Structure and Properties of Electrodeposited FePt Films

Fe-Pt binary alloy thin films were fabricated through a pluse electrodeposition in a novel bath with a simple composition on copper substrates. Composition, morphology and structure of electrodeposited Fe-Pt films were investigated in dependence on deposition potential. In a broad potential range from 2.0 to 6.0V, oxygen was detected in the films. Continuous Fe-Pt alloy films with controllable compositions in 16-58 atom% Fe were achieved on copper substrates. In particular, the films with a composition close to 1:1 Fe/Pt was obtained at -4.7V. All Fe-Pt films as-synthesized exhibited essential characteristics of soft magnetic and isotropic behavior, as investigated by a vibrating sample magnetometer (VSM).

Zhi Hong Li | X. Du | S. Shi | C. Li

[1] L. Schultz,et al. FePt Hard Magnets , 2005 .

[2] Yen-Hwei Chang,et al. The magnetic properties of Fe–Co–Pt alloys films , 2004 .

[3] L. Schultz,et al. Highly coercive electrodeposited FePt films by postannealing in hydrogen , 2004 .

[4] Koki Takanashi,et al. Coercivity exceeding 100 kOe in epitaxially grown FePt sputtered films , 2004 .

[5] L. Schultz,et al. Textured growth of highly coercive L10 ordered FePt thin films on single crystalline and amorphous substrates , 2004 .

[6] G. Hadjipanayis,et al. CoPt and FePt nanowires by electrodeposition , 2002 .

[7] Laura H. Lewis,et al. On the relationship of high coercivity and L10 ordered phase in CoPt and FePt thin films , 1999 .

[8] G. Tourillon,et al. Electrochemically Synthesized Co and Fe Nanowires and Nanotubes , 1999 .

[9] Shailesh Gadad,et al. Oxygen Incorporation during the Electrodeposition of Ni, Fe, and Ni‐Fe Alloys , 1998 .