Influence of chloride and moisture content on steel rebar corrosion in concrete

Reinforced mortar samples were exposed in humidity chambers with different relative humidity or exposed in cyclic moisture conditions. The rebars were in an “as received” condition meaning that the preexisting oxide scale were intact. The lowest chloride concentration that initiated corrosion was 1% Cl− by mass of cement, corrosion was then observed for samples exposed at 97% relative humidity. It is suggested that the corrosion rate decreases when samples are exposed to a relative humidity lower than 97%. The results indicate that threshold levels should be evaluated at rather humid conditions (97%) despite the fact that the maximum corrosion rate at higher chloride levels is observed in the interval 91–94%. For samples exposed to cyclic moisture conditions, a lower chloride concentration was needed to initiate corrosion compared to samples exposed in static moisture conditions.

[1]  J. R. Brown,et al.  XPS depth profiling study on the passive oxide film of carbon steel in saturated calcium hydroxide solution and the effect of chloride on the film properties , 2011 .

[2]  L. Wadsö,et al.  Galvanic corrosion properties of steel in water saturated concrete , 2015 .

[3]  G. A. McRae,et al.  Electrochemical investigation of chloride-induced depassivation of black steel rebar under simulated service conditions , 2010 .

[4]  C. K. Larsen,et al.  Relationship between concrete resistivity and corrosion rate – A literature review , 2013 .

[5]  Ueli Angst,et al.  Chloride induced reinforcement corrosion: Electrochemical monitoring of initiation stage and chloride threshold values , 2011 .

[6]  M. Geiker,et al.  Experimental investigation on the short-term impact of temperature and moisture on reinforcement corrosion , 2013 .

[7]  Stuart Lyon,et al.  Pore size distribution of OPC & SRPC mortars in presence of chlorides , 1995 .

[8]  Chun-Qing Li,et al.  Reinforcement corrosion initiation and activation times in concrete structures exposed to severe marine environments , 2009 .

[9]  W. López,et al.  Influence of the degree of pore saturation on the resistivity of concrete and the corrosion rate of steel reinforcement , 1993 .

[10]  J. C. Wren,et al.  Oxide formation and conversion on carbon steel in mildly basic solutions , 2009 .

[11]  Lars-Olof Nilsson,et al.  Chloride binding capacity and binding isotherms of OPC pastes and mortars , 1993 .

[12]  Ueli Angst,et al.  Critical Chloride Content in Reinforced Concrete: A Review , 2009 .

[13]  J. Marchand,et al.  A coupled AC impedance—creep and shrinkage investigation of hardened cement paste , 2003 .