Silicon carbide for power devices

An overview of the status of SiC technology for power devices is discussed. 4H-SiC is the most desirable SiC polytype for power devices because of its superior electron transport properties. Micropipe defect densities in 4H-SiC have been dramatically reduced, with 0.8 cm/sup -2/ being demonstrated on a 35 mm wafer. Interface trap densities of 1/spl times/10/sup 11/ cm/sup -2/ eV/sup -1/ at the oxide/SiC interface have been achieved, resulting in a high SiC NMOSFET channel mobility of 72 cm/sup 2//V-sec. Device lifetimes for SiC n-channel MOSFETs have are projected to be 5 years at 350/spl deg/C, and time dependent dielectric breakdown of oxides on p-type SiC have lifetimes >700 years at 2 MV/cm and 350/spl deg/C. Sheet resistivities of <10 k/spl Omega//sq. and p-type contact resistivities less than 10/sup -5/ /spl Omega/-cm/sup 2/ have been obtained using high temperature Al/sup +/ ion implantation, and the first SiC CMOS circuits have been demonstrated using this technology. Power MOSFETs in 4H-SiC have been demonstrated to have specific on-resistances lower than equivalent Si devices, and blocking voltages as high as 800 V have been achieved. The highest power devices to date are 4.2 kW, 700 V 4H-SiC npnp thyristors, and their speed is very high, with a t/sub rr/=105 nsecs and maximum operating frequency of 250 kHz.

[1]  G. A. Slack,et al.  Nonmetallic crystals with high thermal conductivity , 1973 .

[2]  E. A. Burgemeister,et al.  Thermal conductivity and electrical properties of 6H silicon carbide , 1979 .

[3]  R. Stein.  Formation of macrodefects in SiC , 1993 .

[4]  B. J. Baliga,et al.  Comparison of 6H-SiC, 3C-SiC, and Si for power devices , 1993 .

[5]  M. Bhatnagar,et al.  Edge terminations for SiC high voltage Schottky rectifiers , 1993, [1993] Proceedings of the 5th International Symposium on Power Semiconductor Devices and ICs.

[6]  R. C. Clarke,et al.  Growth of large SiC single crystals , 1993 .

[7]  P. Neudeck,et al.  Performance limiting micropipe defects in silicon carbide wafers , 1994, IEEE Electron Device Letters.

[8]  J. Palmour,et al.  Conductivity Anisotropy in Epitaxial 6H and 4H Sic , 1994 .

[9]  Anne Henry,et al.  A 4.5 kV 6H silicon carbide rectifier , 1995 .

[10]  Christopher Harris,et al.  SiC power device passivation using porous SiC , 1995 .

[11]  Ion-implantation and activation of aluminum in 6H-SiC , 1995 .

[12]  M. V. Rao,et al.  Al, Al/C and Al/Si implantations in 6H-SiC , 1996 .

[13]  J.W. Palmour,et al.  High power 4H-SiC thyristors , 1996, 1996 54th Annual Device Research Conference Digest.

[14]  Gregory M. Johnson,et al.  Demonstration of a 6H-SiC CMOS technology , 1996, 1996 54th Annual Device Research Conference Digest.

[15]  Hot implantation of N^+ into α-SiC epilayers , 1996 .

[16]  John W. Palmour,et al.  Improved oxidation procedures for reduced SiO2/SiC defects , 1996 .

[17]  A. Henry,et al.  Nitrogen doping concentration as determined by photoluminescence in 4H– and 6H–SiC , 1996 .