Superior Tissue Evolution in Slow-Degrading Scaffolds for Valvular Tissue Engineering.

Synthetic polymers are widely used to fabricate porous scaffolds for the regeneration of cardiovascular tissues. To ensure mechanical integrity, a balance between the rate of scaffold absorption and tissue formation is of high importance. A higher rate of tissue formation is expected in fast-degrading materials than in slow-degrading materials. This could be a result of synthetic cells, which aim to compensate for the fast loss of mechanical integrity of the scaffold by deposition of collagen fibers. Here, we studied the effect of fast-degrading polyglycolic acid scaffolds coated with poly-4-hydroxybutyrate (PGA-P4HB) and slow-degrading poly-ɛ-caprolactone (PCL) scaffolds on amount of tissue, composition, and mechanical characteristics in time, and compared these engineered values with values for native human heart valves. Electrospun PGA-P4HB and PCL scaffolds were either kept unseeded in culture or were seeded with human vascular-derived cells. Tissue formation, extracellular matrix (ECM) composition, remaining scaffold weight, tissue-to-scaffold weight ratio, and mechanical properties were analyzed every week up to 6 weeks. Mass of unseeded PCL scaffolds remained stable during culture, whereas PGA-P4HB scaffolds degraded rapidly. When seeded with cells, both scaffold types demonstrated increasing amounts of tissue with time, which was more pronounced for PGA-P4HB-based tissues during the first 2 weeks; however, PCL-based tissues resulted in the highest amount of tissue after 6 weeks. This study is the first to provide insight into the tissue-to-scaffold weight ratio, therewith allowing for a fair comparison between engineered tissues cultured on scaffolds as well as between native heart valve tissues. Although the absolute amount of ECM components differed between the engineered tissues, the ratio between ECM components was similar after 6 weeks. PCL-based tissues maintained their shape, whereas the PGA-P4HB-based tissues deformed during culture. After 6 weeks, PCL-based engineered tissues showed amounts of cells and ECM that were comparable to the number of human native heart valve leaflets, whereas values were lower in the PGA-P4HB-based tissues. Although increasing in time, the number of collagen crosslinks were below native values in all engineered tissues. In conclusion, this study indicates that slow-degrading scaffold materials are favored over fast-degrading materials to create organized ECM-rich tissues in vitro, which keep their three-dimensional structure before implantation.

[1]  F. Baaijens,et al.  Poly‐ε‐caprolactone scaffold and reduced in vitro cell culture: beneficial effect on compaction and improved valvular tissue formation , 2015, Journal of tissue engineering and regenerative medicine.

[2]  Simon P. Hoerstrup,et al.  Bioresorbable Scaffolds for Cardiovascular Tissue Engineering , 2014, EMJ Interventional Cardiology.

[3]  Benedikt Weber,et al.  Transcatheter implantation of homologous "off-the-shelf" tissue-engineered heart valves with self-repair capacity: long-term functionality and rapid in vivo remodeling in sheep. , 2014, Journal of the American College of Cardiology.

[4]  J. Humphrey,et al.  Beyond burst pressure: initial evaluation of the natural history of the biaxial mechanical properties of tissue-engineered vascular grafts in the venous circulation using a murine model. , 2014, Tissue engineering. Part A.

[5]  Martin Schweiger,et al.  Off-the-shelf human decellularized tissue-engineered heart valves in a non-human primate model. , 2013, Biomaterials.

[6]  Robert T. Tranquillo,et al.  Tubular Heart Valves from Decellularized Engineered Tissue , 2013, Annals of Biomedical Engineering.

[7]  Doris A Taylor,et al.  Decellularized tissue-engineered heart valve leaflets with recellularization potential. , 2013, Tissue engineering. Part A.

[8]  T. Schmitz-Rode,et al.  Non-Destructive Analysis of Extracellular Matrix Development in Cardiovascular Tissue-Engineered Constructs , 2013, Annals of Biomedical Engineering.

[9]  V. Falk,et al.  Functionality, growth and accelerated aging of tissue engineered living autologous vascular grafts. , 2012, Biomaterials.

[10]  G. Thouas,et al.  Progress and challenges in biomaterials used for bone tissue engineering: bioactive glasses and elastomeric composites , 2012, Progress in Biomaterials.

[11]  Frank P T Baaijens,et al.  Decellularized homologous tissue-engineered heart valves as off-the-shelf alternatives to xeno- and homografts. , 2012, Biomaterials.

[12]  Thomas Gilliland,et al.  Tissue-engineered vascular grafts for use in the treatment of congenital heart disease: from the bench to the clinic and back again. , 2012, Regenerative medicine.

[13]  C. Oomens,et al.  Passive and active contributions to generated force and retraction in heart valve tissue engineering , 2012, Biomechanics and modeling in mechanobiology.

[14]  van D Daphne Geemen Tissue properties and collagen remodeling in heart valve tissue engineering , 2012 .

[15]  R. Gurny,et al.  Long term performance of polycaprolactone vascular grafts in a rat abdominal aorta replacement model. , 2012, Biomaterials.

