Production a characterization of new system superconductor TR3Ba8Cu11Oδ

The production and structural & magnetic characterization of new superconductor system TR:3811 (TR=Sm, Y, Yb) is presented in this work. The samples were produced by the solid state reaction method. The analysis of the measures of the diffraction X-ray, were made with the Rietveld refinement technique, that allowed to infer that the system presents a Pmm2 type structure with the following lattice parameters (a=3.88Å, b=3.82Å, c=42.82Å). The magnetization measurements were made by using the VSM-VERSALAB equipment with a magnetic field variation from a 100Oe to 7000Oe, and a temperature from 50K to 350K, showing the superconducting transition of the order of 90K.

[1]  T. Kruaehong.  Electrical properties and crystal structure of Y123, Y358 and Y257/Y211 composite bulk superconductors , 2014 .

[2]  J. Peña,et al.  High Temperature Superconductivity on the New Superconductor System Yb1.8Sm1.2Ba5Cu8O18 , 2013 .

[3]  P. Udomsamuthirun,et al.  XRD spectra of new YBaCuO superconductors , 2011 .

[4]  P. Udomsamuthirun,et al.  The New Superconductors of YBaCuO Materials , 2010 .

[5]  M. Akhavan,et al.  How Tc can go above 100 K in the YBCO family , 2010 .

[6]  D. A. Téllez,et al.  Magnetization fluctuation analysis and superconducting parameters of La0.5RE0.5BaCaCu3O7-δ(RE=Y, Sm, Gd, Dy, Ho, Yb) superconductor , 2009 .

[7]  D. A. Téllez,et al.  Determining superconducting parameters from analysis of magnetization fluctuation for CaLaBaCu3O7−δ superconductor , 2007 .

[8]  M. Cantão,et al.  Magnetoresistivity, fluctuation conductivity and magnetic irreversibility in the Y0.95Pr0.05Ba2Cu3O7−δ compound: a case of split pairing transition , 2004 .

[9]  M. Cyrot,et al.  Introduction To Superconductivity And High-Tc Materials , 1992 .

[10]  T. Graf,et al.  Variation of the superconducting and structural properties of Y2Ba4Cu7Oz with oxygen content (14.1 < z < 15.3, 30 K ⩽ Tc ⩾ 95 K) , 1992 .

[11]  Clem,et al.  Limitations of the London model for the reversible magnetization of type-II superconductors. , 1991, Physical review letters.

[12]  J. Karpinski,et al.  The nonstoichiometry of the high-Tc superconductor Y2Ba4Cu7O15±x (14 K⩽Tc⩽68 K) , 1989 .

[13]  M. L. Mandich,et al.  Crystal structure of the 80 K superconductor YBa2Cu4O8 , 1988, Nature.

[14]  Chu,et al.  Superconductivity at 93 K in a new mixed-phase Yb-Ba-Cu-O compound system at ambient pressure. , 1987, Physical review letters.

[15]  Michael Tinkham,et al.  Introduction to Superconductivity , 1975 .

[16]  A. Schmid.  DIAMAGNETIC SUSCEPTIBILITY AT THE TRANSITION TO THE SUPERCONDUCTING STATE. , 1969 .