Case study: Formation of white etching layers in a failed rolling element bearing race

Abstract The aim of this investigation was to study the formation of white etching layer (WEL) induced by rolling contact fatigue (RCF) in a bearing steel. Through sectioning a failed bearing, the microstructure of the WEL was investigated using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and micro indentation test. The result showed that the WEL is harder than the matrix. It consists of refined grains of martensite, austenite and carbides. In contrast to the thermally-induced WELs, where the austenite is the result of phase transformation due to austenitization, the austenite in the WELs of the current study comes from the original retained austenite. No phase transformation occurred, indicating that the WEL was formed under deformation induced the mechanism. WELs and white etching areas (WEAs) were compared in detail. The result suggested that WELs and WEAs are actually the similar responses to large shear deformation in RCF of martensitic bearing steels.

[1]  W. Daniel,et al.  Metallurgical and physical understanding of rail squat initiation and propagation , 2012 .

[2]  Rolf Dollevoet,et al.  On the mechanism of squat formation on train rails – Part I: Origination , 2013 .

[3]  Guanlin Liu,et al.  Strain-induced refinement in a steel with spheroidal cementite subjected to surface mechanical attrition treatment , 2008 .

[4]  B. Gould,et al.  Investigating the Process of White Etching Crack Initiation in Bearing Steel , 2016, Tribology Letters.

[5]  Hisashi Harada,et al.  Microstructural Changes and Crack Initiation with White Etching Area Formation under Rolling/Sliding Contact in Bearing Steel , 2005 .

[6]  A. Pyzalla,et al.  Changes in microstructure, texture and residual stresses on the surface of a rail resulting from friction and wear , 2001 .

[7]  Liyang Xie,et al.  Hardening mechanism of Cr5 backup roll material induced by rolling contact fatigue , 2014 .

[8]  K. Hiraoka,et al.  Study on Flaking Process in Bearings by White Etching Area Generation , 2006 .

[9]  Pedro E.J. Rivera-Díaz-del-Castillo,et al.  Rolling contact fatigue in martensitic 100Cr6: Subsurface hardening and crack formation , 2014 .

[10]  Yun-Shuai Su,et al.  Microstructural evolution in bearing steel under rolling contact fatigue , 2017 .

[11]  Masato Ohnuma,et al.  Microstructural investigation of white etching layer on pearlite steel rail , 2006 .

[12]  K. Six,et al.  Development of white etching layers on rails: simulations and experiments , 2016 .

[13]  Zili Li,et al.  Laboratory simulation of martensite formation of white etching layer in rail steel , 2016 .

[14]  W. Daniel,et al.  Early stages of rail squat formation and the role of a white etching layer , 2013 .

[15]  Hans-Jörg Fecht,et al.  Comparison between nanophase formation during friction induced surface wear and mechanical attrition of a pearlitic steel , 1996 .

[16]  Werner Österle,et al.  Investigation of white etching layers on rails by optical microscopy, electron microscopy, X-ray and synchrotron X-ray diffraction , 2001 .

[17]  Hans-Jörg Fecht,et al.  Formation of white-etching layers on rail treads , 1996 .

[18]  Study on Rolling Contact Fatigue in Hydrogen Environment at a Contact Pressure below Basic Static Load Capacity , 2010 .

[19]  Seok-Jin Kwon,et al.  Numerical stress analysis and rolling contact fatigue of White Etching Layer on rail steel , 2011 .

[20]  Uta Klement,et al.  Formation mechanisms of white layers induced by hard turning of AISI 52100 steel , 2015 .

[21]  W. Daniel,et al.  Surface damage on new AS60 rail caused by wheel slip , 2012 .

[22]  H. Bhadeshia,et al.  Soft novel form of white-etching matter and ductile failure of carbide-free bainitic steels under rolling contact stresses , 2016 .

[23]  J. Svoboda,et al.  Microscopic investigation of surface layers on rails , 2005 .

[24]  Pedro E.J. Rivera-Díaz-del-Castillo,et al.  Rolling contact fatigue in bearings: multiscale overview , 2012 .

[25]  R. D. Evans,et al.  Microstructural Alterations in Bearing Steels under Rolling Contact Fatigue Part 1—Historical Overview , 2013 .

[26]  John H. Beynon,et al.  Rolling contact fatigue of white etching layer: Part 1: Crack morphology , 2007 .

[27]  Elucidating white-etching matter through high-strain rate tensile testing , 2017 .

[28]  Zhiping Luo,et al.  Phase and microstructural evolution in white etching layer of a pearlitic steel during rolling–sliding friction , 2016 .

[29]  Hans-Jörg Fecht,et al.  Surface modification, corrugation and nanostructure formation of high speed railway tracks , 1997 .

[30]  Robert J.K. Wood,et al.  A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel , 2013 .

[32]  M.-H. Evans,et al.  Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation , 2014 .

[33]  W. Reimers,et al.  Investigation of the Formation of White Etching Layers and Residual Stresses in Railway Rails , 2005 .

[34]  A. Jakovics,et al.  White Etching Crack Root Cause Investigations , 2015 .

[35]  Hans-Jörg Fecht,et al.  Nanostructure formation on the surface of railway tracks , 2001 .

[36]  Kenred Stadler,et al.  Investigation on the mechanisms of white etching crack (WEC) formation in rolling contact fatigue and identification of a root cause for bearing premature failure , 2016 .

[37]  Tomas Beno,et al.  Cutting temperatures during hard turning—Measurements and effects on white layer formation in AISI 52100 , 2014 .

[38]  J. Duffy,et al.  An experimental study of the formation process of adiabatic shear bands in a structural steel , 1988 .

[39]  Jia Li,et al.  A microstructural investigation of the surface of a drilled hole in carbon steels , 2007 .