Constraint-Based Master Curve Analysis of a Nuclear Reactor Pressure Vessel Steel

This report presents the outcome of four fracture test series, addressing the ductile-to-brittle toughness behaviour of a nuclear reactor pressure vessel steel. Each test series corresponds to a specific test specimen geometry, tensile or three-point-bend, with a given degree of crack-tip constraint. A brief overview is given of available constraint-based fracture mechanics methodologies in the ductile-to-brittle transition range, including both engineering and local approach procedures. The obtained experimental data are analysed by means of the Master Curve standard ASTM E1921. Variability of the resulting reference temperature, T0, is successfully confirmed by a selection of constraint-based methodologies.

[1]  D. W. Beardsmore,et al.  Material constraint parameters for the assessment of shallow defects in structural components¿Part I: Parameter solutions , 2005 .

[2]  A. Pineau,et al.  A local criterion for cleavage fracture of a nuclear pressure vessel steel , 1983 .

[3]  Standard Test Methods for Tension Testing of Metallic Materials 1 , 2022 .

[4]  Kim Wallin,et al.  Quantifying Tstress controlled constraint by the master curve transition temperature T0 , 2001 .

[5]  Andrew H. Sherry,et al.  COMPENDIUM OF T‐STRESS SOLUTIONS FOR TWO AND THREE DIMENSIONAL CRACKED GEOMETRIES , 1995 .

[6]  D. W. Beardsmore,et al.  Material constraint parameters for the assessment of shallow defects in structural components. Part II: Constraint-based assessment of shallow defects , 2005 .

[7]  James A. Joyce,et al.  Development of the T0 reference temperature from precracked Charpy specimens , 2001 .

[8]  Nilsson Karl-Fredrik,et al.  NESC-IV Project: an Investigation of the Transferability of Master Curve Technology to Shallow Flaws in Reactor Pressure Vessel Applications - Final Report , 2005 .

[9]  Sevini Filippo.  Application of Surveillance Programme Results to Reactor Pressure Vessel Integrity Assessment" - Results of a Co-ordinated project , 2005 .

[10]  耳野 亨.  ASME boiler and pressure vessel codeの許容応力の改訂 , 1970 .

[11]  J. Heerens,et al.  Fracture toughness characterisation in the ductile-to-brittle transition and upper shelf regimes using pre-cracked Charpy single-edge bend specimens , 2005 .