Validation of Ultrasonic Velocity Measurements for Detecting Void Swelling in First-Wall Structural Materials

Abstract Time-of-flight ultrasonic measurements were conducted on a thick hexagonal block of 304 stainless steel irradiated to ∽33 dpa in EBR-II, and the results of ultrasonic-implied void swelling and carbide-induced densification were compared with those obtained by immersion density measurements and TEM observation. The three types of measurement were found to agree rather well with each other. This study confirmed that ultrasonic velocity measurement is a powerful non-destructive technique to measure the through-thickness-average volumetric changes induced by neutrons in thick structural materials.

[1]  Y. Isobe,et al.  Transmission Electron Microscopy of 304-type Stainless Steel after Exposure to Neutron Flux and Irradiation Temperature Gradients , 2014 .

[2]  M. L. Hamilton,et al.  Void Swelling of Annealed 304 Stainless Steel at ∼ 370-385°C and PWR-Relevant Displacement Rates , 2013 .

[3]  Mitsuyuki Sagisaka,et al.  A simulation model of ultrasonic wave changes due to irradiation-induced microstructural evolution of thick 304 stainless steel blocks , 2013 .

[4]  Mitsuyuki Sagisaka,et al.  Development of a nondestructive inspection method for irradiation-induced microstructural evolution of thick 304 stainless steel blocks , 2013 .

[5]  Y. Isobe,et al.  Ultrasonic NDE for Irradiation-Induced Material Degradations , 2013 .

[6]  Baldev Raj,et al.  NDE methodologies for characterisation of defects, stresses and microstructures in pressure vessels and pipes , 1997 .

[7]  S. Ohta,et al.  Characterization of Thermal Degradation of Stainless Steel with Ultrasonic Velocities and Backscattering Noise , 1996 .

[8]  P. J. Maziasz,et al.  Overview of microstructural evolution in neutron-irradiated austenitic stainless steels , 1993 .

[9]  J. Bates,et al.  Densification-induced strains in 20% cold-worked 316 stainless steel during neutron irradiation , 1978 .

[10]  C. K. Day,et al.  Effect of Neutron Irradiation on the Elastic Constants of Type-304 Stainless Steel , 1973 .

[11]  W. Appleby,et al.  Measurements of the effects of swelling on the Young's modulus of stainless steels , 1973 .

[12]  Y. Isobe,et al.  Void swelling and resultant strains in thick 304 stainless steel components in response to spatial gradients in neutron flux-spectra and irradiation temperature , 2013 .

[13]  F. Garner,et al.  4.02 – Radiation Damage in Austenitic Steels , 2012 .

[14]  F. A. Garner,et al.  10 – Void swelling and irradiation creep in light water reactor (LWR) environments , 2010 .

[15]  F. Garner,et al.  The Effect of Void Swelling on Electrical Resistance and Elastic Moduli in Austenitic Steels , 2004 .

[16]  F. Garner,et al.  Interaction of Void-Induced Phase Instability and Subsequent Void Growth in AISI 304 Stainless Steel , 2000 .

[17]  Baldev Raj,et al.  New methodology for precise ultrasonic velocity measurement and its application , 1993 .

[18]  D. Porter,et al.  Swelling of AISI Type 304L Stainless Steel in Response to Simultaneous Variations in Stress and Displacement Rate , 1985 .