Structure and catalytic properties of VOx/MCM materials for the partial oxidation of methane to formaldehyde

Novel VOx catalysts have been developed for the partial oxidation of methane to formaldehyde by air. High surface area mesoporous siliceous MCM-41 and MCM-48 materials have been used as supports to disperse vanadium oxide to prevalent monomeric, i.e., isolated vanadium oxide species, being necessary to minimize the consecutive oxidation of the desired product to carbon oxides. On these supports, a higher concentration of isolated active sites can be obtained than on conventional silica supports. Vanadium oxide was deposited by impregnation with aqueous solutions of NH4VO3 and VO(C2O4), respectively, followed by calcination of the precursor at 873 K for 16 h. The dispersity and the nature of the vanadium oxide species, i.e., their valence state, coordination, and location on and inside the pore walls, were studied by temperature-programmed reduction, potentiometric titration, solid state 51V NMR, ESR, and UV-Vis spectroscopy. FTIR spectroscopy was used to characterize the acidic porperties. Different vanadium oxide species were observed: (i) VIVOx and VVOx species anchored to the siliceous MCM walls and (ii) VIVOx and VVOx species incorporated into the pore walls. VVOx species anchored to the surface showed properties similar to those on conventional VOx/SiO2 catalysts. However, it was found that the VOx species carry acidic V–OH groups, at least partially. The catalytic properties of the catalysts were tested in a plug flow reactor. Reaction orders with respect to methane and oxygen, respectively, as well as the apparent activation energy were comparable with those reported for vanadium oxide supported on precipitated silica, pointing to similar active sites. However, significant higher space-time yields of formaldehyde could be achieved amounting to about 2.2 kg·kgcat−1·h−1. Increased activity during cofeeding of steam could be observed due to the generation of VVO(OH)x(OSi≡)3−x surface species or the corresponding “reduced sites” VIVO(OH)x(OSi≡)2−x supposed as genuine active sites.

[1]  H. Zanthoff,et al.  The structure of catalytically active vanadium sites in V–Sb oxides: an EPR study of asynthesized and tungsten promoted working catalysts , 1999 .

[2]  R. McCormick,et al.  Methane Partial Oxidation by Unsupported and Silica Supported Iron Phosphate Catalysts: Influence of Reaction Conditions and Co-Feeding of Water on Activity and Selectivity , 1999 .

[3]  F. Frusteri,et al.  High yields in the catalytic Partial Oxidation of Natural Gas to formaldehyde : Catalyst development and reactor configuration , 1998 .

[4]  B. K. Hodnett,et al.  A comparison of the performances of selected catalysts for the partial oxidation of methane to formaldehyde at elevated pressures , 1998 .

[5]  T. Nanba,et al.  Direct conversion of methane into methanol over MoO3/SiO2 catalyst in an excess amount of water vapor , 1998 .

[6]  G. Pan,et al.  Partial oxidation of methane into formaldehyde on a catalysis-separation reactor , 1998 .

[7]  L. P. Didenko,et al.  Partial catalytic oxidation and condensation of methane by oxygen and sulphur , 1998 .

[8]  A. Zukal,et al.  Reducibility of vanadium oxide species in MCM-41 1 Dedicated to Professor Lovat V.C. Rees in recogni , 1998 .

[9]  R. Fricke,et al.  Acidity and Catalytic Behavior of Substituted MCM-48 , 1998 .

[10]  M. Wark,et al.  Selective Catalytic Reduction of NO by NH 3over Vanadium-Containing Zeolites , 1998 .

[11]  M. Bañares,et al.  PARTIAL OXIDATION OF METHANE ON SILICA-SUPPORTED VANADIA CATALYSTS. THE RELEVANCE OF CATALYST BET AREA AND GAS-PHASE ACTIVATION , 1998 .

[12]  T. Ono,et al.  Partial oxidation of CH4 over ZSM-5 catalysts , 1997 .

[13]  Chuan-bao Wang,et al.  Development of active oxide catalysts for the direct oxidation of methane to formaldehyde , 1997 .

[14]  F. Arena,et al.  Working Mechanism of Oxide Catalysts in the Partial Oxidation of Methane to Formaldehyde. I. Catalytic Behaviour of SiO 2, MoO 3/SiO 2, V 2O 5/SiO 2, TiO 2, and V 2O 5/TiO 2Systems , 1997 .

[15]  F. Arena,et al.  Working Mechanism of Oxide Catalysts in the Partial Oxidation of Methane to Formaldehyde. II. Redox Properties and Reactivity of SiO 2, MoO 3 /SiO 2, V 2O 5 /SiO 2, TiO 2, and V 2O 5 /TiO 2Systems , 1997 .

[16]  R. Fricke,et al.  Physico-chemical and catalytic properties of Al-, Ga- and Fe-substituted mesoporous materials related to MCM-41 , 1997 .

[17]  F. Frusteri,et al.  Active species and working mechanism of silica supported MoO3 and V2O5 catalysts in the selective oxidation of light alkanes , 1997 .

[18]  G. Centi,et al.  Toluene gas phase oxidation to benzaldehyde and phenol over V-containing micro- and mesoporous materials , 1997 .

[19]  B. K. Hodnett,et al.  The kinetics of the partial oxidation of methane to formaldehyde over a silica-supported vanadia catalyst , 1997 .

[20]  Heyong He,et al.  Synthesis and Spectroscopic Characterization of Vanadosilicate Mesoporous MCM-41 Molecular Sieves , 1996 .

