Self-reinforced α-SiAlON ceramics with improved damage tolerance developed by a new processing strategy

Alpha-SiAlON ceramics with a refined self-reinforced microstructure, i.e., containing acicular grains with dimensions much smaller than those obtained in previous studies, embedded in a matrix consisting of submicrometer-sized isotropic grains, were prepared by applying a rapid one-step sintering procedure. To suppress the overabundant formation of α-SiAlON nuclei, a combination of stabilizing cations, Y + Yb, was used; to encourage formation of acicular α-SiAlON grains, a small amount of an extra liquid (∼3 vol%) was introduced; to avoid abnormal grain coarsening resulting from dynamic ripening, the final sintering temperature was set to just slightly above the minimum temperature threshold for activating grain growth (1700°C). The fully dense compacts obtained exhibited excellent thermal-shock resistance, and hardness and fracture toughness values of 20 GPa and 5.1 MPa·m1/2, respectively.

[1]  I. Chen,et al.  Microstructure Control of In‐Situ‐Toughened α‐SiAlON Ceramics , 2004 .

[2]  M. Johnsson,et al.  Thermal shock properties of β-sialon ceramics , 2002 .

[3]  Zhe Zhao,et al.  Formation of tough interlocking microstructures in silicon nitride ceramics by dynamic ripening , 2002, Nature.

[4]  M. Nygren,et al.  Formation of in situ Reinforced Microstructures in α-sialon Ceramics: Part II. In the Presence of a Liquid Phase , 2002 .

[5]  M. Nygren,et al.  Formation of in-situ reinforced microstructure in α–sialon ceramics I: Stoichiometric oxygen-rich compositions , 2002 .

[6]  M. Johnsson,et al.  Thermal shock resistance of a/-sialon ceramic composites , 2001 .

[7]  M. Nygren,et al.  Kinetic aspects of superfast consolidation of silicon nitride based ceramics by spark plasma sintering , 2001 .

[8]  I. Chen,et al.  A tough SiAlON ceramic based on α-Si3N4 with a whisker-like microstructure , 1997, Nature.

[9]  Zhijian Shen,et al.  Microstructural stability of duplex α-β-sialon ceramics , 1997 .

[10]  M. Nygren,et al.  α-SiAlON Grains with High Aspect Ratio—Utopia Or Reality? , 1997 .

[11]  M. Nygren,et al.  On the extension of the α-sialon phase area in yttrium and rare-earth doped systems , 1997 .

[12]  Yi-bing Cheng,et al.  Preferred orientation in hot-pressed Ca α-SiAlON ceramics , 1996 .

[13]  T. Andersson,et al.  Indentation Thermal Shock Test for Ceramics , 1996 .

[14]  M. Nygren,et al.  Ytterbium-stabilized -sialon ceramics , 1996 .

[15]  T. Nishimura,et al.  Fabrication of silicon nitride nano-ceramics by spark plasma sintering , 1995 .

[16]  Kiyoshi Hirao,et al.  Microstructure Control of Silicon Nitride by Seeding with Rodlike β‐Silicon Nitride Particles , 1994 .

[17]  P. L. Wang,et al.  Sintering and formation behaviour of R-α'-sialons (R=Nd, Sm, Gd, Dy, Er and Yb) , 1994 .

[18]  F. Lange,et al.  Powder Processing Science and Technology for Increased Reliability , 1989 .

[19]  E. Tani,et al.  Gas-pressure sintering of Si3N4 with concurrent addition of Al2O3 and 5 wt% rare, earth oxide: high fracture toughness Si3N4 with fiber-like structure , 1986 .

[20]  E. A. Charles,et al.  Fracture Toughness Determinations by Indentation , 1976 .