Fracture process of nonstoichiometric oxide based solid oxide fuel cell under oxidizing/reducing gradient conditions

Abstract The influence of chemically induced expansion on the fracture damage of a nonstoichiometric oxide (ceria) based solid oxide fuel cell (SOFC) single cell laminate was investigated by using numerical stress analyses under oxidizing/reducing gradient condition. The single cell examined in this study was composed of electrolyte (Ce0.8Sm0.2O2−δ), anode (Cermets of Ni–Ce0.8Sm0.2O2−δ), and cathode (La0.6Sr0.4Co0.2Fe0.8O3−δ), respectively. The finite element method (FEM) was employed to calculate the residual stress, thermal stresses, and chemically induced expansion stresses for the single cell. The residual and thermal stresses were calculated much smaller than the fracture strength of the individual components of the single cell. On the other hand, the chemically induced expansion stresses were shown to remarkably increase for the temperature range greater than 973 K and accounted their magnitude for primary part of the induced stress. It was shown from the FEM that the maximum circumferential stress induced in the single cell exceeded the fracture strength of the individual components at the onset of the fracture damage detect by acoustic emission (AE) method.

[1]  S. Singhal.  Solid oxide fuel cells for stationary, mobile, and military applications , 2002 .

[2]  Brian W. Sheldon,et al.  Stresses due to oxygen potential gradients in non-stoichiometric oxides , 2004 .

[3]  Hajime Omura,et al.  Tracking the Onset of Damage Mechanism in Ceria-based Solid Oxide Fuel Cells under Simulated Operating Conditions , 2006 .

[4]  Y. Xiong,et al.  Hole and Electron Conductivities of 20 mol % ­ REO 1.5 Doped CeO2 (RE = Yb, Y, Gd, Sm, Nd, La) , 2004 .

[5]  R. Drew,et al.  Wettability and spreading kinetics of molten aluminum on copper-coated ceramics , 2006 .

[6]  Mark C. Williams,et al.  U.S. distributed generation fuel cell program , 2004 .

[7]  A. Atkinson.  Chemically-induced stresses in gadolinium-doped ceria solid oxide fuel cell electrolytes , 1997 .

[8]  I. Yasuda,et al.  Static and Transient Model Analysis on Expansion Behavior of LaCrO3 under an Oxygen Potential Gradient , 2000 .

[9]  Keiji Yashiro,et al.  Effect of Y2O3 addition on the conductivity and elastic modulus of (CeO2)1 − x(YO1.5)x , 2009 .

[10]  H. Yahiro,et al.  Electrical properties and reducibilities of ceria−rare earth oxide systems and their application to solid oxide fuel cell , 1989 .

[11]  T. Hashida,et al.  Effect of rare-earth oxides on fracture properties of ceria ceramics , 2004 .

[12]  Y. Hirata,et al.  Thermal and mechanical properties of rare earth-doped ceria ceramics , 1999 .

[13]  H. Tagawa,et al.  Oxygen nonstoichiometry of Ce1−ySmyO2−0.5y−x (y=0.1, 0.2) , 1999 .

[14]  Masaru Matsumoto,et al.  The market for utility-scale fuel cell plants , 1996 .

[15]  Alan Atkinson,et al.  Chemically-induced stresses in ceramic oxygen ion-conducting membranes , 2000 .