Fatigue Design of Hydraulic Turbine Runners

Turbine runners experience start-stop cycles and vibration cycles. Cracks initiated from service or manufacturing defects and propagated by start-stop cycles become critical when the stress intensi ...

[1]  William John Macquorn Rankine.  On the causes of the unexpected breakage of the journals of railway axles; and on the mean of preventing such accidents by observing the law of continuity in their construction , 1843 .

[2]  F Braithwaite.  ON THE FATIGUE AND CONSEQUENT FRACTURE OF METALS. , 1854 .

[3]  HighWire Press.  Philosophical Transactions of the Royal Society of London , 1781, The London Medical Journal.

[4]  E. Preuß.  Versuche über die Spannungsverteilung in gekerbten Zugstäben , 1913 .

[5]  C. Inglis.  Stresses in a plate due to the presence of cracks and sharp corners , 1913 .

[6]  H. Gough,et al.  Fatigue in Metals , 1923, The Journal of the Royal Aeronautical Society.

[7]  A. Thum,et al.  Dauerfestigkeit und konstruktion , 1932 .

[8]  R. B. Heywood.  The Relationship Between Fatigue and Stress Concentration , 1947 .

[9]  R. Peterson.  Stress Concentration Design Factors , 1953 .

[10]  S. Manson.  Behavior of materials under conditions of thermal stress , 1953 .

[11]  N. Muskhelishvili.  Some basic problems of the mathematical theory of elasticity , 1953 .

[12]  L. Coffin,et al.  A Study of the Effects of Cyclic Thermal Stresses on a Ductile Metal , 1954, Journal of Fluids Engineering.

[13]  D. S. Dugdale,et al.  Fatigue tests on notched mild steel plates with measurements of fatigue cracks , 1957 .

[14]  P. Paris.  A rational analytic theory of fatigue , 1961 .

[15]  H. Neuber.  Theory of Stress Concentration for Shear-Strained Prismatical Bodies With Arbitrary Nonlinear Stress-Strain Law , 1961 .

[16]  R. Heywood.  Designing Against Fatigue , 1962 .

[17]  B. Massey,et al.  Mechanics of Fluids , 2018 .

[18]  P. C. Paris,et al.  A Critical Analysis of Crack Propagation Laws , 1963 .

[19]  William F. Brown,et al.  Stress-Intensity Factors for a Single-Edge-Notch Tension Specimen by Boundary Collocation of a Stress Function , 1964 .

[20]  James Ferguson,et al.  Multivariable Curve Interpolation , 1964, JACM.

[21]  John R. Rice,et al.  Mechanics of Crack Tip Deformation and Extension by Fatigue , 1967 .

[22]  J. Rice.  A path-independent integral and the approximate analysis of strain , 1968 .

[23]  H. Neuber,et al.  Der zugbeanspruchte Flachstab mit optimalem Querschnittsübergang , 1969 .

[24]  T. A. Cruse,et al.  Numerical solutions in three dimensional elastostatics , 1969 .

[25]  H. Bueckner.  NOVEL PRINCIPLE FOR THE COMPUTATION OF STRESS INTENSITY FACTORS , 1970 .

[26]  K. N. Smith.  A Stress-Strain Function for the Fatigue of Metals , 1970 .

[27]  E. Wolf.  Fatigue crack closure under cyclic tension , 1970 .

[28]  George C. Sih.  Proceedings of an international conference on Dynamic Crack Propagation , 1973 .

[29]  G. Sih,et al.  Alternating method applied to edge and surface crack problems , 1973 .

[30]  W. K. Wilson.  Finite element methods for elastic bodies containing cracks , 1973 .

[31]  W. T. Koiter,et al.  Asymptotic approximations to crack problems , 1973 .

[32]  O. C. Zienkiewicz,et al.  Optimization of shape to minimize stress concentration , 1975 .

[33]  J. R. Griffiths,et al.  Fatigue problems in power engineering , 1977 .

[34]  James C. Newman,et al.  Stress-intensity factors for a wide range of semi-elliptical surface cracks in finite-thickness plates , 1979 .

[35]  Eckart Schnack,et al.  An optimization procedure for stress concentrations by the finite element technique , 1979 .

[36]  Z. Bažant,et al.  Surface singularity and crack propagation , 1979 .

