Characterisation and milling time optimisation of nanocrystalline aluminium powder for selective laser melting

The aim of this study is to investigate the properties of high-energy ball-milled nanocrystalline aluminium powders and to determine the optimum milling time required to produce an advanced aluminium powder for selective laser melting (SLM). Previous research has indicated that powders suitable for SLM include milled nanocrystalline aluminium powders with an average grain size of 60 nm and good flowability (Carr index less than 15 %). This study employs advanced nanometrology methods and analytical techniques to investigate the powder morphology, phase identification, average grain size and flowability of ball-milled powders. Stearic acid is used to prevent excessive cold welding of the ball-milled powder and to reduce abrasion of the grinding bowl and balls. The results indicate that, whilst the average particle size achieves a steady state after 14 h of milling, the grain size continues to decrease as the milling time progressed (e.g. the transmission electron microscopy measured average grain size is 56 nm after 20 h of milling compared to 75 nm for 14 h of milling). The aluminium powders milled for 16 and 20 h exhibit good flow behaviour, achieving a Carr index of 13.5 and 15.8 %, respectively. This study shows that advanced nanocrystalline aluminium powders suitable for SLM require ball milling for between 16 and 20 h, with 18 h being the optimum milling time.

[1]  Daniel Roy Eyers,et al.  Assessment of non-uniform shrinkage in the laser sintering of polymer materials , 2013 .

[2]  F. G. Cuevas,et al.  High-strength PM aluminium by milling in ammonia gas and sintering , 2005 .

[3]  R. Poprawe,et al.  Laser additive manufacturing of metallic components: materials, processes and mechanisms , 2012 .

[4]  M. Tan,et al.  Mixing of carbon nanotubes (CNTs) and aluminum powder for powder metallurgy use , 2011 .

[5]  D. L. Zhang,et al.  Processing of advanced materials using high-energy mechanical milling , 2004 .

[6]  C. Koch,et al.  Formation of amorphous Ni-Zr alloy powder by mechanical alloying of intermetallic powder mixtures and mixtures of nickel or zirconium with intermetallics , 1988 .

[7]  A. Al-Azzawi,et al.  Mechanical Alloying and Milling , 2015 .

[8]  J. A. Rodríguez,et al.  Structure and properties of attrition-milled aluminium powder , 1997 .

[9]  D. Bae,et al.  Tensile behavior of bulk nanocrystalline aluminum synthesized by hot extrusion of ball-milled powders , 2008 .

[10]  J. Kruth,et al.  Fine-structured aluminium products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder , 2013 .

[11]  R. Setchi,et al.  Synthesis and characterisation of advanced ball-milled Al-Al2O3 nanocomposites for selective laser melting , 2016 .

[12]  Mansour Razavi,et al.  Production of Al–20 wt.% Al2O3 composite powder using high energy milling , 2009 .

[13]  R. Drew,et al.  Fabrication and properties of mechanically milled alumina/aluminum nanocomposites , 2010 .

[14]  L. Takács,et al.  Effect of grain refinement on mechanical properties of ball-milled bulk aluminum , 2008 .

[15]  F. G. Cuevas,et al.  Influence of milling media on the microstructure and mechanical properties of mechanically milled and sintered aluminium , 2005 .

[16]  Ihar Yadroitsau,et al.  Direct manufacturing of 3D objects by selective laser melting of metal powders , 2008 .

[17]  J. Benjamin Dispersion strengthened superalloys by mechanical alloying , 1970, Metallurgical and Materials Transactions B.

[18]  R L Carr,et al.  CLASSIFYING FLOW PROPERTIES OF SOLIDS , 1965 .

[19]  Vinod Yadava,et al.  Finite element analysis of temperature distribution in single metallic powder layer during metal laser sintering , 2007 .

[20]  Farghalli A. Mohamed,et al.  Particulate reinforced metal matrix composites — a review , 1991, Journal of Materials Science.

[21]  K. A. Padmanabhan Mechanical properties of nanostructured materials , 2001 .