[21]  B. K. Hodnett,et al.  The role of reactant and product bond energies in determining limitations to selective catalytic oxidations , 1996 .

[22]  G. Stucky,et al.  Pseudotetrahedral O3/2VO Centers Immobilized on the Walls of a Mesoporous, Cubic MCM-48 Support: Preparation, Characterization, and Reactivity toward Water As Investigated by 51V NMR and UV−Vis Spectroscopies , 1996 .

[23]  R. Herman,et al.  Direct conversion of methane to methanol and formaldehyde over a double-layered catalyst bed in the presence of steam , 1996 .

[24]  F. Frusteri,et al.  Temperature-programmed reaction: a powerful and reliable method for catalyst testing in the partial oxidation of methane to formaldehyde , 1995 .

[25]  A. Aboukaïs,et al.  Transition-metal ion dimers formed in CeO2: an EPR study , 1995 .

[26]  E. Schreier,et al.  Synthesis and characterization of VAPSO-44 and VAPSO-5 , 1995 .

[27]  F. Arena,et al.  On the nature of the catalytic activity of silica-based oxide catalysts in the partial oxidation of methane to formaldehyde with O2 , 1994 .

[28]  F. Arena,et al.  Effect of the metal oxide loading on the activity of silica supported MoO3 and V2O5 catalysts in the selective partial oxidation of methane , 1993 .

[29]  B. K. Hodnett,et al.  Transient experiments on the selective oxidation of methane to formaldehyde over V2O5/SiO2 studied in the temporal-analysis-of-products reactor , 1993 .

[30]  F. Frusteri,et al.  A basic approach to evaluate methane partial oxidation catalysts , 1993 .

[31]  H. Eckert,et al.  Bonding states of surface vanadium(V) oxide phases on silica: structural characterization by vanadium-51 NMR and Raman spectroscopy , 1993 .

[32]  M. Bañares,et al.  Methane-Selective Oxidation of Silica-Supported Molybdenum(VI) Catalysts: Structure and Catalytic Performance , 1993 .

[33]  J. S. Beck,et al.  Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism , 1992, Nature.

[34]  A. V. Nosov,et al.  Characterization of silica-supported vanadia-promoted rhodium catalysts by51V-NMR spectroscopy , 1992 .

[35]  A. V. Ramaswamy,et al.  Synthesis and catalytic properties of crystalline, microporous vanadium silicates with MEL structure , 1992 .

[36]  G. Centi,et al.  Physicochemical characterization of V-silicalite , 1992 .

[37]  S. Tsang,et al.  Influence of homogeneous gas phase reactions in the partial oxidation of methane to methanol and formaldehyde in the presence of oxide catalysts , 1991 .

[38]  D. Bazin,et al.  In situ high temperature and high pressure exafs studie of Pt/Al2O3 catalysts. Part I: Reduction and deactivation , 1991 .

[39]  N. Parkyns,et al.  Progress in the partial oxidation of methane to methanol and formaldehyde , 1991 .

[40]  D. Rudd,et al.  SIMULATION OF METHANE PARTIAL OXIDATION OVER SILICA-SUPPORTED MOO3 AND V2O5 , 1991 .

[41]  A. Wokaun,et al.  Spectroscopic investigation of the structure of silica-supported vanadium oxide catalysts at submonolayer coverages , 1991 .

[42]  F. Massoth,et al.  ESCA and gravimetric reduction studies on V/Al2O3 and V/SiO2 catalysts , 1990 .

[43]  H. Eckert,et al.  Solid-state vanadium-51 NMR structural studies on supported vanadium(V) oxide catalysts: vanadium oxide surface layers on alumina and titania supports , 1989 .

[44]  N. Spencer,et al.  V2O5SiO2-catalyzed methane partial oxidation with molecular oxygen , 1989 .

[45]  N. Spencer.  Partial oxidation of methane to formaldehyde by means of molecular oxygen , 1988 .

[46]  H. Eckert,et al.  Water in Silicate Glasses: Quantitation and Structural Studies by ^(1)H Solid Echo and MAS-NMR Methods , 1988 .

[47]  M. Hatano,et al.  The catalysts for the synthesis of formaldehyde by partial oxidation of methane , 1987 .

[48]  K. Klier,et al.  Partial Oxidation of Methane , 1986 .

[49]  F. Solymosi,et al.  Partial oxidation of methane by nitrous oxide over Bi2O3–SnO2 , 1985 .

[50]  Y. Murakami,et al.  Reaction mechanism of ammoxidation of toluene: IV. Oxidation state of vanadium oxide and its reactivity for toluene oxidation , 1982 .

[51]  P. Eisenberger,et al.  Observations and interpretation of x-ray absorption edges in iron compounds and proteins. , 1976, Proceedings of the National Academy of Sciences of the United States of America.

[52]  P. Richards,et al.  Far-Infrared Spectra of Al 2 O 3 Doped with Ti, V, and Cr , 1969 .

[53]  E. P. Parry,et al.  An infrared study of pyridine adsorbed on acidic solids. Characterization of surface acidity , 1963 .

[54]  C. Ballhausen,et al.  Introduction to Ligand Field Theory , 1962 .

[55]  E. Barrett,et al.  (CONTRIBUTION FROM THE MULTIPLE FELLOWSHIP OF BAUGH AND SONS COMPANY, MELLOX INSTITUTE) The Determination of Pore Volume and Area Distributions in Porous Substances. I. Computations from Nitrogen Isotherms , 1951 .