[37]  James C. Newman,et al.  An empirical stress-intensity factor equation for the surface crack , 1981 .

[38]  James C. Newman,et al.  Stress-Intensity Factors for Internal and External Surface Cracks in Cylindrical Vessels , 1982 .

[39]  J. Newman,et al.  Stress-intensity factor equations for cracks in three-dimensional finite bodies subjected to tension and bending loads , 1984 .

[40]  V. Braibant,et al.  Shape optimal design using B-splines , 1984 .

[41]  T. Lorentzen,et al.  The application of fracture mechanics to surface cracks in shafts , 1986 .

[42]  Kathleen R Dennis.  Fatigue Crack Growth of the Gun Tube Steel under Spectrum Loading. , 1986 .

[43]  G. C. Sih,et al.  Review of triaxial crack border stress and energy behavior , 1989 .

[44]  E. Schnack,et al.  Shape design of elastostatic structures based on local perturbation analysis , 1989 .

[45]  G. C. Sih,et al.  Initiation and growth characterization of corner cracks near circular hole , 1990 .

[46]  S. Suresh.  Fatigue of materials , 1991 .

[47]  L. P. Pook.  A note on corner point singularities , 1992, International Journal of Fracture.

[48]  Fred Nilsson.  A consistent few parameter crack growth description procedure , 1992 .

[49]  W. Schütz,et al.  Zur Geschichte der Schwingfestigkeit , 1993 .

[50]  Andrea Carpinteri,et al.  Shape change of surface cracks in round bars under cyclic axial loading , 1993 .

[51]  L. P. Pook,et al.  Some implications of corner point singularities , 1994 .

[52]  T. Belytschko,et al.  Element‐free Galerkin methods , 1994 .

[53]  M. Bergman,et al.  STRESS INTENSITY FACTORS FOR CIRCUMFERENTIAL SURFACE CRACKS IN PIPES , 1995 .

[54]  Paul F. Joseph,et al.  Surface cracks in toroidal shells , 1995 .

[55]  X. B. Lin,et al.  Numerical analysis of fatigue growth of external surface cracks in pressurised cylinders , 1997 .

[56]  Theo Fett,et al.  Stress intensity factors and weight functions , 1997 .

[57]  X. B. Lin,et al.  Shape growth simulation of surface cracks in tension fatigued round bars , 1997 .

[58]  Walter D. Pilkey.  Peterson's Stress Concentration Factors , 1997 .

[59]  D. A. Hills,et al.  Simulation of the growth of near-surface defects , 1998 .

[60]  N. Couroneau,et al.  Simplified model for the fatigue growth analysis of surface cracks in round bars under mode I , 1998 .

[61]  Fred Nilsson,et al.  Fatigue crack growth of surface cracks under non-symmetric loading , 1999 .

[62]  Paul C. Paris,et al.  Service load fatigue damage — a historical perspective , 1999 .

[63]  Andrea Carpinteri,et al.  External surface cracks in shells under cyclic internal pressure , 2000 .

[64]  Paul A. Wawrzynek,et al.  Automated 3‐D crack growth simulation , 2000 .

[65]  Hiroshi Tada,et al.  The stress analysis of cracks handbook , 2000 .

[66]  Roberto Brighenti.  Axially-cracked pipes under pulsating internal pressure , 2000 .

[67]  Jaap Schijve,et al.  Fatigue of structures and materials , 2001 .

[68]  G. Härkegård,et al.  Approximate Viscoplastic Notch Analysis , 2001 .

[69]  Eckart Schnack,et al.  Shape optimization under fatigue using continuum damage mechanics , 2002, Comput. Aided Des..

[70]  Gunnar Härkegård,et al.  Neuber prediction of elastic-plastic strain concentration in notched tensile specimens under large-scale yielding , 2003 .

[71]  François Avellan,et al.  Simulation of Transient Phenomena in Francis Turbine Power Plants : Hydroelectric Interaction , 2003 .

[72]  Jaap Schijve,et al.  Fatigue of Structures and Materials in the 20th Century and the State of the Art. , 2003 .

[73]  Bastiaan N. Veelo,et al.  Variations of Shape in Industrial Geometric Models , 2004 .

[74]  Andrea Carpinteri,et al.  Fatigue growth of a surface crack in a welded T-joint , 2005 .