Feasibility of manufacturing geopolymer bricks using circulating fluidized bed combustion bottom ash

This paper presents a study on geopolymer bricks manufactured using bottom ash from circulating fluidized bed combustion (CFBC). The alkali activators used for synthesis were sodium silicate, sodium hydroxide, and potassium hydroxide and lithium hydroxide solutions. The study included the impact of alkali activator on compressive strength. The reaction products were analysed by XRD, FT-IR and SEM/EDS. The compressive strength of bricks was dependent on the modulus of the sodium silicate activator and the type and concentration of alkali activator. The highest compressive strength could be gained when the modulus was 1.5, and the value could reach 16.1 MPa (7 d after manufacture) and 21.9 MPa (28 d after manufacture). Under pure alkaline systems, the compressive strength was in the order of 10 M KOH>10 M NaOH>5 M LiOH>5 M KOH>5 M NaOH. Quartz was the only crystalline phase in the original bottom ash, and no new crystalline phase was found after the reaction. The main product of reaction was amorphous alkali aluminosilicate gel and a small amount of crystalline phase was also found by SEM.

[1]  Á. G. Torre,et al.  Quantitative determination of phases in the alkaline activation of fly ash. Part II: Degree of reaction , 2006 .

[2]  C. Bergmann,et al.  Fly ash of mineral coal as ceramic tiles raw material. , 2007, Waste management.

[3]  A. Fernández-Jiméneza,et al.  Quantitative determination of phases in the alkali activation of fly ash . Part I . Potential ash reactivity , 2005 .

[4]  I. Topcu,et al.  Properties of geopolymer from circulating fluidized bed combustion coal bottom ash , 2011 .

[5]  D. Levacher,et al.  Effects of the use of fly ash as a binder on the mechanical behaviour of treated dredged sediments , 2009, Environmental technology.

[6]  Guanghong Sheng,et al.  Effect of Zeolitization of CFBC Fly Ash on Immobilization of Cu 2 , 2007 .

[7]  Chang Seon Shon,et al.  Potential use of stockpiled circulating fluidized bed combustion ashes in manufacturing compressed earth bricks , 2009 .

[8]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[9]  W. Lutze,et al.  Kinetics of fly ash geopolymerization , 2011 .

[10]  R. Cioffi,et al.  Coal fly ash as raw material for the manufacture of geopolymer-based products. , 2008, Waste management.

[11]  Hua Xu,et al.  The effect of alkali metals on the formation of geopolymeric gels from alkali-feldspars , 2003 .

[12]  E. Ventura-Ramos,et al.  Synthesis and characterization of a concrete based on metakaolin geopolymer , 2009 .

[13]  A. H. Yegneswaran,et al.  THERMAL IMMOBILIZATION OF Cr, Cu AND Zn OF GALVANIZING WASTES IN THE PRESENCE OF CLAY AND FLY ASH , 2007, Environmental technology.

[14]  P. Chindaprasirt,et al.  Comparative study on the characteristics of fly ash and bottom ash geopolymers. , 2009, Waste management.

[15]  G. C. Lukey,et al.  Effect of Alkali Metals on the Preferential Geopolymerization of Stilbite/Kaolinite Mixtures , 2001 .

[16]  A. Chervonnyi,et al.  Geopolymeric Agent for Immobilization of Radioactive Ashes after Biomass Burning , 2003 .

[17]  J. Zhai,et al.  Self-cementitious properties of fly ashes from CFBC boilers co-firing coal and high-sulphur petroleum coke , 2007 .

[18]  J. Zhai,et al.  Mineralogical Characterizations and Reaction Path Modeling of the Pozzolanic Reaction of Fly Ash-Lime Systems , 2008 .

[19]  Jianping Zhai,et al.  Utilization of fly ash coming from a CFBC boiler co-firing coal and petroleum coke in Portland cement , 2007 .

[20]  P. Sarker.  Analysis of geopolymer concrete columns , 2009 .

[21]  Etsuo Sakai,et al.  Characterization of fly ash directly collected from electrostatic precipitator , 1999 .

[22]  29SI NMR AND SMALL-ANGLE X-RAY SCATTERING STUDIES OF THE EFFECT OF ALKALINE IONS (LI+, NA+, AND K+) IN SILICO-ALKALINE SOLS , 1999 .

[23]  Ángel Palomo,et al.  Mid-infrared spectroscopic studies of alkali-activated fly ash structure , 2005 .

[24]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[25]  John L. Provis,et al.  The Role of Sulfide in the Immobilization of Cr(VI) in Fly Ash Geopolymers , 2008 .

[26]  Á. G. Torre,et al.  Quantitative determination of phases in the alkali activation of fly ash. Part I. Potential ash reactivity , 2006 .

[27]  M. Naeth,et al.  Implications of fly ash application to soil for plant growth and feed quality , 1998 .

[28]  J.S.J. van Deventer,et al.  Factors affecting the immobilization of metals in geopolymerized flyash , 1998 .

[29]  A. Nemec,et al.  Preparation of geopolymer from fluidized bed combustion bottom ash , 2008 .

[30]  S. H. Lin,et al.  Use of fly ash from a cogeneration plant in concrete , 1994 .

[31]  J. Zhai,et al.  Synthesis of thermostable geopolymer from circulating fluidized bed combustion (CFBC) bottom ashes. , 2010, Journal of hazardous materials.

[32]  K. Sagoe-Crentsil,et al.  The effect of Al2O3 and SiO2 on setting and hardening of Na2O-Al2O3 -SiO2-H2O geopolymer systems , 2008 .

[33]  Jiming Hao,et al.  Atmospheric environmental protection in China: Current status, developmental trend and research emphasis , 2007 .

[34]  J. Deventer,et al.  Geopolymer technology: the current state of the art , 2007 .

[35]  Gleb G. Mejeoumov,et al.  Potential use of stockpiled circulating fluidized bed combustion ashes in controlled low strength material (CLSM) mixture , 2010 .

[36]  C. Chan,et al.  Air pollution in mega cities in China , 2008 .