Swelling and methylene blue adsorption of poly(N,N-dimethylacrylamide-co-2-hydroxyethyl methacrylate) hydrogel

Abstract Dyes from wastewater have a negative impact on health and environment, even at low concentrations. Several methods have been proposed for their removal, one of them is using hydrogels as adsorbents for wastewater treatment. In this work, we propose N,N-dimethylacrylamide and 2-hydroxyethyl methacrylate copolymer (p(HEMA-co-DMAa)) as an adsorbent alternative. Swelling behavior as function of pH and temperature was studied. Morphological characterization of crosslinked copolymer and its hydrogel structure were performed by SEM analysis and FTIR spectroscopy. Swelling measurements and sorption studies were made using methylene blue (as cationic dye model) under different medium pH. Results from confocal images of swollen p(HEMA-co-DMAa) in methylene blue solutions indicate a macroporous material formed. The dye diffuses homogeneously through the entire hydrogel during swelling. The p(HEMA-co-DMAa) hydrogels were able to uptake up to 3.6 times their weight of water depending on temperature; the lower the equilibrium temperature the higher the water uptake. P(HEMA-co-DMAa) hydrogels adsorption capacity is competitive compared with other adsorbents already reported. It was determined that the LCST of the hydrogel at 321 K and the formation of a complex at pH = 8. The optimal removal time was at 4 h after the copolymer was added. The hydrogel was stable (as suggested by FTIR spectrum) and able to uptake methylene blue in a wide pH range. Therefore, it is suitable as adsorbent alternative; additionally, the p(HEMA-co-DMAa) hydrogels would be environmentally friendly due to their biocompatibility and non-cytotoxicity.

[1]  A. Dirani,et al.  Temperature Dependence of the Surface and Volume Hydrophilicity of Hydrophilic Polymer Brushes. , 2016, Langmuir : the ACS journal of surfaces and colloids.

[2]  Athanassia Athanassiou,et al.  Transparent and flexible amorphous cellulose-acrylic hybrids , 2016 .

[3]  Takaaki Sato,et al.  Investigation of Changes in the Microscopic Structure of Anionic Poly(N-isopropylacrylamide-co-Acrylic acid) Microgels in the Presence of Cationic Organic Dyes toward Precisely Controlled Uptake/Release of Low-Molecular-Weight Chemical Compound. , 2016, Langmuir : the ACS journal of surfaces and colloids.

[4]  S. Meriç,et al.  Preparation of N-isopropylacrylamide/itaconic acid/Pumice highly swollen composite hydrogels to explore their removal capacity of methylene blue , 2017 .

[5]  D. Horák,et al.  Raft polymerization ofN,N-dimethylacrylamide from magnetic poly(2-hydroxyethyl methacrylate) microspheres to suppress nonspecific protein adsorption , 2016 .

[6]  Xue Li,et al.  Stimuli-responsive polymers and their applications , 2017 .

[7]  C. Peniche,et al.  Synthesis and characterization of pH and temperature responsive poly(2-hydroxyethyl methacrylate-co-acrylamide) hydrogels , 2015 .

[8]  G. Hsiue,et al.  Poly(2-hydroxyethyl methacrylate) film as a drug delivery system for pilocarpine. , 2001, Biomaterials.

[9]  A-Young Sung,et al.  Ophthalmic application of poly(HEMA)s containing nanoparticles and dimethylacrylamide. , 2012, Journal of nanoscience and nanotechnology.

[10]  Hong Zhang,et al.  Facile preparation of poly(acrylic acid–acrylamide) hydrogels by frontal polymerization and their use in removal of cationic dyes from aqueous solution , 2011 .

[11]  A. Drozdov,et al.  Modeling the effects of temperature and pH on swelling of stimuli-responsive gels , 2015 .

[12]  Kouichi Sutani,et al.  Stimulus responsive drug release from polymer gel.: Controlled release of ionic drug from polyampholyte gel , 2002 .

[13]  M. Serpe,et al.  Poly (N-isopropylacrylamide) microgel-based assemblies for organic dye removal from water. , 2011, ACS applied materials & interfaces.

[14]  T. Singh,et al.  Kinetics and thermodynamics of cationic dye adsorption onto dry and swollen hydrogels poly(acrylic acid-sodium acrylate-acrylamide) sodium humate , 2015 .

[15]  A. Concheiro,et al.  Surface functionalization of polypropylene devices with hemocompatible DMAAm and NIPAAm grafts for norfloxacin sustained release , 2011 .

[16]  A. Ibrahim,et al.  Synthesis, Characterization, Swelling Studies and Dye Removal of Chemically Crosslinked Acrylic Acid/Acrylamide/N,N-Dimethyl Acrylamide Hydrogels , 2016 .

[17]  M. Gutiérrez,et al.  Ice-Templated Materials: Sophisticated Structures Exhibiting Enhanced Functionalities Obtained after Unidirectional Freezing and Ice-Segregation-Induced Self-Assembly† , 2008 .

[18]  J. Kennedy,et al.  Amphiphilic networks. VI. Swelling and sustained release of poly (N,N-dimethylacrylamide) -l-polyisobutylene, poly (N-N-dimethylamino ethylmethacrylate) -l-polyisobutylene and poly (2-hydroxyethyl methacrylate) -l-polyisobutylene networks☆ , 1993 .

[19]  G. Hild,et al.  Hydroxyalkyl methacrylates: hydrogel formation based on the radical copolymerization of 2-hydroxyethylmethacrylate and 2,3-dihydroxypropylmethacrylate , 1982 .

