Triblock Copolymers Based on ε-Caprolactone and Trimethylene Carbonate for the 3D Printing of Tissue Engineering Scaffolds

Background Biodegradable PCL-b-PTMC-b-PCL triblock copolymers based on trimethylene carbonate (TMC) and ε-caprolactone (CL) were prepared and used in the 3D printing of tissue engineering scaffolds. Triblock copolymers of various molecular weights containing equal amounts of TMC and CL were prepared. These block copolymers combine the low glass transition temperature of amorphous PTMC (approximately -20°C) and the semi-crystallinity of PCL (glass transition approximately -60°C and melting temperature approximately 60°C). Methods PCL-b-PTMC-b-PCL triblock copolymers were synthesized by sequential ring opening polymerization (ROP) of TMC and ε-CL. From these materials, films were prepared by solvent casting and porous structures were prepared by extrusion-based 3D printing. Results Films prepared from a polymer with a relatively high molecular weight of 62 kg/mol had a melting temperature of 58°C and showed tough and resilient behavior, with values of the elastic modulus, tensile strength and elongation at break of approximately 120 MPa, 16 MPa and 620%, respectively. Porous structures were prepared by 3D printing. Ethylene carbonate was used as a crystalizable and water-extractable solvent to prepare structures with microporous strands. Solutions, containing 25 wt% of the triblock copolymer, were extruded at 50°C then cooled at different temperatures. Slow cooling at room temperature resulted in pores with widths of 18 ± 6 μm and lengths of 221 ± 77 μm, rapid cooling with dry ice resulted in pores with widths of 13 ± 3 μm and lengths of 58 ± 12 μm. These PCL-b-PTMC-b-PCL triblock copolymers processed into porous structures at relatively low temperatures may find wide application as designed degradable tissue engineering scaffolds. Conclusions In this preliminary study we prepared biodegradable triblock copolymers based on 1,3-trimethylene carbonate and ε-caprolactone and assessed their physical characteristics. Furthermore, we evaluated their potential as melt-processable thermoplastic elastomeric biomaterials in 3D printing of tissue engineering scaffolds.

[1]  Long Jiang,et al.  Biodegradable and Biobased Polymers , 2017 .

[2]  D. Grijpma,et al.  A Combinatorial Photocrosslinking Method for the Preparation of Porous Structures with Widely Differing Properties. , 2015, Macromolecular rapid communications.

[3]  L. Moroni,et al.  Influence of PCL molecular weight on mesenchymal stromal cell differentiation , 2015 .

[4]  Benjamin M Wu,et al.  Recent advances in 3D printing of biomaterials , 2015, Journal of Biological Engineering.

[5]  Dong-Woo Cho,et al.  Chapter 7 – Extrusion Bioprinting , 2015 .

[6]  Ibrahim T. Ozbolat,et al.  Bioprinting Technology: A Current State-of-the-Art Review , 2014 .

[7]  M. Salit,et al.  Ontology analysis of global gene expression differences of human bone marrow stromal cells cultured on 3D scaffolds or 2D films. , 2014, Biomaterials.

[8]  D. Bourissou,et al.  Mild and Efficient Preparation of Block and Gradient Copolymers by Methanesulfonic Acid Catalyzed Ring-Opening Polymerization of Caprolactone and Trimethylene Carbonate , 2013 .

[9]  T. Satoh,et al.  Diphenyl Phosphate as an Efficient Acidic Organocatalyst for Controlled/Living Ring-Opening Polymerization of Trimethylene Carbonates Leading to Block, End-Functionalized, and Macrocyclic Polycarbonates , 2013 .

[10]  J. Feijen,et al.  Ultraviolet light crosslinking of poly(trimethylene carbonate) for elastomeric tissue engineering scaffolds. , 2010, Biomaterials.

[11]  Swee Hin Teoh,et al.  Evaluation of polycaprolactone scaffold degradation for 6 months in vitro and in vivo. , 2009, Journal of biomedical materials research. Part A.

[12]  Cunxian Song,et al.  The in vivo degradation, absorption and excretion of PCL-based implant. , 2006, Biomaterials.

[13]  B. Ding,et al.  Synthesis and characterization of ABA-type block copolymers of trimethylene carbonate and ϵ-caprolactone , 2004 .

[14]  Jongseung Yoon,et al.  Enabling nanotechnology with self assembled block copolymer patterns , 2003 .

[15]  J. Feijen,et al.  Triblock Copolymers Based on 1,3‐Trimethylene Carbonate and Lactide as Biodegradable Thermoplastic Elastomers , 2003 .

[16]  Beat Hammer,et al.  In vivo efficacy of bone-marrow-coated polycaprolactone scaffolds for the reconstruction of orbital defects in the pig. , 2003, Journal of biomedical materials research. Part B, Applied biomaterials.

[17]  H. Kricheldorf,et al.  Polylactones, 47. A‐B‐A triblock copolyesters and random copolyesters of trimethylene carbonate and various lactones via macrocyclic polymerization , 1999 .

[18]  M. Mochizuki,et al.  Structural Effects on the Biodegradation of Aliphatic Polyesters , 1996 .