Understanding the Resistive Switching Phenomena of Stacked Al/Al2O3/Al Thin Films from the Dynamics of Conductive Filaments

We present the resistive switching characteristics of Metal-Insulator-Metal (MIM) devices based on amorphous Al2O3 which is deposited by Atomic Layer Deposition (ALD). A maximum processing temperature for this memory device is 300°C, making it ideal for Back-End-of-Line (BEOL) processing. Although some variations in the forming, set, and reset voltages (,, and ) are obtained for many of the measured MIM devices (mainly due to roughness variations of the MIM interfaces as observed after atomic-force microscopy analysis), the memristor effect has been obtained after cyclic measurements. These resistive transitions in the metal oxide occur for both bipolar and unipolar conditions, while the ratio is around 4–6 orders of magnitude and is formed at gate voltages of V. In unipolar mode, a gradual reduction in is observed and is related to combined (a) incomplete dissolution of conductive filaments (made of oxygen vacancies and metal ions) which leaves some residuals and (b) thickening of chemically reduced Al2O3 during localized Joule heating. This is important because, by analyzing the macroscopic resistive switching behavior of this MIM structure, we could indirectly relate it to microscopic and/or nanoscopic phenomena responsible for the physical mechanism upon which most of these devices operate.

[1]  Xing Wu,et al.  Intrinsic nanofilamentation in resistive switching , 2013 .

[2]  Andrew M. Minor,et al.  Focused Ion Beam Microscopy and Micromachining , 2007 .

[3]  Robert Elliman,et al.  Effect of Electrode Roughness on Electroforming in HfO 2 and Defect-Induced Moderation of Electric-Field Enhancement , 2015 .

[4]  D. Tsai,et al.  Surface effects of electrode-dependent switching behavior of resistive random-access memory , 2016 .

[5]  D. Stewart,et al.  The missing memristor found , 2008, Nature.

[6]  L. Larcher,et al.  Localized characterization of charge transport and random telegraph noise at the nanoscale in HfO2 films combining scanning tunneling microscopy and multi-scale simulations , 2017 .

[7]  Y. Asai,et al.  Competitive effects of oxygen vacancy formation and interfacial oxidation on an ultra-thin HfO2-based resistive switching memory: beyond filament and charge hopping models. , 2016, Physical chemistry chemical physics : PCCP.

[8]  T. Mikolajick,et al.  Reliability of Al2O3-doped ZrO2 high-k dielectrics in three-dimensional stacked metal-insulator-metal capacitors , 2010 .

[9]  Leon O. Chua,et al.  Three Fingerprints of Memristor , 2013, IEEE Transactions on Circuits and Systems I: Regular Papers.

[10]  Surface effect on resistive switching behaviors of ZnO , 2011 .

[11]  R. Dittmann,et al.  Redox‐Based Resistive Switching Memories – Nanoionic Mechanisms, Prospects, and Challenges , 2009, Advanced materials.

[12]  A. Torres,et al.  MOHOS-type memory performance using HfO2 nanoparticles as charge trapping layer and low temperature annealing , 2012 .

[13]  A. Torres,et al.  HfO2 nanoparticles embedded within a SOG-based oxide matrix as charge trapping layer for SOHOS-type memory applications , 2012 .

[14]  D. Misra,et al.  Oxygen vacancy defect engineering using atomic layer deposited HfAlOx in multi-layered gate stack , 2016 .

[16]  O. Heinonen,et al.  The effect of a Ta oxygen scavenger layer on HfO2-based resistive switching behavior: thermodynamic stability, electronic structure, and low-bias transport. , 2016, Physical chemistry chemical physics : PCCP.

[17]  K. Pey,et al.  Performance of ultra‐thin HfO2‐based MIM devices after oxygen modulation and post‐metallization annealing in N2 , 2016 .

[18]  Leon O. Chua.  Resistance switching memories are memristors , 2011 .

[19]  Dalibor Biolek,et al.  Some fingerprints of ideal memristors , 2013, 2013 IEEE International Symposium on Circuits and Systems (ISCAS2013).

[20]  Kin Leong Pey,et al.  The nature of dielectric breakdown , 2008 .

[21]  L. Larcher,et al.  Single vacancy defect spectroscopy on HfO2 using random telegraph noise signals from scanning tunneling microscopy , 2016 .

[22]  K. Pey,et al.  CAFM based spectroscopy of stress-induced defects in HfO2 with experimental evidence of the clustering model and metastable vacancy defect state , 2016, 2016 IEEE International Reliability Physics Symposium (IRPS).

[23]  Xing Wu,et al.  Evolution of Filament Formation in Ni/HfO2/SiOx/Si‐Based RRAM Devices , 2015 .

[24]  Xing Wu,et al.  Compliance current dominates evolution of NiSi2 defect size in Ni/dielectric/Si RRAM devices , 2016, Microelectron. Reliab..

[25]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[26]  S. Yasuda,et al.  Nonpolar resistance switching of metal/binary-transition-metal oxides/metal sandwiches: Homogeneous/inhomogeneous transition of current distribution , 2007, cond-mat/0702564.

[27]  A. Herrera‐Gomez,et al.  Accurate modeling of gate tunneling currents in Metal-Insulator-Semiconductor capacitors based on ultra-thin atomic-layer deposited Al2O3 and post-metallization annealing , 2017 .

[28]  W. Marsden.  I and J , 2012 .

[29]  Nagarajan Raghavan,et al.  Analysis of quantum conductance, read disturb and switching statistics in HfO2 RRAM using conductive AFM , 2016, Microelectron. Reliab..

[30]  Alfonso Torres-Jácome,et al.  Influence of the surface roughness of the bottom electrode on the resistive-switching characteristics of Al/Al2O3/Al and Al/Al2O3/W structures fabricated on glass at 300 °C , 2014, Microelectron. Reliab..

[31]  Y. Fujisaki.  Review of Emerging New Solid-State Non-Volatile Memories , 2013 .