Low velocity impact response of carbon fiber laminates fabricated by pulsed infusion: A review of damage investigation and semi-empirical models validation

Abstract The research reported in this paper was aimed mainly to investigate the different NDE techniques on specimens made by a new process labeled as “pulsed infusion”, very crucial for voids content under critical loading conditions. The impact load, in fact, is critical for composite laminates due to their anisotropy, in particular in extreme temperature conditions due to their brittleness. An additional and very relevant aim was to collect a large number of experimental results to supply useful information for the numerical models needed to simulate the dynamic behavior of composite laminates. At the aim to investigate the response under dynamic loads of laminates fabricated by a new vacuum assisted technology labeled as “pulsed infusion”, rectangular carbon fiber composite specimens were subjected to low velocity impact tests. Experimental tests up to complete penetration and at different energy levels, were carried out by a modular falling weight tower. All the parameters related to the phenomenon, like penetration energy, maximum force and indentation depths, were used to validate existing semi-empirical and numerical models. The largely used ultra sound technique (US) was adopted to investigate the delamination together with the thermo graphic technique. The results of the measurements were compared with data obtained on the same specimens by holographic analysis (ESPI). One of the scope was to investigate the crucial internal impact damage and assess the ability of an unconventional ND system (ESPI) in giving right information about non-visual damage generated inside composite laminates subjected to dynamic loads. Moreover, some of the specimens were cut to allow the fractographic analysis. The efficiency of the above mentioned new fabrication technology was studied also comparing the results with measurements from literature on impacted autoclave cured laminates. By the comparison between the results, good agreements were found denoting the efficiency and the applicability of the new fabrication and the used NDE methods.

[1]  Valentina Lopresto,et al.  On the penetration energy for fibre-reinforced plastics under low-velocity impact conditions , 2001 .

[2]  G.A.O. Davies,et al.  Numerical modelling of impact damage , 1994 .

[3]  Gerd Busse,et al.  Optoacoustic phase angle measurement for probing a metal , 1979 .

[4]  J. Vārna,et al.  Optically measured full-field displacements on the edge of a cracked composite laminate , 2008 .

[5]  S. Putic,et al.  The influence of high and low temperatures on the impact properties of glass-epoxy composites , 2007 .

[6]  Valentina Lopresto,et al.  Influence of material thickness on the response of carbon-fabric/epoxy panels to low velocity impact , 1999 .

[7]  X. Zhang,et al.  IMPACT DAMAGE PREDICTION IN CARBON COMPOSITE STRUCTURES , 1995 .

[8]  E. Antonucci,et al.  A Global–Local Numerical Model for the Prediction of Impact Induced Damage in Composite Laminates , 2014, Applied Composite Materials.

[9]  Aniello Riccio,et al.  Delamination buckling and growth phenomena in stiffened composite panels under compression. Part I: An experimental study , 2014 .

[10]  Said Rechak,et al.  Modelling of damage and failure of glass/epoxy composite plates subject to impact fatigue , 2001 .

[11]  X. Zhang,et al.  Impact damage in composite aircraft structures-experimental testing and numerical simulation , 1998 .

[12]  V. Lopresto,et al.  Damage Mechanisms and Energy Absorption in Composite Laminates Under Low Velocity Impact Loads , 2013 .

[13]  Pietro Ferraro.  Evaluation by holographic interferometry of impact damage in composite aeronautical structures , 1992, Other Conferences.

[14]  Valentina Lopresto,et al.  A new damage index for the indentation depth evaluation of composites under low velocity impact loads , 2013 .

[15]  Gerhard Busse,et al.  Progress in phase angle thermography , 2003 .

[16]  Wade C. Jackson,et al.  The Use of Impact Force as a Scale Parameter for the Impact Response of Composite Laminates , 1993 .

[17]  C. Meola,et al.  On the use of lock-in thermography to monitor delamination growth in composite panels under compression , 2014 .

[18]  Relevance of Impacter Shape to Nonvisible Damage and Residual Tensile Strength of a Thick Graphite/Epoxy Laminate , 1991 .

[19]  Pietro Ferraro,et al.  On the holographic detection of core-to-skin disbonds in composite sandwich structures , 1994 .

[20]  D. Koss,et al.  Damage development in carbon/epoxy laminates under quasi-static and dynamic loading , 1999 .

[21]  Paul A. Lagace,et al.  A Preliminary Proposition for a Test Method to Measure (Impact) Damage Resistance , 1993 .

[22]  M. Giordano,et al.  A new cost-saving vacuum infusion process for fiber-reinforced composites: Pulsed infusion , 2014 .

[23]  Valentina Lopresto,et al.  Indentation and penetration of carbon fibre reinforced plastic laminates , 2003 .

[24]  P. Ferraro,et al.  Evaluation of delaminated area of polymer/Carbon Nanotubes fiber reinforced composites after flexural tests by ESPI , 2014, 2014 IEEE Metrology for Aerospace (MetroAeroSpace).

[25]  A damage index of indentation sensitivity in low velocity impact conditions , 2015 .