Higher power density limit at COMD in GaInP/AlGaInP in quantum dots than in wells

Quantum dots (QD) offer significant advantages over quantum wells (QW) as the active material in high power lasers. We have determined power density values at catastrophic optical mirror damage (COMD), a key factor limiting high power laser diode performance, for various QW and QD red and NIR emitting structures in the in the AlGaInP system. The devices used were 50 μm oxide stripe lasers mounted p-side up on copper heatsinks operated pulsed. The COMD power density limit decreases as pulse length increases. At short pulse lengths the limit is higher in QD (19.1±1.1 MW/cm2) than in QW devices (11.9±2.8 MW/cm2 and 14.3±0.4 MW/cm2 for two different spot sizes). We used the high energy Boltzmann tail of the spontaneous emission from the front facet to measure temperature rise to investigate the physical mechanisms (non-radiative recombination of injected carriers and reabsorption of laser light at the facet) leading to COMD and distinguish between the behaviour at COMD of QW and QD devices. Over the range 1x to 2x threshold current the temperature rise in the QW structures was higher. Scanning electron microscopy showed a difference between the QD and QW lasers in the appearance of the damage after COMD.

[1]  J. C. Jaeger,et al.  Conduction of Heat in Solids , 1952 .

[2]  P. Blood,et al.  Measurement and calculation of spontaneous recombination current and optical gain in GaAs-AlGaAs quantum-well structures , 1991 .

[3]  Charles Howard Henry,et al.  Measurement of gain and absorption spectra in AlGaAs buried heterostructure lasers , 1980 .

[4]  Peter Michael Smowton,et al.  Filamentation and linewidth enhancement factor In InGaAs quantum dot lasers , 2001, CLEO 2001.

[5]  C. Henry,et al.  Catastrophic damage of AlxGa1−xAs double‐heterostructure laser material , 1979 .

[6]  T. Elsaesser,et al.  Real-time thermal imaging of catastrophic optical damage in red-emitting high-power diode lasers , 2008 .

[7]  Yoshiyasu Ueno,et al.  Effect of thermal resistivity on the catastrophic optical damage power density of AlGaInP laser diodes , 1993 .

[8]  Jens W. Tomm,et al.  Nanoscopic measurements of surface recombination velocity and diffusion length in a semiconductor quantum well , 2002 .

[9]  C. L. Tien,et al.  Facet heating of quantum well lasers , 1993 .

[10]  A. McKee,et al.  Facet-passivation processes for the improvement of Al-containing semiconductor laser diodes , 2006, Journal of Lightwave Technology.

[11]  Peter Michael Smowton,et al.  Optimisation of high power AlGaInP laser diodes for optical storage applications , 2006 .

[12]  B. Sumpf,et al.  Surface recombination and facet heating in high-power diode lasers , 2008 .

[13]  D. Webb,et al.  Raman microprobe study of the time development of AlGaAs single quantum well laser facet temperature on route to catastrophic breakdown , 1991 .

[14]  S. Sweeney,et al.  Direct measurement of facet temperature up to melting point and COD in high-power 980-nm semiconductor diode lasers , 2003 .

[15]  A. Rosen,et al.  High-power semiconductor red laser arrays for use in photodynamic therapy , 2005, IEEE Journal of Selected Topics in Quantum Electronics.

[16]  Wolfgang Schmid,et al.  Investigation of dark line defects induced by catastrophic optical damage in broad-area AlGaInP laser diodes , 2006 .

[17]  L. O'Faolain,et al.  Reduced surface sidewall recombination and diffusion in quantum-dot lasers , 2006, IEEE Photonics Technology Letters.

[18]  Mikhail V. Maximov,et al.  Complete suppression of filamentation and superior beam quality in quantum-dot lasers , 2003 .