Hydrogen permeance of palladium–copper alloy membranes over a wide range of temperatures and pressures

The permeance of Pd–Cu alloys containing 40, 53, 60, and 80 wt.% Pd has been determined over the 623–1173 K temperature range for H2 partial pressure differences as great as 2.6 MPa. Pure palladium and copper membranes were also evaluated. The Pd–Cu alloys exhibited predictable permeances that reflected the crystalline phase structures as shown in the binary phase diagram. Under conditions of face-centered-cubic (fcc) stability, the permeance increased steadily with palladium content, approaching the permeance of pure palladium membranes. The 53 and 60 wt.% Pd alloys were evaluated at temperatures within the body-centered-cubic (bcc) stability region. For both alloys, the bcc permeance was several times greater than the fcc permeance with the 60 wt.% Pd bcc permeance at 623 K reaching about 70% of the permeance of palladium. These bcc alloys were subjected to temperature increases during testing that resulted in transition from bcc to fcc, followed by temperature decreases that should revert the alloys to bcc. The permeances dropped abruptly during the transition from bcc to fcc. However, on cooling back to the bcc stability region, neither the 60 nor 53 wt.% Pd alloy completely regained a bcc permeance during the test period. All of the Pd–Cu alloys subjected to testing at 1173 K showed some permeance decline that was attributed to intermetallic diffusion between the membrane and support. The application of a diffusion barrier between the support and membrane foil in a 53 wt.% Pd permeance test successfully blocked the intermetallic diffusion and prevented degredation of the membrane’s performance.

[1]  Shigeyuki Uemiya,et al.  Separation of hydrogen through palladium thin film supported on a porous glass tube , 1991 .

[2]  Dwayne Thomas Friesen,et al.  Hydrogen-permeable metal membranes for high-temperature gas separations , 1994 .

[3]  B. Morreale,et al.  The permeability of hydrogen in bulk palladium at elevated temperatures and pressures , 2003 .

[4]  D. Edlund,et al.  The relationship between intermetallic diffusion and flux decline in composite-metal membranes: implications for achieving long membrane lifetime , 1995 .

[5]  W. Klose,et al.  Deactivation of a Palladium-Supported Alumina Catalyst by Hydrogen Sulfide during the Oxidation of Methane , 1994 .

[6]  J. Piper Diffusion of Hydrogen in Copper‐Palladium Alloys , 1966 .

[7]  R. Buxbaum,et al.  Evaluation of tantalum-based materials for hydrogen separation at elevated temperatures and pressures ☆ , 2003 .

[8]  T. Kojima,et al.  Stability and hydrogen permeation behavior of supported platinum membranes in presence of hydrogen sulfide , 1999 .

[9]  D. Edlund A Membrane Reactor for H2S Decomposition , 1996 .

[10]  H. Toulhoat,et al.  Ethylene, sulphur, and chlorine coadsorption on Pd(111) : a theoretical study of poisoning and promotion , 1999 .

[11]  Robert L. McCormick,et al.  Preparation and characterization of Pd-Cu composite membranes for hydrogen separation , 2003 .

[12]  J. Way,et al.  The influence of alloy composition on the H2 flux of composite PdCu membranes , 2002 .

[13]  M. Hansen,et al.  Constitution of Binary Alloys , 1958 .

[14]  S. Nam,et al.  Hydrogen separation by Pd alloy composite membranes: introduction of diffusion barrier , 2001 .

[15]  C. Corti,et al.  The Purification of Hydrogen A REVIEW OF THE TECHNOLOGY EMPHASISING THE CURRENT STATUS OF PALLADIUM MEMBRANE DIFFUSION , 1983 .

[16]  D. Laughlin,et al.  Cu-Pd (Copper-Palladium) , 1991 .

[17]  Y. Ma,et al.  Thin Composite Palladium and Palladium/Alloy Membranes for Hydrogen Separation , 2003, Annals of the New York Academy of Sciences.