Corrosiveness of Thermally Modified Wood

Thermally modified wood is becoming commercially available in North America for use in outdoor applications. While there have been many studies on how thermal modification affects the dimensional stability, water vapor sorption, and biodeterioration of wood, little is known about whether thermally modified wood is corrosive to metal fasteners and hangers used to hold these members in place. As thermally modified wood is used in outdoor applications, it has the potential to become wet which may lead to corrosion of embedded fasteners. Here, we examine the corrosiveness of thermally modified ash and oak in an exposure test where stainless steel, hot-dip galvanized steel, and carbon steel nails are driven into wood and exposed to a nearly 100% relative humidity environment at 27 °C for one year. The corrosion rates were compared against control specimens of untreated and preservative-treated southern pine. Stainless steel fasteners did not corrode in any specimens regardless of the treatment. The thermal modification increased the corrosiveness of the ash and oak, however, an oil treatment that is commonly applied by the manufacturer to the wood after the heat treatment reduced the corrosiveness. The carbon steel fasteners exhibited higher corrosion rates in the thermally modified hardwoods than in the preservative-treated pine control. Corrosion rates of galvanized fasteners in the hardwoods were much lower than carbon steel fasteners. These data can be used to design for corrosion when building with thermally modified wood, and highlight differences between corrosion of metals embedded in wood products.

[1]  Rebecca E. Ibach,et al.  WOOD PRESERVATION. , 1927, Science.

[2]  A. Stamm,et al.  Minimizing wood shrinkage and swelling : effect of heating in various gases , 1937 .

[3]  R. Farmer.  Corrosion of Metals in Association with Wood , 1967 .

[4]  D. Knotková‐Čermáková,et al.  Corrosive Effect of Plastics, Rubber and Wood on Metals in Confined Spaces , 1971 .

[5]  C. Smith,et al.  The corrosion of metals by wood , 1982 .

[6]  M. Omizo,et al.  Modeling , 1983, Encyclopedic Dictionary of Archaeology.

[7]  A. Baker,et al.  Corrosion of nails in CCA- and ACA-treated wood in two environments , 1992 .

[8]  K. Becker,et al.  Gravimetric determination of tannins and their correlations with chemical and protein precipitation methods , 1993 .

[9]  J. K. Dennis,et al.  Corrosion behaviour of zinc and zinc alloy coated steel in preservative treated timber , 1995 .

[10]  J. K. Dennis,et al.  Corrosion Resistance of Zinc-alloy Coated Steel in Construction Industry Environments , 1997 .

[11]  J. Jermer,et al.  Corrosion of fasteners in heat-treated wood – progress report after two years’ exposure outdoors , 2005 .

[12]  H. Makkar.  Use of nuclear and related techniques to develop simple tannin assays for predicting and improving the safety and efficiency of feeding ruminants on tanniniferous tree foliage : Achievements, result implications, and future research , 2005 .

[13]  X. G. Zhang,et al.  Corrosion of Zinc and Zinc Alloys , 2005 .

[14]  C. Hill,et al.  Wood Modification: Chemical, Thermal and Other Processes , 2006 .

[15]  C. Brischke,et al.  Interrelationship between the severity of heat treatments and sieve fractions after impact ball milling: a mechanical test for quality control of thermally modified wood , 2006 .

[16]  M. Rifai,et al.  Investigation and analysis of three gilded wood samples from the tomb of Tutankhamun , 2007 .

[17]  Samuel L. Zelinka,et al.  Uncertainties in Corrosion Rate Measurements of Fasteners Exposed to Treated Wood at 100 % Relative Humidity , 2007 .

[18]  T. Amburgey,et al.  A comparative study on brown-rot fungus decay and subterranean termite resistance of thermally-modified and ACQ-C-treated wood , 2007, Holz als Roh- und Werkstoff.

[19]  D. Rammer,et al.  Corrosion Of Metals In Contact With Treated Wood: Developing Test Methods , 2008 .

[20]  C. Brischke,et al.  INCREASED RESISTANCE OF THERMALLY MODIFIED NORWAY SPRUCE TIMBER TMT AGAINST BROWN ROT DECAY BY OLIGOPORUS PLACENTA STUDY ON THE MODE OF PROTECTIVE ACTION , 2008 .

