Silicon heterojunction solar cell: a new buffer Layer concept with low-temperature epitaxial silicon

Amorphous silicon/crystalline silicon heterojunction solar cells, deposited by the plasma-enhanced chemical vapor deposition (PECVD) technique, have been fabricated using different technologies to passivate defects at the heterointerface: without treatment, the insertion of a thin intrinsic amorphous layer or that of a thin intrinsic epitaxial layer. The open circuit voltage of heterojunction solar cells fabricated including an intrinsic amorphous buffer layer is strangely lower than in devices with no buffer layer. The structure of the amorphous buffer layer is investigated by high resolution transmission electron microscope observations. As an alternative to amorphous silicon, the insertion of a fully epitaxial silicon layer, deposited at low temperature with conventional PECVD technique in a hydrogen-silane gas mixture, was tested. Using the amorphous silicon/crystalline silicon (p a-Si/i epi-Si/n c-Si) heterojunction structure in solar cells, a 13.5% efficiency and a 605-mV open circuit voltage were achieved on flat Czochralski silicon substrates. These results demonstrate that epitaxial silicon can be successfully used to passivate interface defects, allowing for an open circuit voltage gain of more than 50 mV compared to cells with no buffer layer. In this paper, the actual structure of the amorphous silicon buffer layer used in heterojunction solar cells is discussed. We make the hypothesis that this buffer layer, commonly considered amorphous, is actually epitaxial.

[1]  S. Vepřek,et al.  Highlights of preparative solid state chemistry in low pressure plasmas , 1982 .

[2]  Makoto Tanaka,et al.  Development of New a-Si/c-Si Heterojunction Solar Cells: ACJ-HIT (Artificially Constructed Junction-Heterojunction with Intrinsic Thin-Layer) , 1992 .

[3]  T. Sawada,et al.  High-efficiency a-Si/c-Si heterojunction solar cell , 1994, Proceedings of 1994 IEEE 1st World Conference on Photovoltaic Energy Conversion - WCPEC (A Joint Conference of PVSC, PVSEC and PSEC).

[4]  Very Low Temperature Epitaxial Growth of -type Silicon for Solar Cells , 1995 .

[5]  E. Centurioni,et al.  Influence of Front Contact Material on Silicon Heterojunction Solar Cell Performance , 1997 .

[6]  M. Gemmi,et al.  Very high frequency hydrogen plasma treatment of growing surfaces: a study of the p-type amorphous to microcrystalline silicon transition , 2000 .

[7]  M. Taguchi,et al.  HITTM cells—high-efficiency crystalline Si cells with novel structure , 2000 .

[8]  Ralf B. Bergmann,et al.  Optimization and characterization of amorphous/crystalline silicon heterojunction solar cells , 2002 .

[9]  R. Hussein,et al.  Comparison of multicrystalline silicon surfaces after wet chemical etching and hydrogen plasma treatment: application to heterojunction solar cells , 2002 .

[10]  E. Centurioni,et al.  Homojunction and heterojunction silicon solar cells deposited by low temperature-high frequency plasma enhanced chemical vapour deposition , 2002 .

[11]  M. Tanaka,et al.  Development of hit solar cells with more than 21% conversion efficiency and commercialization of highest performance hit modules , 2003, 3rd World Conference onPhotovoltaic Energy Conversion, 2003. Proceedings of.

[12]  E. Centurioni,et al.  Thin film silicon materials and solar cells grown by pulsed PECVD technique , 2003 .

[13]  E. Centurioni,et al.  Role of front contact work function on amorphous silicon/crystalline silicon heterojunction solar cell performance , 2003, IEEE Electron Device Letters.

[14]  A. Froitzheim,et al.  Design criteria for amorphous/crystalline silicon heterojunction solar cells - a simulation study , 2003, 3rd World Conference onPhotovoltaic Energy Conversion, 2003. Proceedings of.

[15]  E. Centurioni,et al.  Silicon heterojunction solar cells with p nanocrystalline thin emitter on monocrystalline substrate , 2004 .

[16]  F. Palma,et al.  Comparison of amorphous/crystalline heterojunction solar cells based on n- and p-type crystalline silicon , 2004 .