MORPHOLOGY AND MECHANICAL PROPERTIES OF POLYPROPYLENE-WOOD FLOUR COMPOSITES

The microstructure and mechanical properties of polymer composites based on polypropylene and wood flour modified with monochloroacetic acid were investigated. Scanning electron microscopy and wide-angle X-ray diffraction were used as methods to probe the composite microstructures, while the tensile test was used to measure the physical strength. The wood flour modification was performed at different levels of monochloroacetic acid, ranging from 0.01 to 1 mol, while the modified wood flour was used as filler for polypropylene at 10, 20 and 30 wt.-%. It was found that increasing the monochloroacetic acid fraction influences the microstructure of the composites and leads to more homogeneous products. The introduction of non-modified wood flour decreases the polypropylene crystallization degree, but it improves after introduction of monochloroacetic acid. Physical-mechanical tests showed positive effects on tensile tests and Charpy notched impact strength. The new composites appear to be promising materials for construction purposes.

[1]  W. Ruland,et al.  X-ray determination of crystallinity and diffuse disorder scattering , 1961 .

[2]  S. Nenkova,et al.  Investigation of the Microstructure of Polypropylene Composites Filled with Wood Flour Modified with Monochloracetic Acid , 2006 .

[3]  R. Young,et al.  Lignin‐polypropylene composites. Part 1: Composites from unmodified lignin and polypropylene , 2002 .

[4]  I. Fukumoto,et al.  Effect of bagasse fiber on the flexural properties of biodegradable composites , 2005 .

[5]  F. M. B. Coutinho,et al.  Polypropylene–wood fiber composites: Effect of treatment and mixing conditions on mechanical properties , 1997 .

[6]  J. Balatinecz,et al.  Mechanical properties of wood‐fiber/toughened isotactic polypropylene composites , 1997 .

[7]  M. Reboredo,et al.  Mechanical properties of woodflour unsaturated polyester composites , 1998 .

[8]  Mehdi Tajvidi,et al.  Water uptake and mechanical characteristics of natural filler–polypropylene composites , 2003 .

[9]  N. Shiraishi,et al.  Wood–phenol adhesives prepared from carboxymethylated wood. I , 1986 .

[10]  T. Hirotsu,et al.  Effect of maleated polypropylene on the performance of polypropylene/cellulose composite , 2005 .

[11]  G. Michler,et al.  Modified polypropylene wood flour composites. II. Fracture, deformation, and mechanical properties , 2004 .

[12]  M. Reboredo,et al.  Dependence of the mechanical properties of woodflour- polymer composites on the moisture content , 1998 .

[13]  J. Balatinecz,et al.  A comparison of compounding processes for wood‐fiber/thermoplastic composites , 1997 .

[14]  J. Kenny,et al.  Mechanical characterization of polypropylene–wood flour composites , 2003 .

[15]  Alessandro Gandini,et al.  Chemical Modification of Wood , 2008 .

[16]  R. Young,et al.  Lignin–polypropylene composites. II. Plasma modification of kraft lignin and particulate polypropylene , 2004 .

[17]  R. Wool,et al.  Kraft lignin as fiber treatment for natural fiber‐reinforced composites , 2005 .