Hydrogen enhanced crack growth in 18 Ni maraging steels

The kinetics of sustained-load subcritical crack growth for 18 Ni maraging steels in high purity hydrogen are examined using crack-tip stress intensity,K, as a measure of crack driving force. Crack growth rate as a function of stress intensity exhibited a clearly definedK-independent stage (Stage II). Crack growth rates in an 18 Ni (250) maraging steel are examined for temperatures from -60°C to 100°C. A critical temperature was observed above which crack growth rates became diminishingly small. At lower temperatures the activation energy for Stage II crack growth was found to be 16.7 ± 3.3 kJ/mole. Temperature and hydrogen partial pressure are shown to interact in a complex manner to determine the apparentKth and the crack growth behavior. Comparison of results on ‘250’ and ‘300’ grades of 18 Ni maraging steel indicate a significant influence of alloy composition and/or strength level on the crack growth behavior. These phenomenological observations are discussed in terms of possible underlying controlling processes.

[1]  R. Wei,et al.  The kinetics of subcritical crack growth under sustained loading , 1973 .

[2]  H. Read.  Hydrogen embrittlement in metal finishing , 1961 .

[3]  H. Eschbach,et al.  Permeability measurements with gaseous hydrogen for various steels , 1963 .

[4]  A. Tetelman,et al.  Embrittlement of a ferrous alloy in a partially dissociated hydrogen environment , 1971 .

[5]  D. D. Perlmutter,et al.  Effects of Hydrogen on Properties of Metals , 1956 .

[6]  J. A. Donovan,et al.  Hydrogen embrittlement of metals , 1972 .

[7]  N. Petch.  XXX. The lowering of fracture-stress due to surface adsorption , 1956 .

[8]  R. P. Wei,et al.  Kinetics of Subcritical Crack Growth and Deformation in a High Strength Steel , 1973 .

[9]  D. Vaughan,et al.  The Role of Surface Stress on Hydrogen Absorption by 4340 Steel , 1968 .

[10]  Paul C. Paris,et al.  SUB-CRITICAL FLAW GROWTH. , 1968 .

[11]  C. D. Beachem,et al.  A new model for hydrogen-assisted cracking (hydrogen “embrittlement”) , 1972 .

[12]  R. A. Oriani,et al.  The Thermodynamics of Stressed Solids , 1966 .

[13]  W. Beck,et al.  Hydrogen permeation in metals as a function of stress, temperature and dissolved hydrogen concentration , 1966, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[14]  N. Petch,et al.  Delayed Fracture of Metals under Static Load , 1952, Nature.

[15]  H. Smith,et al.  A note on stress corrosion cracking rates , 1971 .

[16]  Jeffrey J. Thomas,et al.  Protective Coatings for Metals , 1955 .

[17]  Harold R. Smith,et al.  A STUDY OF STRESS-CORROSION CRACKING BY WEDGE-FORCE LOADING , 1968 .

[18]  H. H. Johnson.  Hydrogen brittleness in hydrogen and hydrogen-oxygen gas mixtures , 1973 .

[19]  R. Staehle,et al.  Slow crack growth in hydrogen and hydrogen sulfide gas environments , 1972 .

[20]  W. A. Van Der Sluys,et al.  Mechanisms of environment induced subcritical flaw growth in AISI 4340 steel , 1969 .

[21]  R. A. Oriani,et al.  Testing of the decohesion theory of hydrogen-induced crack propagation , 1972 .

[22]  R. P. Wei,et al.  On the dilatation field in front of a moving crack , 1972 .

[23]  M. Isida.  Effect of width and length on stress intensity factors of internally cracked plates under various boundary conditions , 1971 .

[24]  S. Wiederhorn.  Moisture assisted crack growth in ceramics , 1968 .

[25]  J. F. Lancaster,et al.  The metallurgy of welding, brazing and soldering, , 1970 .

[26]  L. S. Darken,et al.  Behavior of Hydrogen in Steel During and After Immersion in Acid , 1949 .