Wear and friction characteristics of CGRP composite under wet contact condition using two different test techniques

This paper presents an investigation on wear and friction characteristics of chopped strand mat (CSM) glass fibres 450 g/m2 reinforced polyester (CGRP) composite under wet contact condition against polished stainless steel counterface. The experiments were conducted using two different techniques, Pin-on-Disc (POD) and Block-on-Ring (BOR), which were integrated in a newly developed machine that could carry both techniques running simultaneously against identical counterface characteristics. CGRP composite was tested in two different orientations (parallel and anti-parallel), i.e. P-O and AP-O. The effects of test duration (5-30 min), rotational speed (500 and 700 rpm) and applied load (30-100 N) on specific wear rate and friction coefficient were evaluated. Worn surface morphologies of the composite were observed with a scanning electron microscopy (SEM) and the damage features were characterized. The results revealed that CSM glass fibres orientations and test parameters have a significant influence on the wear and frictional characteristics of the composite in both POD and BOR techniques. CGRP in AP-O showed better wear and frictional performance compared to P-O. When the composite was tested using POD, abrasive wear nature was observed on the worn surface in both orientations. Meanwhile, using BOR technique, smoother surface was observed in AP-O. Presence of water assisted to cool the interface and polish the composite surface in the case of BOR. On the other hand, in POD, rough surface was observed on the composite surface in both P-O and AP-O. Additionally, the counterface roughness was increased at all tested condition and highly pronounced in POD when the CGRP was tested in P-O.

[1]  J. Wu,et al.  The tribological properties of Kevlar pulp reinforced epoxy composites under dry sliding and water lubricated condition , 2006 .

[2]  Zhongya Zhang,et al.  Effect of fiber length on the wear resistance of short carbon fiber reinforced epoxy composites , 2007 .

[3]  M. Furey,et al.  Tribological behavior of unidirectional graphite-epoxy and carbon-PEEK composites , 1993 .

[4]  A. Borruto,et al.  Influence of surface wettability on friction and wear tests , 1998 .

[5]  J. Bijwe,et al.  Influence of orientation and volume fraction of Aramid fabric on abrasive wear performance of polyethersulfone composites , 2006 .

[6]  H. Pihtili,et al.  Effect of load and speed on the wear behaviour of woven glass fabrics and aramid fibre-reinforced composites , 2002 .

[7]  Nihat Tosun,et al.  Investigation of the wear behaviour of a glass-fibre-reinforced composite and plain polyester resin , 2002 .

[8]  Yuji Yamamoto,et al.  Friction and wear of water lubricated PEEK and PPS sliding contacts. Part 2. Composites with carbon or glass fibre , 2004 .

[9]  Jin Tong,et al.  Tribological behaviours of PA/UHMWPE blend under dry and lubricating condition , 2006 .

[10]  B. F. Yousif,et al.  Tribological Evaluations of Polyester Composites Considering Three Orientations of CSM Glass Fibres Using BOR Machine , 2007 .

[11]  B. F. Yousif,et al.  On The Effect Of Woven Glass Fabric Orientations On Wear And Friction Properties Of Polyester Composite , 2007 .

[12]  Yuji Yamamoto,et al.  Friction and Wear of Water Lubricated PEEK and PPS Sliding Contacts , 2002 .

[13]  B. F. Yousif,et al.  Tribological studies of polyester reinforced with CSM 450-R-glass fiber sliding against smooth stainless steel counterface , 2006 .

[14]  B. F. Yousif,et al.  On Tribo-Test Machine Integrating Pin-on-Disc and Block-on-Ring , 2007 .

[15]  B. F. Yousif,et al.  An investigation on worn surfaces of chopped glass fibre reinforced polyester through SEM observations , 2008 .

[16]  Lei Chen,et al.  Comparative investigation on the wear and transfer behaviors of carbon fiber reinforced polymer composites under dry sliding and water lubrication , 2005 .