[21]  Analytical Determination of the Surface Area of a Threaded Fastener , 2008 .

[22]  Douglas R. Rammer,et al.  Electrochemical corrosion testing of fasteners in extracts of treated wood , 2008 .

[23]  G. Kear,et al.  Weight loss studies of fastener materials corrosion in contact with timbers treated with copper azole and alkaline copper quaternary compounds , 2009 .

[24]  D. R. Rammer,et al.  Optical method for measuring the surface area of a threaded fastener , 2009 .

[25]  Douglas R. Rammer,et al.  Corrosion Rates of Fasteners in Treated Wood Exposed to 100% Relative Humidity , 2009 .

[26]  E. Furtado,et al.  Decay resistance of thermally-modified Eucalyptus grandis wood at 140 degrees C, 160 degrees C, 180 degrees C, 200 degrees C and 220 degrees C. , 2010, Bioresource technology.

[27]  M. Pétrissans,et al.  Use of wood elemental composition to predict heat treatment intensity and decay resistance of different softwood and hardwood species , 2010 .

[28]  Donald S. Stone,et al.  Exposure testing of fasteners in preservative treated wood: Gravimetric corrosion rates and corrosion product analyses , 2010 .

[29]  C. Hill,et al.  Analysis of the water vapour sorption isotherms of thermally modified acacia and sesendok , 2010 .

[30]  D. Stone,et al.  The effect of tannins and pH on the corrosion of steel in wood extracts , 2011 .

[31]  D. Stone,et al.  Corrosion of metals in wood: Comparing the results of a rapid test method with long-term exposure tests across six wood treatments , 2011 .

[32]  Dominique Derome,et al.  Combining hygrothermal and corrosion models to predict corrosion of metal fasteners embedded in wood , 2011 .

[33]  C. Hill,et al.  Water vapour sorption behaviour of thermally modified wood , 2013 .

[34]  D. Stone,et al.  Mechanism of Transport Through Wood Cell Wall Polymers , 2013 .

[35]  C. Brischke,et al.  Mode of action of brown rot decay resistance in modified wood: a review , 2014 .

[36]  S. Zelinka.  Corrosion of Metals in Wood Products , 2014 .

[37]  Dominique Derome,et al.  The effect of moisture content on the corrosion of fasteners embedded in wood subjected to alkaline copper quaternary treatment , 2014 .

[38]  S. Zelinka.  Comparing the Methodologies in ASTM G198 Using Combined Hygrothermal-Corrosion Modeling , 2014 .

[39]  M. Zhilin,et al.  New AMS Dating of Bone and Antler Weapons from the Shigir Collections Housed in the Sverdlovsk Regional Museum, Urals, Russia , 2015, Proceedings of the Prehistoric Society.

[40]  J. Van Acker,et al.  Introduction of the COST FP 1303 Cooperative Performance Test , 2015 .

[41]  Dominique Derome,et al.  Comparison of the corrosion of fasteners embedded in wood measured in outdoor exposure with the predictions from a combined hygrothermal-corrosion model , 2016 .

[42]  M. Thévenon,et al.  Control of wood thermal treatment and its effects on decay resistance: a review , 2016, Annals of Forest Science.

[43]  J. Jakes,et al.  The role of chemical transport in the brown-rot decay resistance of modified wood , 2016 .

[44]  J. Jermer,et al.  Corrosion of fasteners in furfurylated wood : final report after 9 years exposure outdoors , 2017 .

[45]  S. Zelinka.  Role of transport in wood damage mechanisms – WSE 2017 keynote lecture , 2018 .

[46]  S. Zelinka,et al.  Corrosion of metal fasteners embedded in acetylated and untreated wood at different moisture contents , 2018, Wood Material Science & Engineering.

[47]  J. Jakes,et al.  Acetylation increases relative humidity threshold for ion transport in wood cell walls – A means to understanding decay resistance , 2018, International Biodeterioration & Biodegradation.

[48]  Peter N. Ciesielski,et al.  Effects of Moisture on Diffusion in Unmodified Wood Cell Walls: A Phenomenological Polymer Science Approach , 2019 .

[49]  B. Lai,et al.  Copper distribution and oxidation states near corroded fasteners in treated wood , 2019, SN Applied Sciences.