen,et al.  Adhering wear mechanism of cemented carbide cutter in the intervallic cutting of stainless steel , 1998 .

[25]  M. Arndt,et al.  Performance of new AlTiN coatings in dry and high speed cutting , 2003 .