Deposition of superhydrophobic nanostructured Teflon-like coating using expanding plasma arc

Abstract A novel approach was used to grow nanostructured Teflon-like superhydrophobic coatings on stainless steel (SS). In this method Teflon tailings were pyrolyzed to generate fluorocarbon precursor molecules, and an expanding plasma arc (EPA) was used to polymerize these precursors to deposit Teflon-like coating. The coating shows super hydrophobic behavior with water contact angle (WCA) of 165°. The coating was observed to be uniform. It consists of nanostructured (∼80–200 nm) features, which were confirmed by scanning electron microscopy. The chemical bond state of the film was determined by XPS and FTIR, which indicate the dominance of –CF 2 groups in the deposited coating. The combination of nanofeature induced surface roughness and the low surface energy imparted by Teflon-like coating is responsible for the observed superhydrophobic nature.

[1]  P. Favia,et al.  Deposition of super-hydrophobic fluorocarbon coatings in modulated RF glow discharges , 2003 .

[2]  D. Bodas,et al.  Deposition of PTFE thin films by RF plasma sputtering on 〈100〉 silicon substrates , 2005 .

[3]  Masatsugu Shimomura,et al.  Superhydrophobic and lipophobic properties of self-organized honeycomb and pincushion structures. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[4]  Didem Öner,et al.  Ultrahydrophobic Surfaces. Effects of Topography Length Scales on Wettability , 2000 .

[5]  O. Takai,et al.  Preparation of ultra water-repellent films by microwave plasma-enhanced CVD , 1997 .

[6]  Van de Sanden,et al.  Fast deposition of amorphous carbon films by an expanding cascaded arc plasma jet , 1995 .

[7]  S. Wiberley,et al.  Introduction to infrared and Raman spectroscopy , 1965 .

[8]  J. Heberlein,et al.  Synthesis of Si–C–N coatings by thermal Plasmajet chemical vapour deposition applying liquid precursors , 2001 .

[9]  C. Hsieh,et al.  Influence of fluorine/carbon atomic ratio on superhydrophobic behavior of carbon nanofiber arrays , 2006 .

[10]  M. Kormunda,et al.  Rf sputtering of composite SiOx/plasma polymer films and their basic properties , 2002 .

[11]  P. Tsai,et al.  An Integrated Approach to Initiate Preventive Strategies for Workers Exposed to Teflon Pyrolytic Gases in a Plastic Industry , 2000 .

[12]  Lei Jiang,et al.  Super-Hydrophobicity of Large-Area Honeycomb-Like Aligned Carbon Nanotubes , 2002 .

[13]  C. Sung,et al.  Endurable water-repellent glass for automobiles , 1999 .

[14]  Wei Chen,et al.  Ultrahydrophobic and Ultralyophobic Surfaces: Some Comments and Examples , 1999 .

[15]  Jin Zhai,et al.  Super-hydrophobic surfaces: From natural to artificial , 2002 .

[16]  Gareth H. McKinley,et al.  Superhydrophobic Carbon Nanotube Forests , 2003 .