Correlation between surface composition and luminescence of nanocrystalline silicon particles dispersed in pure water

The stability of the luminescene of nanocrystalline silicon (nc-Si) particles passivated with a number of different elements, including hydrogen, carbon, and oxygen, has been investigated in pure water. Each sample emitted red light with a peak wavelength in the range of 740–800nm. The intensity of red luminescence decreased after a short period of time when the hydrogen- and/or carbon-passivated samples were immersed in pure water. Further, the peak wavelength concomitantly shifted toward a shorter wavelength. These effects were attributed to the generation of defects (Pb centers), the reduction in particle size due to the desorption of hydrogen and/or carbon atoms, and the replacement of the Si–H and/or Si–C bonds, respectively, with Si-O bonds on the surface of nc-Si particles. On the other hand, the oxygen-passivated samples showed stable luminescence in addition to a slight blueshift of the peak wavelength upon immersion in pure water for 400h. This stability was attributed to the development of stab...

[1]  L. Canham.  Silicon quantum wire array fabrication by electrochemical and chemical dissolution of wafers , 1990 .

[2]  N. Koshida,et al.  Characterization of an advanced high-efficiency electron emission device , 2005 .

[3]  P. Fauchet,et al.  Macroporous Silicon Electrical Sensor for DNA Hybridization Detection , 2004, Biomedical microdevices.

[4]  G. Bruno,et al.  Structural and optical investigation of plasma deposited silicon carbon alloys: Insights on Si-C bond configuration using spectroscopic ellipsometry , 2005 .

[5]  Keisuke Sato,et al.  Improved luminescence intensity and stability of nanocrystalline silicon due to the passivation of nonluminescent states , 2005 .

[6]  H. Ohno,et al.  A self‐consistent computer simulation of compound semiconductor metal‐insulator‐semiconductor C‐V curves based on the disorder‐induced gap‐state model , 1988 .

[7]  Keisuke Sato,et al.  Nucleation and growth of nanocrystalline silicon studied by TEM, XPS and ESR , 2003 .

[8]  Kenji Hirakuri,et al.  Influence of paramagnetic defects on multicolored luminescence from nanocrystalline silicon , 2006 .

[9]  Yu-Lun Chueh,et al.  Oxygen defect and Si nanocrystal dependent white-light and near-infrared electroluminescence of Si-implanted and plasma-enhanced chemical-vapor deposition-grown si-rich SiO2 , 2005 .

[10]  Kenji Hirakuri,et al.  Stability of nanocrystalline silicon particles in solution , 2006 .

[11]  Three primary color luminescence from natively and thermally oxidized nanocrystalline silicon , 2006 .

[12]  A. V. Rao,et al.  Surface chemical modification of TEOS based silica aerogels synthesized by two step (acid–base) sol–gel process , 2006 .

[13]  S. Guha,et al.  Effect of electrical bias on metastability in hydrogenated nanocrystalline silicon solar cells , 2005 .

[14]  Allan,et al.  Theoretical aspects of the luminescence of porous silicon. , 1993, Physical review. B, Condensed matter.

[15]  Olivier Jambois,et al.  Photoluminescence and electroluminescence of size-controlled silicon nanocrystallites embedded in SiO2 thin films , 2005 .

[16]  Howard W. H. Lee,et al.  Photoluminescence as a Function of Aggregated Size from n-Butyl-Terminated Silicon Nanoclusters , 2000 .

[17]  W. Theiß,et al.  Optical properties of porous silicon , 1997 .