Sulfur and temperature effects on the spatial distribution of reactions inside a lean NOx trap and resulting changes in global performance

Abstract We experimentally studied the influence of temperature and sulfur loading on the axial distribution of reactions inside a commercial lean NOx trap (LNT) catalyst to better understand the global performance trends. Our measurements were made on a monolith core, bench-flow reactor under cycling conditions (60-s lean/5-s rich) at 200, 325, and 400 °C with intra-catalyst and reactor-outlet gas speciation. Postmortem elemental and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) analyses of the catalyst also supplemented our gas species measurements. For the unsulfated catalyst, the NOx storage/reduction (NSR) reactions were localized in the front (upstream) portion of the monolith, whereas oxygen storage/reduction reactions were distributed more evenly along the entire catalyst length. As a result, two axially distinct reaction zones were developed inside the working catalyst: an upstream “NSR zone” where both NOx and oxygen storage/reduction took place and a downstream oxygen storage capacity (OSC)-only zone where the NSR reactions did not penetrate. The NSR zone involved less than half the LNT at 325 and 400 °C, but it included almost the entire length at 200 °C. Sulfation poisoned both the NSR and OSC reactions beginning at the catalyst upstream edge, with the NSR degradation occurring more rapidly and distinctly than the OSC. As sulfation proceeded, a third zone (the sulfated zone) developed and the NSR zone moved downstream, with a concomitant decrease in both the OSC-only zone and global NOx conversion. The sulfation impact on NOx conversion was greatest at 200 °C, when the NSR zone was largest. Ammonia selectivity increased with sulfation, which we attributed to a shortened OSC-only zone and resultantly reduced consumption of NH3, slipping from the NSR zone, by downstream OSC. Lower temperatures also increased NH3 selectivity. Nitrous oxide selectivity also increased with decreasing temperature but showed little dependence on sulfation. We proposed explanations for these trends in NH3 and N2O selectivity based on shifts in competing reaction rates in the three zones.

[1]  C. Querini,et al.  Stability of Ba,K/CeO2 catalyst during diesel soot combustion: Effect of temperature, water, and sulfur dioxide , 2006 .

[2]  Erik Fridell,et al.  NOx storage and reduction over Pt based catalysts with hydrogen as the reducing agent: Influence of H2O and CO2 , 2007 .

[3]  E. Fridell,et al.  In situ FTIR study of SO2 interaction with Pt/BaCO3/Al2O3 NOx storage catalysts under lean and rich conditions , 2006 .

[4]  Edward Jobson,et al.  Future Challenges in Automotive Emission Control , 2004 .

[5]  O. Saur,et al.  Study of ceria sulfation , 1997 .

[6]  D. Duprez,et al.  A study of the deactivation by sulfur and regeneration of a model NSR Pt/Ba/Al2O3 catalyst , 2005 .

[7]  Pio Forzatti,et al.  How to control the selectivity in the reduction of NOx with H2 over Pt-Ba/Al2O3 Lean NOx Trap catalysts , 2006 .

[8]  William S. Epling,et al.  The effect of exothermic reactions during regeneration on the NOX trapping efficiency of a NOX storage/reduction catalyst , 2006 .

[9]  D. Barton Smith,et al.  NOx adsorption on Pt/K/Al2O3 , 2006 .

[10]  Markus Kögel,et al.  On the mechanism of sulphur poisoning and regeneration of a commercial gasoline NOx-storage catalyst , 2005 .

[11]  Pio Forzatti,et al.  STUDY OF THE EFFECT OF BA LOADING FOR CATALYTIC ACTIVITY OF PT–BA/AL2O3 MODEL CATALYSTS , 2004 .

[12]  Todd J. Toops,et al.  Effect of Ceria on the Storage and Regeneration Behavior of a Model Lean NOx Trap Catalyst , 2007 .

[13]  Jae-Soon Choi,et al.  Sulfur impact on NOx storage, oxygen storage, and ammonia breakthrough during cyclic lean/rich operation of a commercial lean NOx trap , 2007 .

[14]  M. Twigg.  Progress and future challenges in controlling automotive exhaust gas emissions , 2007 .

[15]  P. Gilot,et al.  Experimental study of SO2 adsorption on barium-based NOx adsorbers , 2000 .

[16]  Russell G. Tonkyn,et al.  Nitrogen release from a NOx storage and reduction catalyst , 2006 .

[17]  W. Epling,et al.  The effects of regeneration conditions on NOX and NH3 release from NOX storage/reduction catalysts , 2007 .

[18]  Johannes A. Lercher,et al.  Studies on the deactivation of NOx storage-reduction catalysts by sulfur dioxide , 2002 .

[19]  Stephen Poulston,et al.  Regeneration of NOx trap catalysts , 2003 .

[20]  Friedemann Rohr,et al.  New insight into the interaction of sulfur with diesel NOx storage catalysts , 2007 .

[21]  C. Courson,et al.  Experimental study of the SO2 removal over a NOx trap catalyst , 2002 .

[22]  Jae-Soon Choi,et al.  Spatially resolved in situ measurements of transient species breakthrough during cyclic, low-temperature regeneration of a monolithic Pt/K/Al2O3 NOx storage-reduction catalyst , 2005 .

[23]  Neal W. Currier,et al.  Ammonia is a hydrogen carrier in the regeneration of Pt/BaO/Al2O3 NOx traps with H2 , 2007 .

[24]  Masahiko Takeuchi,et al.  NOx Storage-Reduction Catalysts for Gasoline Engines , 2004 .

[25]  Koji Yokota,et al.  The new concept 3-way catalyst for automotive lean-burn engine: NOx storage and reduction catalyst , 1996 .

[26]  W. Epling,et al.  Overview of the Fundamental Reactions and Degradation Mechanisms of NOx Storage/Reduction Catalysts , 2004 .

[27]  Jae-Soon Choi,et al.  Intra-channel evolution of carbon monoxide and its implication on the regeneration of a monolithic Pt/K/Al2O3 NOx storage-reduction catalyst , 2006 .