[16]  Benedikt Weber,et al.  Injectable living marrow stromal cell-based autologous tissue engineered heart valves: first experiences with a one-step intervention in primates. , 2011, European heart journal.

[17]  Misty J. Williams-Fritze,et al.  Characterization of the Natural History of Extracellular Matrix Production in Tissue-Engineered Vascular Grafts during Neovessel Formation , 2011, Cells Tissues Organs.

[18]  Swee Hin Teoh,et al.  Evaluation of polycaprolactone scaffold degradation for 6 months in vitro and in vivo. , 2009, Journal of biomedical materials research. Part A.

[19]  Casey K. Chan,et al.  Degradation behaviors of electrospun resorbable polyester nanofibers. , 2009, Tissue engineering. Part B, Reviews.

[20]  Marcel C M Rutten,et al.  Dynamic straining combined with fibrin gel cell seeding improves strength of tissue-engineered small-diameter vascular grafts. , 2009, Tissue engineering. Part A.

[21]  D. Hutmacher,et al.  The return of a forgotten polymer : Polycaprolactone in the 21st century , 2009 .

[22]  A. Mikos,et al.  The role of lipase and alpha-amylase in the degradation of starch/poly(epsilon-caprolactone) fiber meshes and the osteogenic differentiation of cultured marrow stromal cells. , 2009, Tissue engineering. Part A.

[23]  Leda Klouda,et al.  Effect of biomimetic conditions on mechanical and structural integrity of PGA/P4HB and electrospun PCL scaffolds , 2008, Journal of materials science. Materials in medicine.

[24]  Marcel C M Rutten,et al.  Autologous Human Tissue-Engineered Heart Valves: Prospects for Systemic Application , 2006, Circulation.

[25]  Frank P T Baaijens,et al.  Fibrin as a cell carrier in cardiovascular tissue engineering applications. , 2005, Biomaterials.

[26]  Eve Langelier,et al.  Tissue reorganization in response to mechanical load increases functionality. , 2005, Tissue engineering.

[27]  H. S. Azevedo,et al.  Understanding the enzymatic degradation of biodegradable polymers and strategies to control their degradation rate , 2005 .

[28]  C. Nicolini,et al.  Lipase-catalyzed degradation of poly(ε-caprolactone) , 2004 .

[29]  K J Halbhuber,et al.  Comparative study of cellular and extracellular matrix composition of native and tissue engineered heart valves. , 2004, Matrix biology : journal of the International Society for Matrix Biology.

[30]  Xuesi Chen,et al.  Enzymatic degradation of poly(L-lactide) and poly(epsilon-caprolactone) electrospun fibers. , 2004, Macromolecular bioscience.

[31]  David P. Martin,et al.  Medical applications of poly-4-hydroxybutyrate: a strong flexible absorbable biomaterial , 2003 .

[32]  Giulio Gabbiani,et al.  Mechanisms of force generation and transmission by myofibroblasts. , 2003, Current opinion in biotechnology.

[33]  L. Niklason,et al.  Effects of polyglycolic acid on porcine smooth muscle cell growth and differentiation. , 2003, Journal of biomedical materials research. Part A.

[34]  R. Adhikari,et al.  Biodegradable synthetic polymers for tissue engineering. , 2003, European cells & materials.

[35]  F J Schoen,et al.  Functional Living Trileaflet Heart Valves Grown In Vitro , 2000, Circulation.

[36]  R. Bank,et al.  Collagen Structure Regulates Fibril Mineralization in Osteogenesis as Revealed by Cross‐Link Patterns in Calcifying Callus , 2000, Journal of bone and mineral research : the official journal of the American Society for Bone and Mineral Research.

[37]  R. Bank,et al.  Sensitive fluorimetric quantitation of pyridinium and pentosidine crosslinks in biological samples in a single high-performance liquid chromatographic run. , 1997, Journal of chromatography. B, Biomedical sciences and applications.

[38]  S P Robins,et al.  Standardization of pyridinium crosslinks, pyridinoline and deoxypyridinoline, for use as biochemical markers of collagen degradation. , 1996, Clinical chemistry.

[39]  R. Bank,et al.  Amino acid analysis by reverse-phase high-performance liquid chromatography: improved derivatization and detection conditions with 9-fluorenylmethyl chloroformate. , 1996, Analytical biochemistry.

[40]  N. Tietz,et al.  Lipase in serum--the elusive enzyme: an overview. , 1993, Clinical chemistry.

[41]  D. Buttle,et al.  Improved quantitation and discrimination of sulphated glycosaminoglycans by use of dimethylmethylene blue. , 1986, Biochimica et biophysica acta.

[42]  F. Naftolin,et al.  Monitoring of collagen and collagen fragments in chromatography of protein mixtures. , 1980, Analytical biochemistry.

[43]  C. Bolognesi,et al.  Improved microfluorometric DNA determination in biological material using 33258 Hoechst. , 1979, Analytical biochemistry.