Effects of alkaline-activated fly ash and Portland cement on soft soil stabilisation

This paper studies the effects of sodium-based alkaline activators and class F fly ash on soil stabilisation. Using the unconfined compressive strength test (UCS), the effectiveness of this binder is compared with that of a common cement-based binder. Influence of the activator/ash ratio, sodium oxide/ash ratio and sodium hydroxide concentration was also analysed. Sodium hydroxide concentrations of 10, 12.5 and 15 molal were used for the alkaline-activated specimens (AA), with activator/ash ratios between 1 and 2.5 and ash percentages of 20, 30 and 40 %, relatively to the total solids (soil + ash). UCS was determined at curing periods of 7, 28, 90 and 365 days, and the most effective mixtures were analysed for mineralogy with XRD. The results showed a clear increase in strength with decreasing activator/ash ratio (up to a maximum of 43.4 MPa), which is a positive result since the activator is the most expensive component in the mixture. Finally, UCS results of the cement and AA samples, at 28 days curing, were very similar. However, AA results proved to be just between 20 and 40 % of the maximum UCS obtained at 1 year curing, while cement results at 28 days are expected to be between 80 and 90 % of its maximum.

[1]  Xiaomin Zhu,et al.  Alkali-activated fly ash-based geopolymers with zeolite or bentonite as additives , 2009 .

[2]  J.S.J. van Deventer,et al.  Effect of the Alkali Metal Activator on the Properties of Fly Ash-Based Geopolymers , 1999 .

[3]  P. Svoboda,et al.  Assessment of phase formation in alkali activated low and high calcium fly ashes in building materials , 2010 .

[4]  Ángel Palomo,et al.  Alkali-activated fly ashes: A cement for the future , 1999 .

[5]  J. Deventer,et al.  The geopolymerisation of alumino-silicate minerals , 2000 .

[6]  Stephanie Glendinning,et al.  Sub-bases layers of residual granite soil stabilised with lime , 2009 .

[7]  Kiyonobu Kasama,et al.  HIGH-STRENGTHENING OF CEMENT-TREATED CLAY BY MECHANICAL DEHYDRATION , 2007 .

[8]  Ángel Palomo,et al.  An XRD Study of the Effect of the SiO2/Na2O Ratio on the Alkali Activation of Fly Ash , 2007 .

[9]  H. Khoury,et al.  Utilization of bituminous limestone ash from EL-LAJJUN area for engineering applications , 2008 .

[10]  D Hardjito,et al.  Fly Ash-Based Geopolymer Concrete , 2005 .

[11]  M. J. Tomlinson,et al.  Foundation design and construction , 1963 .

[12]  C. Villa,et al.  Geopolymer synthesis using alkaline activation of natural zeolite , 2010 .

[13]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[14]  J. I. Escalante-García,et al.  Coarse blast furnace slag as a cementitious material, comparative study as a partial replacement of Portland cement and as an alkali activated cement , 2009 .

[15]  Hua Xu,et al.  Effect of Source Materials on Geopolymerization , 2003 .

[16]  Loreal V. Heebink,et al.  ENVIRONMENTAL EVALUATION FOR UTILIZATION OF ASH IN SOIL STABILIZATION , 2001 .

[17]  J. W. P. and,et al.  Characterization of Fly-Ash-Based Geopolymeric Binders Activated with Sodium Aluminate , 2002 .

[18]  Chanakya Arya,et al.  Buckling resistance of unstiffened webs , 2009 .

[19]  Stephanie Glendinning,et al.  Deep soft soil improvement by alkaline activation , 2011 .

[20]  Masaki Kitazume,et al.  QA/QC for deep-mixed ground: current practice and future research needs , 2011 .

[21]  R. P. Johnson,et al.  General rules and rules for buildings , 2004 .

[22]  Fernando Pacheco-Torgal,et al.  Durability of alkali-activated binders: A clear advantage over Portland cement or an unproven issue? , 2012 .

[23]  P. Chindaprasirt,et al.  Comparative study on the characteristics of fly ash and bottom ash geopolymers. , 2009, Waste management.

[24]  J.S.J. van Deventer,et al.  The interface between natural siliceous aggregates and geopolymers , 2004 .

[25]  B. Rangan,et al.  DEVELOPMENT AND PROPERTIES OF LOW-CALCIUM FLY ASH-BASED GEOPOLYMER CONCRETE , 2005 .

[26]  J. Deventer,et al.  Understanding the relationship between geopolymer composition, microstructure and mechanical properties , 2005 .

[27]  Jadambaa Temuujin,et al.  Preparation and characterisation of fly ash based geopolymer mortars , 2010 .

[28]  Shigemitsu Hatanaka,et al.  High-Strength Geopolymer Using Fine High-Calcium Fly Ash , 2011 .

[29]  Á. Palomo,et al.  Characterisation of fly ashes. Potential reactivity as alkaline cements , 2003 .