Femtosecond laser micro-structuring of alumina ceramic

Al2O3 ceramic has been micro-structured in air using 180 fs, l = 775 nm optical pulses in a fluence range 1.4 < F < 21 J cm � 2 with observed ablation rates of 25 < V < 900 mm 3 /pulse. The threshold fluence was F th = 1.1 J cm � 2 at this ultrashort pulse-length in the NIR. Melting could be minimised using ultrafast optical pulses, improving the edge quality. By optimising the processing parameters, the residual surface roughness could be reduced below the pristine surface Ra = 0.8 mm. The debris produced consists mainly of single crystal nanoparticles of alumina with diameters from 20 nm to 1 mm with an average diameter of 300 nm. # 2005 Elsevier B.V. All rights reserved.

[1] Diletta Sciti,et al. Excimer laser-induced microstructural changes of alumina and silicon carbide , 2000 .

[2] B. Wolff-Rottke,et al. Nanosecond and femtosecond excimer-laser ablation of oxide ceramics , 1995 .

[3] Razvan Stoian,et al. Single and multiple ultrashort laser pulse ablation threshold of Al2O3 (corundum) at different etch phases , 2000 .

[4] J. Ihlemann,et al. Femtosecond ultraviolet laser micromachining of Al2O3–TiC ceramics , 1999 .

[5] B. Luk’yanchuk,et al. Strategy of nanocluster and nanostructure synthesis by conventional pulsed laser ablation , 2000 .

[6] Rui Vilar,et al. Excimer laser ablation of Al2O3–TiC ceramics: laser induced modifications of surface topography and structure , 1998 .

[7] J. Ihlemann,et al. XeCl laser ablation of Al2O3–TiC ceramics , 2000 .

[8] P. Fox,et al. Femtosecond laser micro-structuring of aluminium under helium , 2004 .

[9] David Ashkenasi,et al. Femtosecond laser ablation of sapphire : time-of-flight analysis of ablation plume , 1998 .

[10] R. Vilar,et al. Influence of the processing parameters on the formation and deposition of particles in UV pulsed laser ablation of Al2O3–TiC ceramics , 2003 .

[11] B. Wolff-Rottke,et al. Excimer laser micro machining of inorganic dielectrics , 1996 .

[12] David Ashkenasi,et al. Laser processing of sapphire with picosecond and sub-picosecond pulses , 1997 .