Fine Size YAG:Tb Phosphor Particles Prepared by Spray Pyrolysis

− YAG:Tb(Y 3 Al 5 O 12 :Tb) phosphor particles were prepared by spray pyrolysis from spray solution containing various types of flux materials. The effects of type of flux, organic material and post-treatment temperature on the characteristics of morphology, crystallinity and photoluminescence of YAG:Tb phosphor particles were investigated. Citric acid and ethylene glycol used as organic additive improved the photoluminescence intensity of the YAG:Tb phosphor particles without destruction of the morphology after post-treatment at high temperature. However, the spherical shape of the precursor particles obtained by spray pyrolysis from spray solution containing high amount of flux material disappeared after post-treatment at 1300C. YAG:Tb phosphor particles prepared from spray solution containing lithium carbonate flux had fine size and regular morphology after post-treatment. Lithium carbonate used as flux material was also efficient in improvement of the photoluminescence intensity of the YAG:Tb phosphor particles. The optimum photoluminescence intensity of the YAG:Tb phosphor particles prepared from spray solution containing lithium carbonate flux was 189% of that of the phosphor particles prepared from spray solution without flux material.