[20]  A. Banerjee,et al.  pH-Responsive, Bolaamphiphile-Based Smart Metallo-Hydrogels as Potential Dye-Adsorbing Agents, Water Purifier, and Vitamin B12 Carrier , 2007 .

[21]  Naoya Ogata,et al.  Temperature-Responsive Interpenetrating Polymer Networks Constructed with Poly(Acrylic Acid) and Poly(N,N-Dimethylacrylamide) , 1994 .

[22]  Jing Zhu,et al.  Preparation of thermosensitive hydrogels by means of tandem physical and chemical crosslinking , 2011 .

[23]  Y. Ho,et al.  Pseudo-second order model for sorption processes , 1999 .

[24]  D. Chakrabarty,et al.  Tuning of the swelling and dye removal efficacy of poly(acrylamide-AMPS)-based smart hydrogel , 2017 .

[25]  Ian Soutar,et al.  Studies of the smart thermoresponsive behavior of copolymers of N-isopropylacrylamide and N, N-dimethylacrylamide in dilute aqueous solution , 2003 .

[26]  M. Rafatullah,et al.  Application of chitosan and its derivatives as adsorbents for dye removal from water and wastewater: a review. , 2014, Carbohydrate polymers.

[27]  B. Işık,et al.  Thermoresponsive poly(N-isopropylacrylamide-co-acrylamide-co-2-hydroxyethyl methacrylate) hydrogels , 2002 .

[28]  G. Campbell,et al.  Preparation and characterization of a poly(2-hydroxyethyl methacrylate) biomedical hydrogel , 2001 .

[29]  M. Refojo,et al.  Wettability of hydrogels. I. Poly (2-hydroxyethyl methacrylate). , 1975, Journal of biomedical materials research.

[30]  Xinyu Hu,et al.  Synthesis and characterization of a novel semi-IPN hydrogel based on Salecan and poly(N,N-dimethylacrylamide-co-2-hydroxyethyl methacrylate). , 2014, Carbohydrate polymers.

[31]  Takaaki Sato,et al.  Relationship between temperature-induced changes in internal microscopic structures of poly(N-isopropylacrylamide) microgels and organic dye uptake behavior. , 2014, Langmuir : the ACS journal of surfaces and colloids.

[32]  J. Macossay,et al.  Radiation grafting of N,N′-dimethylacrylamide and 2-hydroxyethylmethacrylate onto polypropylene films by one step method , 2013 .

[33]  S. Azizian.  Kinetic models of sorption: a theoretical analysis. , 2004, Journal of colloid and interface science.

[34]  Changsheng Zhao,et al.  Post-crosslinking towards stimuli-responsive sodium alginate beads for the removal of dye and heavy metals. , 2015, Carbohydrate polymers.

[35]  M. Shibayama,et al.  Thermal properties of copolymer gels containing N-isopropylacrylamide , 1996 .

[36]  M. Vidal,et al.  Evaluation of poly(2-hydroxyethyl methacrylate) gels as drug delivery systems at different pH values. , 2000, International journal of pharmaceutics.

[37]  A. Pinkus,et al.  Useful NMR solvent mixture for polyesters: Trifluoroacetic acid-d/chloroform-d , 1993 .

[38]  Se-kwon Kim,et al.  Preparation and characterization of nano chitosan for treatment wastewaters. , 2013, International journal of biological macromolecules.

[39]  Takao Yamamoto,et al.  Synthesis and phase behavior of aqueous poly(N-isopropylacrylamide-co-acrylamide), poly(N-isopropylacrylamide-co-N,N-dimethylacrylamide) and poly(N-isopropylacrylamide-co-2-hydroxyethyl methacrylate) , 2006 .

[40]  M. Serpe,et al.  Poly (N-isopropylacrylamide) microgels for organic dye removal from water. , 2011, ACS applied materials & interfaces.

[41]  H. D. H. Stöver,et al.  Thermally Responsive 2-Hydroxyethyl Methacrylate Polymers: Soluble–Insoluble and Soluble–Insoluble–Soluble Transitions , 2011 .

[42]  Teruo Okano,et al.  Temperature dependence of swelling of crosslinked poly(N,N′-alkyl substituted acrylamides) in water , 1990 .

[43]  Rajat Singh,et al.  Enzymatic decolorization and degradation of azo dyes – A review , 2015 .

[44]  A. Durmuş,et al.  Dye removal by a novel hydrogel-clay nanocomposite with enhanced swelling properties , 2008 .

[45]  E. Muniz,et al.  Removal of methylene blue dye from an aqueous media using superabsorbent hydrogel supported on modified polysaccharide. , 2006, Journal of colloid and interface science.

[46]  Erhan Pişkin,et al.  Functional copolymers of N-isopropylacrylamide for bioengineering applications , 2007 .

[47]  K. F. Mueller.  Thermotropic aqueous gels and solutions of N,N-dimethylacrylamide-acrylate copolymers , 1992 .

[49]  Miguel F. Refojo,et al.  Hydrogels from 2‐hydroxyethyl methacrylate and propylene glycol monoacrylate , 1965 .

[50]  Yong Pei,et al.  The effect of pH on the LCST of poly(N-isopropylacrylamide) and poly(N-isopropylacrylamide-co-acrylic acid) , 2004, Journal of biomaterials science. Polymer edition.

[51]  Daniel Chappard,et al.  2-Hydroxyethyl Methacrylate (HEMA): Chemical Properties and Applications in Biomedical Fields , 1992 .

[52]  I. Langmuir.  THE ADSORPTION OF GASES ON PLANE SURFACES OF GLASS, MICA AND PLATINUM. , 1918 .